Structure Characterization of the Two Kinds of Nanometer Size .Alpha.-Ferric Oxide-Stearate Alternating Langmuir-Blodgett Films by Fourier Transform Infrared Spectroscopy
J YANG,XG PENG,Y ZHANG,H WANG,TJ LI
DOI: https://doi.org/10.1021/j100119a037
IF: 4.177
1993-01-01
The Journal of Physical Chemistry
Abstract:Structure, infrared optical properties, and molecular orientation of 70- and 20-angstrom nanoparticulate alpha-Fe2O3-stearate alternating Langmuir-Blodgett films were studied by using FTIR absorption spectra and Kramers-Kronig (KK) analysis. The KK analysis results show that the average refractive indexes of the films are 1.83 (70 angstrom) and 1.62 (20 angstrom), respectively. According to the refractive index, extinction spectra, and the linear infrared dichroic spectra of the films, the molecular orientation was calculated. The orientation angles are 5-degrees and 38-degrees for fatty chains, 80-degrees and 65-degrees for COO- asymmetric mode, and 55-degrees and 39-degrees for COO- symmetric mode of stearate ions in 20- and 70-angstrom alpha-Fe2O3-St LB films, respectively. From these results, the carboxylate groups were considered to be a relatively spherical symmetric distribution, and on the contrary, the hydrocarbon chains were found almost perpendicular to the substrate. The band progressions of Fe2O3-St LB films in the range of 1360-1320 cm-1 can be detected, especially in the case of 20-angstrom Fe2O3-St LB films. These indicated that the films possess a high-order alternating structure. The hexagonal-like close packing (hcp) form of the nanoparticles was considered as a possible structure between two stearate ion layers. The obvious hypsochrome shift was observed in the UV-visible spectra of the 20- and 70-angstrom Fe2O3-St films, indicating the influence of quantum size effect.