Abstract:The non-contact electrical resistivity method was employed to investigate the microstructural development of three grades of cement under a fixed water-to-cement ratio (w/c) and the same curing conditions. The method was verified by measuring the heat of hydration and estimating the degree of hydration of the three pastes. The results showed that the existence of a linear relationship between the compressive strength at 28 d (f 28) and bulk electrical resistivity at 72 h (ρ72); thus, the proposed method can be used to assess the strength of cement. Moreover, the results indicated that the quality of cement can be further distinguished by interpreting the trend in the resistivity curve. The high-strength cement will have lower electrical resistivity values during cement dissolution due to the higher content of ions in the pore solution, while it will have higher resistivity values during cement hardening due to the greater amount of hydrates. The electrical resistivity of the cement solution (ρ0) filtered from the cement paste at an early age was measured to demonstrate the effect of the ionic concentration on the bulk electrical resistivity in the initial hydration period. The measured liquid resistivity of cement can be used as an indication of clinker reactivity; higher-strength cement will always have lower measured values. The rate of electrical resistivity development curve was plotted to elucidate the setting range of cement pastes based on three critical points. The time at the second critical point (C2) coincided with the final setting time determined using a Vicat needle. New general relationships between the gel-space ratio and electrical resistivity were developed. Furthermore, autogenous shrinkage was measured for the three cement pastes, and the behaviour could be anticipated from the electrical resistivity measurements.

Monitoring of Hydration Using the Electrical Resistance of Carbon Fiber Reinforced Cement Materials

Investigation of the Early-Age Microstructural Development of Hydrating Cement Pastes Through Electrical Resistivity Measurements

Carbon fiber reinforced cement and its stress sensor

Portland Cement Hydration by Electrical Resistivity Method and Computer Simulation

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Electrochemical Impedance Spectroscopy Monitoring of Hydration Behaviors of Cement with Na2CO3 Accelerator

A Mathematical Model for the Electrical Resistivity of Cement Paste at Early Ages Considering the Partially Saturated State

Temperature and humidity variation of specific resistance of carbon fiber reinforced cement

The Humidity Sensing Property of Cements with Added Carbon

Electrical Resistance Stability of High Content Carbon Fiber Reinforced Cement Composite

A study on the hydration of calcium aluminate cement pastes containing silica fume using non-contact electrical resistivity measurement

Experimental Research of Electrical Conductivity and Pressure-Sensitivity of Carbon Fiber Reinforced Cement

Early Hydration Process of Portland Cement Paste by Electrical Measurement

Hydration of Cement with Retarder Characterized Via Electrical Resistivity Measurements and Computer Simulation

Monitoring the Setting and Hardening Behaviour of Cement Paste by Electrical Resistivity Measurement

Monitoring the hydration behavior of hardened cement paste affected by different environmental pH regimes

Reinforcement Effect and Mechanism of Carbon Fibers to Mechanical and Electrically Conductive Properties of Cement-Based Materials

Conductive Mechanism and Hydration Property of Cement-Based Materials with Steel Fibers

Early Age Properties of Cementitious Materials by Electrical Resistivity Measurement

Study on the producing technology and properties of carbon fiber reinforced cement sensor

Influence of Calcium Sulfate State and Fineness of Cement on Hydration of Portland Cements Using Electrical Measurement