Abstract:Accurate prediction of fatigue performance and life is a key issue in the design and applications of the high strength-to-weight ratio of many contemporary magnesium alloys, which are suitable for ultimate weight reduction purposes in automotive and aircraft components. For example, the ever increasing demands for higher efficiency and light weight typical cases of power generation, aerospace and automotive industries call the maximum exploitation of the material’s properties. The combination of low density (about 1.74 g/ cm3), high specific strength and excellent castability qualifies magnesium alloys as ideal materials for the lightweight constructions [1]. Thus, purely empirical models that heavily rely on larger safety factors are of limited uses. It is now widely recognized that fatigue damage models that are closely related to the microstructural features to provide a more reliable basis for a life prediction, provided that the relevant microstructural damage mechanisms are accurately accounted for. Therefore, there are increasing interests in the fatigue tests combined with the high-resolution microscopic techniques, environmental influencing factors, and especially in understanding their fatigue crack initiation and propagation behaviors with process rationalization [2-4]. Subsequently experimental observations on cast magnesium alloys have accumulatively revealed that the dendrite cell size, pores, secondary phase particles, persistent slip bands and twinning in the dendrite cells considerably affect on the fatigue durability and fatigue cracking behavior or crack growth mechanism of dendritic magnesium alloys [5-8]. The quantitative estimation of small fatigue crack growth rate of cast magnesium alloys is whether simply and effectively to assist the reversed design of cast magnesium alloys or ceaselessly to improve the strength and toughness of cast magnesium alloys. At the same time, it is necessary how to understand that these microstructural features of cast magnesium alloys play role in the fatigue cracking behavior or that the microstructural evolution reacts to the applied loadings. However, it is difficult to use conventional alloying techniques to improve some of their properties, e.g. elastic modulus, elastic-plastic deforming property and the different thermal expansion between phases during the shrinking at the high elevated temperatures. Under these conditions the elastic, and the possible plastic, properties of the secondary phase will influence the mechanical response during an applied loading since the interface of secondary phase will transmit stresses from the matrix around the secondary phase when the interface both the matrix and secondary phase has a compatible strain field. If the elastic

Influence of Microstructure on Tensile Properties and Fatigue Crack Growth in Extruded Magnesium Alloy AM60

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Small fatigue crack growth in an extruded dual-phase Mg-Li alloy

Relationship Between the Fatigue Behavior and Grain Structures of an As-Extruded Mg-6.2%Zn-0.6%Zr (in Wt.%) Alloy

In-situ Analysis of Microscopic Plastic and Failure Behaviors of Extruded Magnesium Alloy

Investigation of Surface Fatigue Microcrack Growth Behavior of Cast Mg–Al Alloy

Low-cycle Fatigue Small Crack Initiation and Propagation Behaviour of Cast Magnesium Alloys Based on In-Situ SEM Observations

Fatigue Cracking Behaviors and Influence Factors of Cast Magnesium Alloys

Tensile Mechanical Properties and Deformation Mechanism of the Extruded ZM61 Magnesium Alloy at High Strain Rates

In Situ Monitoring of Dislocation, Twinning, and Detwinning Modes in an Extruded Magnesium Alloy under Cyclic Loading Conditions

Stress-state dependency of ductile fracture in an extruded magnesium alloy and its underlying mechanisms

Investigation of the microstructure and properties of extrusion-shear deformed ZC61 magnesium alloy under high strain rate deformation

Multiscale Mechanical Behavior and Microstructure Evolution of Extruded Magnesium Alloy Sheets: Experimental and Crystal Plasticity Analysis

Effects of optimizing continuous forging extrusion process on the microstructure and mechanical properties of AZ31 magnesium alloy

Effects of Distance and Alignment Holes on Fatigue Crack Behaviors of Cast Magnesium Alloys

Damage evolution of extruded magnesium alloy from deformation twinning and dislocation slipping in uniaxial stress-controlled low cycle fatigue

Towards revealing the relationship between deformation twin and fatigue crack initiation in a rolled magnesium alloy

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

Microstructural Evolution and Mechanical Properties of Extruded AZ80 Magnesium Alloy during Room Temperature Multidirectional Forging Based on Twin Deformation Mode

In-situ synchrotron X-ray tomography investigation of damage mechanism of an extruded magnesium alloy in uniaxial low-cycle fatigue with ratchetting

Research Progress on Microstructure Evolution and Strengthening-Toughening Mechanism of Mg Alloys by Extrusion