Abstract:TiC bonded diamond composites were prepared from a mixture of Ti, graphite, and diamond powders as raw materials, with Si as sintering additives, through high-temperature and high-pressure (HTHP) technology. The reaction between Ti and graphite under 4.5–5 GPa pressure and 1.7–2.3 kW output power can produce TiC as the main phase. The diamond particles are surrounded by TiC, and the interface is firmly bonded. The coefficient of friction (COF) of TiC–diamond composites with POM and PP balls decreases with increasing load for a specific friction velocity. However, the COF of TiC–diamond composites with agate, Cu and Al balls increases with the rising load because of the enhanced adhesive wear effect. The COF of PP, Cu and Al balls slightly increases with the increase in friction velocity at a certain load. SEM results show that the surface of agate balls has rough, pear-shaped grooves and shallow scratches. The scratches on the surface of POM balls are wrinkled. The PP balls have pear-shaped groove scratches on their wear surfaces. The wear mechanism of TiC–diamond composites with Cu ball pairs is primarily adhesive wear. The abrasion of TiC–diamond composites with Cu ball pairs remains almost unchanged as the load increases. However, the depth and width of the pear-shaped grooves on the wear surface of TiC–diamond composites are significantly increased. This phenomenon may be attributed to the high rotational speed, which helps to remove the residual abrasive debris from the friction grooves. As a result, there is a decrease in both the depth and width of the pear-shaped grooves, leading to a smoother overall surface. The wear mechanism of TiC–diamond composites with Al ball pairs is abrasive wear, which increases with an increasing load. When the load is constant, as the speed increases, the wear morphology of TiC–diamond composites with Al ball pairs transitions from rough to smooth and then back to rough again. This phenomenon may be attributed to the wear mechanism at low speeds being groove wear and adhesive wear. As the speed increases, the wear particles are more easily removed from the wear track, leading to a reduction in abrasiveness. As the speed increases, the wear surface becomes roughened by a combination of grooves and dispersed wear debris. This can be attributed to the increased dynamic interaction between surfaces caused by higher speed, resulting in a combination of abrasive and adhesive wear. In addition, Cu and Al ball wear debris appeared as irregular particles that permeated and adhered to the surface of the TiC phase among the diamond particles. The results suggest that TiC–diamond composites are a very promising friction material.

Tribological studies on ultra-fine diamond composite coatings deposited on tungsten carbide

Microstructure evolution and tribological behavior of laser cladded Al 1.8 CrCuFeNi 2 /WC composite coatings on Ti-6Al-4 V

Microstructure and Tribological Performance of Self-Lubricating Diamond/tetrahedral Amorphous Carbon Composite Film

In Situ Synthesis and Tribological Characterization of TiC–Diamond Composites: Effect of the Counterface Material on Wear Rate and Mechanism

Tribological Properties of Diamond Films and Graphite/diamond Composite Films with Dry Friction

Fabrication and tribological properties of textured diamond coatings on WC-Co cemented carbide surfaces

The Microstructure and Wear Properties of Diamond Composite Coatings on TC4 Made by Induction Brazing

Preparation and tribological properties of novel cold–sprayed Ti–diamond composite coating

Study on the Tribology Properties of the Particles/Cu Composite Coatings

The Dry Sliding Wear Behavior of HVOF-Sprayed WC: Metal Composite Coatings

Tribological behavior of aluminum matrix composites reinforced with ceramic particulates in dry sliding against a semimetallic friction material

Study on the friction and wear properties of nickel-based-WC-10Ni composite coatings prepared on the surface of TC4 titanium alloy

Research on microstructure, mechanical property and wear mechanism of AlCoCrFeNi/WC composite coating fabricated by HVOF

Study on tribology and cutting performance of boron doped diamond composite coated tool

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

Study on the abrasive resistance of Ni-based coatings containing WC hard phase

Tribological Performances of Diamond Film and Graphite/diamond Composite Film

Friction and wear behaviors of boron-containing high entropy alloy/diamond composites

Comparing the tribological behavior of polycrystalline diamonds against steel GCr15 and ceramic Si 3 N 4 : friction and wear

Tribological Properties of Ultrananocrystalline Diamond Nanowire Thin Film: Influence of Sliding Ball Counterbodies

Wear performance of the plasma sprayed fine WC-Co composite powders coatings