Effect of Microstructure Heterogeneity on Fatigue Crack Growth of TA15 Electron Beam Welded Joint

LI Xing-zhi,HU Shu-bing,XIAO Jiang-zhong,JI Long-bo
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2010.12.007
2010-01-01
Abstract:By a means of horizontally intercepting fatigue specimen,the microstructure,hardness,fatigue crack growth rate and fatigue fractograph in the welding seam (WS) and heat-affected zone (HAZ) of thick TA15 alloy electron beam (EB) welded joint were studied. The results indicate that on the same height from the top of WS,the microstructure heterogeneity is the most severe in HAZ,from the top to root of WS,the microstructure heterogeneity increases with decreasing α' martensite size. Attributed primarily to the effect of microstructure heterogeneity,the fatigue crack growth rate (FCGR) is faster in HAZ than that in WS. The fatigue fractographs show this macroscopical difference by scanning electron microscopy (SEM) analyses.