Multilayer Route to Iron Nanoparticle Formation in an Insulating Matrix
Feng Wang,Marek Malac,Ray F. Egerton,Alkiviathes Meldrum,Xiaobin Zhu,Zhigang Liu,Nicole Macdonald,Peng Li,Mark R. Freeman
DOI: https://doi.org/10.1063/1.2434953
IF: 2.877
2007-01-01
Journal of Applied Physics
Abstract:Well-protected, isolated bcc-iron nanoparticles embedded in silicon dioxide were prepared by e-beam evaporation and postannealing of multilayers in an ultrahigh vacuum system. The spherical shape and isolation of the particles were confirmed by plan-view and cross-sectional transmission electron microscopy. Oxidation was evaluated from the electron energy-loss near edge structure. In this technique, a postedge peak of 40eV above the iron L3 threshold, originating from backscattering of oxygen atoms, provides a clear indication of iron oxide. The white-line ratio (WLR), measuring the 3d-orbital occupancy, is used to estimate the oxidation-layer thickness. In the samples of large iron nanoparticles (with average diameter larger than 10nm), a very thin surface layer appears to be the oxide maghemite, approximately one atomic layer according to the WLR evaluations. The evolution of the coercivity with particle size, as measured by the magneto-optical Kerr effect, shows that the reversal process is dominated by the surface anisotropy and is also affected by the dipole interaction, particularly in samples with large volume-filling factor.