Abstract:Magnesium borate whisker (Mg2B2O5 w) reinforced Mg matrix composite was fabricated by vacuum-gas pressure infiltration process. The Mg2B2O5 w preforms forming process was determined. The Mg2B2O5 whiskers were fabricated into a preform by wet forming method without any binder. The Vacuum-Gas Pressure Infiltration process and parameters are also developed. The micrographs revealed reasonably uniform distribution and random orientation of the whiskers in the as-cast Mg2B2O5 w/AZ91D composite and the composites were without pores defect. The phases were analyzed by XRD patterns for the as-received whiskers, the whiskers sintered at 1 000 degrees C for 3 h and the as-cast composite, respectively. Then, the microstructure evolution of the composite was investigated when the composite was heat-treated. Meanwhile, the relationships between microstructure and micro-hardness of the alloy heat-treated were also studied. The heat-treatment condition were solution at 415 degrees C for 8 and 24 h, respectively, aging treatment at 200 degrees C for 8, 12, 16, 20 and 24 h, respectively and solution at 415 degrees C for 8 or 24 h and subsequent aging treated for 8, 12, 16, 20, 24 h, respectively. The phases were analyzed by XRD patterns for the composites after different heat treated process. The results of XRD patterns were shown to be in good agreement with the microstructures evolution of the composites. The results showed that the micro-hardness of the solution treated composites is decreased due to resolution of eutectic phase, whereas the micro-hardness of the aged composites was increased gradually and the peak hardness is reached to 201 HV in the composite aged for 16 hours. Solution treatment at 415 degrees C for 24 h, the beta-Mg17, Al12 phase is dissolved in the alpha-Mg phase to form oversaturated solid-solution in the composite and then the diffusive beta phase precipitates after subsequent aging treatment at 200 degrees C for 8 h; hence the micro-hardness of the composite was increased 30%. However, as the aging time increased to 24 h, the hardness of the composite was reduced to 183 HV because the beta-Mg17 Al12 phase precipitate changed from continuous fine platelets to discontinuous coarse platelets. It was concluded that the process of solution at 415 degrees C for 24 h and subsequent aging treatment at 200 degrees C for 8 h was the best process for the composite.

Effect Of Solution Treatment On Tensile Properties Of Aa2024 Matrix Composite Reinforced With Magnesium Borate Whisker

Spectroscopic Characterization and Properties of Mg2B2O5w/AZ91D Magnesium Composites

Microstructure and Mechanical Properties of ABOw and Nickel-Coated MWCNTs Reinforced 2024al Hybrid Composite Fabricated by Squeeze Casting

Strengthening and toughening of carbon fiber reinforced AA2024 by interface self-regulation reaction

Re -dissolution behavior of secondary phases and mechanical response of CNT/2024Al composites

Microstructure and property evolution of aluminium/potassium titanate whiskers composite during Rheo-casting

Effect of solution treatment on porosity, tensile properties and fatigue resistance of Al–Cu alloy fabricated by wire arc additive manufacturing

Effect of Precipitation Heat Treatment on a Mechanically Alloyed Al‐Based Composite Reinforced with Metallic Glassy Powder

Interfacial reaction of aluminum borate whisker reinforced Mg-10Gd-3Y-1Zn-0.4Zr (wt%) alloy matrix composite

Effect of Electromagnetic Stirring and Solution Treatment on Microstructure and Properties of AZ31 Magnesium Alloy

High strength-ductility synergy of MgAlB4 whisker reinforced aluminum matrix composites achieved by in situ synthesis

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Effect of the Addition of Steel Fibers on the Bonding Interface and Tensile Properties of Explosion-Welded 2A12 Aluminum Alloy and SS-304 Steel

Effect of solution time on the microstructure, precipitation behavior and mechanical properties of (Co0.5NiFeCrTi0.5 + SiC)p/7075Al hybrid composite

Combined effects of ultrasonic vibration and FeCoNiCrCu coating on interfacial microstructure and mechanical properties of Al/Mg bimetal by compound casting

Effects of Different Heating and Cooling Rates during Solution Treatment on Microstructure and Properties of AA7050 Alloy Wires

Effects of Solution Treatment on Microstructure Transformation, Tensile and Exfoliation Corrosion Properties of 7136 Aluminum Alloy

Effect Of Solution Treatment And Extrusion On The Microstructure And Mechanical Properties Of A Mg-2gd-Nd-0.4zn-0.3zr Alloy

Effects of Heat Treatment on the Interface Microstructure and Mechanical Properties of Friction-Stir-Processed AlCoCrFeNi/A356 Composites

Effect of surface modification of Al2O3 powder with Y2O3 on microstructure and tensile properties of aluninium matrix composites

Influence of Solution Treatment Time on Precipitation Behavior and Mechanical Properties of Mg-2.0Nd-2.0Sm-0.4Zn-0.4Zr Alloy