Effect of solidification rate on microstructure and crystal orientation of ferromagnetic shape memory alloys Co–Ni–Al

J. Liu,H.X. Zheng,J.G. Li

DOI: https://doi.org/10.1016/j.msea.2006.02.142

2006-01-01

Abstract:Effect of solidification rate on the solidified microstructure and crystal orientation based on a new type ferromagnetic shape memory Co-Ni-Al alloys have been studied by the liquid metal cooling directional solidification. The results show that at the lower rate of 5 mu m/s for the Co32Ni40Al28 alloys, worm-like gamma' phase precipitated in martensite matrix and faceted gamma particles were introduced under the rate of 10 mu m/s. For a rather faster growth rate of 150 mu m/s, interdendritic beta+gamma eutectic lamella appears after the dendritic beta formed. The single austenite phase was observed in the Co38Ni34Al28 alloy at the rate of 5 mu m/s. At the same time, the preferred orientations changed with the variation of the solidification conditions. It is found that < 111 > oriented martensite crystal can be obtained in the Co32Ni40Al28 alloy at the rate of 5 mu m/s, while < 110 > and < 100 > orientations become stronger at the rate of 10 mu m/s. But the preferred orientation degree at 150 mu m/s is very poor. The Co38Ni34Al28 rod with < 110 > oriented austenite can be prepared at the rate of 5 mu m/s. (c) 2006 Elsevier B.V. All rights reserved.