Studies on the Crystallization and Properties of PA6/Potassium Chloride Composites
Xiao-ying Hu,Qiang Zheng,Cai-hong Wang,Jun Wang,Jie Yu,Sheng-jun Lu
DOI: https://doi.org/10.11777/j.issn1000-3304.2016.15321
2016-01-01
Abstract:The polyamide 6 (PA6)/KCl composites were prepared by the melt blending method. The effect of KCl content on the crystallization behavior, as well as the rheological and mechanical properties of the composities was studied by differential scanning calorimeter (DSC), advanced rheometer (ARES-G2), Fourier fransform infrared spectrometer (IR) and universal testing machine. The mechanism of confined crystallization was also systematically investigated. The mechanical property results show that the tensile strength and notch impact strength increased first and decreased finally with the increase of KCl content. When the amount of KCl was 3 phr, the tensile strength and notch impact strength of the PA6/KCl composities reached the maximum values of 82. 67 MPa and 7. 34 kJ/m(2), respectively, which presented 10. 8% and 34. 68% improvement compared to those of the pure PA6. The dynamic mechanical property measurement results demonstrated that the storage modulus of the composite materials was higher than that of pure PA6 in the measuring temperature range, and the storage modulus of the composites increased with the increase of KC1 content. The crystallization behavior results reveal that with the addition of KCl content, the temperature of nucleation, the growth temperature of crystal, the melt temperature of crystal and the glass transition temperature of spherulites dramatically decreased. The density and the rate of nucleation also decreased gradually, the crystallization ability of PA6/KCl composites decreased and the crystallinity decreased from 20. 30% to 19. 34%, the crystallization induction time gradually increased. The rheological property results showed that with the increase of KCl content, the composites exhibited zero shear viscosity and pseudo plastic fluid behavior, and the phenomenon of shear thinning became more and more obvious, the changes in relaxation mechanism led to the gradually increase in the characteristic relaxation time tau(1), tau(2) and tau(3).