Effect of Quenching Rate on Microstructure, Mechanical and Corrosion Properties of Al-Zn-Mg-Cu-Cr-Zr Alloy
Chengbo Li,Cai Zhao,Puli Cao,Daibo Zhu,Bo Xiao,Qinyao Chen
DOI: https://doi.org/10.1007/s11837-024-06661-9
2024-06-12
JOM
Abstract:The quench sensitivity of the corrosion and mechanical properties of an Al-Zn-Mg-Cu-Cr-Zr alloy was investigated utilizing tensile testing, intergranular corrosion experiments and microstructure characterization. The research results indicated that, with a decrease in quenching rate, quenching precipitates sequentially nucleated non-uniformly at grain boundaries (GBs) ( η phase), E phase ( η phase) and Al 3 Zr particles ( η and T phases). As the quenching rate decreased, the size and area fraction of quenching precipitates increased within the grains, consuming many solute atoms. This led to a reduction in the precipitation of the η ′ strengthening phase during the aging process, resulting in a decrease in mechanical properties. Simultaneously, the decrease in quenching rate resulted in a significant increase in the size of the η phase at the GBs, Zn and Mg content, and the width of the precipitate-free zone at the GBs, making the GBs more susceptible to corrosion. This accelerated the rate of corrosion crack propagation along the GBs, reducing the corrosion resistance of the alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mineralogy,mining & mineral processing