Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Morphology Control of Electrodeposited ZnO Using Different Amino Acids As Soft Templets

Morphology Control Of Cuo Micro-Particles Using Zn2+ Ion And Ultrasonic Treatment

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Effect of ammonia on morphology, wettability and photoresponse of ZnO nanorods grown by hydrothermal method

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Preparation of Large-Scale Highly Oriented Zno Noodle Arrays and Study on the Photoconductivity

Morphological control of ZnO nanostructures by electrodeposition.

Morphological Control Of Alpha-Feooh Nanostructures By Electrodeposition

Morphological Control of α-FeOOH Nanostructures by Electrodeposition

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

Zno Microcrystals With Diverse Morphologies

Morphologically Controlled Electrodeposition of Zno and Cu2o by the Colloidal Crystal Template Method

Effects of preparing conditions on the electrodeposition of well-aligned ZnO nanorod arrays

Effect of the morphology on the optical properties of ZnO nanostructures

Morphology regulation, structural, and photocatalytic properties of ZnO hierarchical microstructures synthesized by a simple hydrothermal method

Effects of amines additives on the shapes of TiO2 nanoparticles

FORMLAITION MECHANISM AND INFLUENCE OF SURFACTANT ON MORPHOLOGIES OF ZINC OXIDE NANORODS

Morphology-Controllable synthesis of ZnO nano-/Micro- Structures by a solvothermal process in ethanol solution

Morphology and orientation controlling of ZnO nanofibers via chemical bath deposition

Novel Morphologies of ZnO Nanotetrapods

Oxidation-Crystallization Process of Colloids: An Effective Approach for the Morphology Controllable Synthesis of SnO2 Hollow Spheres and Rod Bundles