Abstract:Welding residual stress (WRS) significantly influences the fatigue life and safety of welded steel structures. Post-weld heat treatment (PWHT) is a common method employed to mitigate WRS. In present study, the WRS evolution law and relaxation mechanism of U-rib-to-deck joints was investigated during PWHT. High-temperature heat treatment tests with varying holding times were conducted on U-rib-to-deck joints to reduce WRS. The WRS distributions were measured using the hole-drilling method before and after PWHT. ABAQUS software, incorporating the Norton-Bailey creep constitutive model, was employed to simulate the WRS evaluation during both welding and PWHT processes. The simulated values were validated against the measured data, and the effects of different holding times, holding temperatures, and heating and cooling rates during PWHT on WRS relaxation were discussed. The results demonstrate that PWHT effectively reduces WRS and leads to a more uniform distribution. Extending the PWHT holding time from 0.5 h to 1 h and 2 h results in a gradual decrease in WRS relaxation at 600 °C, primarily occurring in the high-value stress region of the weld zone with a small amplitude. Elevating the PWHT temperature from 500 °C to 550 °C and subsequently to 600 °C amplifies the significance of WRS relaxation. Variations in heating and cooling rates (200 °C/h and 80 °C/h, 100 °C/h and 40 °C/h, 50 °C/h and 20 °C/h) lead to a gradual decrease in WRS relaxation across the entire model. Furthermore, considering the creep effect, the stress relaxation rate in the weld is approximately 70 %–80 %, which found to be about 2–3 times higher than that without considering the creep effect. By understanding the evolution law and relaxation mechanism, this study provides valuable insights for designing PWHT processes and assessing their impact on structural safety and fatigue life.

A study on the mechanical stress relieving and safety assessment without post-weld heat treatment

Low Stress Welding Technology Without Post-Weld Heat Treatment

Thermo-mechanical Stress and Fatigue Damage Analysis on Multi-Stage High Pressure Reducing Valve

Effect of Post-Weld Heat Treatment on the Plastic Buckling of Welded Cylindrical Shells

Thermo-mechanical Stress Analysis of Feed-Water Valves in Nuclear Power Plants

Modal and Structural Analysis on a Main Feed Water Regulating Valve under Different Loading Conditions

The primary-auxiliary local post-welding heat treatment method to control welding residual stresses for pressure vessels

Influence of post-weld heat treatment on welding residual stress in U-rib-to-deck joint

Comparison of Stress Relief by PWHT and VSR in Large-Dimension Straight Welded Pipe

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Boiler membrance wall welding stress relief techniques by VSR process

Local Post Weld Heat Treatment of a Pressure Vessel: A Postmortem Evaluation

Assessing Toughness Levels for Nuclear Containment Vessels Steel to Determine the Need for Postweld Heat Treatment Based on the Master Curve Method

Thermal Effect of Welding on Mechanical Behavior of High-Strength Steel

A combined computational and experimental study on vibration stress relief for large welded DH36 steel tube

Effects of Vibratory Weld Conditioning on Residual Stresses and Transverse Contraction Distortions in Multipass Welding

Effect of Local Rapid Cooling Heat Treatment on Residual Stress of Pressure Vessel Inner Wall Welding Layer

A rigid-flexible coordinated method to control weld residual stress and deformation during local PWHT for ultra-large pressure vessels

On Residual Stress and Relief for an Ultra-Thick Cylinder Weld Joint Based on Mixed Hardening Model: Numerical and Experimental Studies

Residual Stress Distribution in Hard-Facing of Pressure Relief Valve Seat

The Residual Stress Relief of Post Weld Heat Treatment in SMA490BW Welded Joints: Simulation and Experiment