Abstract:Ultrafiltration hollow fiber membranes were prepared from poly(ether imide) (PEI) with a wet spinning method. Effects of N,N-dimethylacetamide (DMAc) as a solvent additive in internal coagulant and acetic acid as a nonsolvent additive in dope solution on the morphologies and performances of the membranes were investigated respectively. Scanning electron microscope (SEM) study indicated that the addition of DMAc into the internal coagulant changed the inner fiber surface from dense skin layer to porous structure. However, the pure water flux of the membrane decreased with the increase of DMAc content. On the other hand, the addition of acetic acid into casting solution promoted the spinodal demixing of the membrane-forming system and suppressed the macrovoid formation in the membrane. Nodular structure was formed in the fiber skin layer. With the increase of acetic acid ratio, the pure water flux of the membrane increased about four times, and the solute retention showed a slight decrease. The mechanical properties could also be improved slightly by this additive. The influences of PEI dope concentration on membrane morphologies and properties were also studied. It was found that tighter structure was formed for higher PEI concentration, in turn, the pure water flux of the membrane decreased from 23.4l/(m2h) 100kPa for 17wt.% PEI concentration to 7.2l/(m2h) 100kPa for 25wt.% PEI concentration. The thermal resistance of the PEI ultrafiltration membranes prepared in this work was examined using a hot water treatment up to 80°C. No change was observed for the permeation performances of the membranes, while the study of mechanical properties showed that the elongation at break of the membrane decreased slightly.

Preparation and Characterization of Microporous Polyethylene Hollow Fiber Membranes

Preparation and Structural Control of Polyethylene Hollow Fiber Membranes

Preparation of High Density Polyethylene/polyethylene- Block -Poly(ethylene Glycol) Copolymer Blend Porous Membranes Via Thermally Induced Phase Separation Process and Their Properties

Structure formation and characterization of PVDF hollow fiber membranes by melt-spinning and stretching method

Preparation and Characterization of Pvdf-Hfp Microporous Membrane by Template Method

Preparation and Performance of Polyethersulfone Hollow-Fiber Membrane

Characterization of a positively charged composite nanofiltration hollow fiber membrane prepared by a simplified process

Preparation and Characterization of Low-Pressure Nanofiltration Membranes and the Application in the Separation Process of Dye Molecules

Preparation and Characterization of PVDF‐HFP Membrane

Preparation of poly(4-methyl-1-pentene) asymmetric or microporous hollow-fiber membranes by melt-spun and cold-stretch method

Polypropylene Hollow-Fiber Membrane Made Using the Dissolution-Induced Pores Method

Effect of stretching on structure and properties of polyethylene hollow fiber membranes made by melt-spinning and stretching process

Experimental And Numerical Analyses On The Poly(Lactide-Co-Glycolide) Hollow Fiber Membranes

Ultrafiltration Hollow Fiber Membranes from Poly(Ether Imide): Preparation, Morphologies and Properties

Preparation of high-flux polyethylene hollow fiber microfiltration membranes with multiple pore structure through the combination technology of braided tube reinforcement and TIPS method

High performance zeolite NaA membranes synthesized on the inner surface of zeolite/PES–PI blend composite hollow fibers

Preparation and characterization of polyvinylidene fluoride (PVDF) hollow fiber membranes

Preparation of Free-Standing High Quality Mesoporous Carbon Membranes

Engineered pinhole-stitching process of PEI-based hollow fiber membrane enables preferred performance toward light gas separation

Study of polyamide-6 hollow fiber membranes prepared via a thermally induced phase-separation method

Preparation and Performances of Poly(Phthalazinone Ether Sulfone Ketone) Hollow Fiber Membranes with Excellent Thermotolerance