STUDY ON NOVEL POLY(PHTHALAZINONE ETHER NITRILE KETONE)HOLLOW FIBER ULTRAFILTRATION MEMBRANES

YANG Da-ling,ZHANG Yao,ZHANG Shou-hai,HAN Jun-nan,JIAN Xi-gao

DOI: https://doi.org/10.16796/j.cnki.1000-3770.2008.10.006

2008-01-01

Abstract:By using poly(phthalazinone ether nitrile ketone)(PPENK) as membrane material,N-methyl-2-pyrrclidone (NMP) as solvent,the hollow fiber membrane were prepared by the dry-wet phase inversion technique. The effect of PPENK concentration,additive content,air gap distance,gel-bath temperature and fiber thickness during the membrane prepared process on the structure and property of PPENK hollow fiber ultrafiltration membranes were studied. By the retention test of BSA,the results showed that the pure water flux of membranes was 770 L·m-2·h-1 when the PPENK concentration was 13% and ratio of near-to cloud point α=0.9 for EgOH content; with the increase of the air gap distance,pure water flux of the membrane decreased while the retention of BSA increased,the best air gap range was 5～8 cm; With the increase of gel-bath temperature,pure water fluxes increased while the retention of BSA decreased. The proper gel-bath temperature was 21～25℃ and the optimum range of fiber thickness was about 0.15～0.18 mm.