Abstract:This work aims to manufacture PVDF/PDMS waterproof and moisture-permeable membranes. This objective was achieved using the electrostatic spinning in-situ polymerization method proposed by the authors. Furthermore, it was also studied how different PDMS/PVDF content significantly changed nano-fiber membrane properties such as morphology, structure and mechanical properties to improve the properties and morphology of PVDF/PDMS nano-fiber membrane. Both PVDF/DMAc solution and PDMS/THF solution had to be firstly fabricated under certain conditions. Then related equipment was utilized to characterize and test the morphology and properties of PVDF/PDMS nano-fiber membrane. Based on experiments and analysis, it's also explored how different PVDF/PDMS percent impacted on nano-fiber membrane morphology, structure, mechanical properties and waterproof and moisture permeable properties. Results showed that PVDF/PDMS membrane fabricated by electrostatic spinning in-situ polymerization method could easily manufacture PVDF/PDMS waterproof and moisture permeable membrane and that mixing solution with PVDF/PDMS mass ratio 7:3 obviously improved the morphology of waterproof and moisture permeable membrane and physical properties where PVDF/PDMS mass ratio was 7:3, which voltage was 28 kV, which injection speed was 0.5 cm/h and which receiving distance was 20 cm. Furthermore, the morphology of the textile fibrous network was very uniform such as fiber diameter: 150 nm, water contact angle(WCA): 145.7 degrees, air permeability: 3.9 mm/s, hydrostatic pressure: 132 kPa, water vapor transmission: 5115 g/m 2 ·24 h. It was concluded that the method was analytically derived and effective. PVDF/PDMS waterproof and moisture permeable membrane and its manufacturing method could be applied to textile fields and clothing fields.

Fabrication of Profiled Microfiber Spinneret Based on UV-LIGA Technology

Fabrication of spinneret for spinning non-circular microfiber based on UV-LIGA technique

A rotary spinneret for high output of electrospun fibers with bimodal distribution

Centrifugal spinning：A high-efficient approach to fabricate micro-/nano-fibers(Part 1)

Facile Fabrication of Microfluidic Chips for 3D Hydrodynamic Focusing and Wet Spinning of Polymeric Fibers

Effective Method for High-Throughput Manufacturing of Ultrafine Fibres Via Needleless Centrifugal Spinning

Research on Spinnability of 55 Dtex/36 F Superfine Lobed PET/PA Composite DTT

Fabrication of PS/PVDF-HFP Multi-Level Structured Micro/Nano Fiber Membranes by One-Step Electrospinning

Dissipative particle dynamics simulations of centrifugal melt electrospinning

Process Study of Fabricating Bi-layer Micro Gears through UV-LIGA Technique

Fabrication and Property Optimization of Electrostatic Spinning PVDF/PDMS Waterproof and Moisture Permeable Membrane

Large-Scale Preparation of Polymer Nanofibers for Air Filtration by a New Multineedle Electrospinning Device

Fabrication Of Micro Yarn Composed Of Nanofibers By Blown Bubble Spinning

Advances in Fabrication of Polymer Fibers by Electrospinning

Numerical Simulation and Experimental Verification of Melt-Spinning Parameters' Effects on Multi-Leaf Hollow-Profiled Fiber Preparation

Effect of Air-Flow Parameters on the Morphology of Nanofibrous Yarns by Blown Bubble-Spinning

High-throughput production of kilogram-scale nanofibers by Kármán vortex solution blow spinning

Effect of improved electric field distribution on jet motion, fiber morphology, and properties of electrospun thermoplastic polyurethane fibrous membrane

Research on rotary nozzle structure and flow field of the spinneret for centrifugal spinning

Enhancing the Spun Yarn Properties by Controlling Fiber Stress Distribution in the Spinning Triangle with Rotary Heterogeneous Contact Surfaces

Research on the Fabrication of Micro-nano Fiber by Drawing