Abstract:Poly(butyl acrylate)/nanosilica (PBA/SiO2) composite particles were prepared by in situ emulsion polymerization initiated by 2,2’-azobis(2-amidinopropane)dihydrochloride (AIBA) initiator adsorbed on the surface of nanosilica particles. The morphology of the composite particles was observed by transmission electron microscopy, and the combination grade of PBA latex particles with SiO2 particles was characterized by centrifugation/re-dispersion and HF etching experiments. The results show that the PBA/SiO2 composite particles exhibit the raspberry-like morphology with most SiO2 particles aggregated at the surface of PBA latex particles. When the mass fraction of SiO2 in the composite particles is in the range of 14.6% to 22.6%, more than 60% SiO2 particles are enriched on the surface of composite particles, and about 30% SiO2 particles are encapsulated in the inner of composite particles. The results also show that the combination strength between SiO2 particles and PBA in the composite particles prepared by in situ emulsion polymerization is stronger than that in the composite particles prepared by direct mixing of PBA latex (prepared by using AIBA as initiator) and SiO2 dispersion. It was considered that, via the ATBA adsorbed on the surface of SiO2 particles, the PBA chains are anchored onto SiO2 particles during in situ emulsion polymerization, the hydrophilicity/hydrophobicity of SiO2 particles and compatibility of SiO2 with PBA vary with the amount of anchored PBA, these lead to the above distribution manner of SiO2 particles in the composite latexes and the morphology of the resultant composite particles.

Preparation Of Poly(Butyl Methacrylate)/Gamma-Al2o3 Nanocomposites Via Ultrasonic Irradiation

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Synthesis and Characterization of Poly(butyl Acrylate)/silica and Poly(butyl Acrylate)/silica/poly(methyl Methacrylate) Composite Particles

Preparation of Poly(methyl Methacrylate)/ultrafine CaCO3 Composite Particles by In-Situ Dispersion Polymerization

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

Synthesis and characterization of poly(methyl methacrylate-butyl acrylate)/nano-titanium oxide composite particles.

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Preparation of Polymer/inorganic Nanoparticles Composites Through Ultrasonic Irradiation

Synthesis and Characterization of PMMA/Al 2 O 3 Composite Particles by in Situ Emulsion Polymerization

Morphology and Formation Mechanism of Poly(butyl Acrylate)/nanosilica Composite Particles Prepared by in Situ Emulsion Polymerization

Synthesis and characterization of PMMA/Al2O3 composite particles by in situ emulsion polymerization

Preparation of polyacrylamide and gamma-zirconium phosphate nanocomposites by intercalative polymerization.

Using Anionic Polymerizable Surfactants in Ultrasonically Irradiated Emulsion Polymerization to Prepare Polymer Nanoparticles

Preparation and characterization of polymer/inorganic nanoparticle composites through electron irradiation

Radiation Preparation of Microporous Materials Using Bicontinuous Microemulsion Polymerization

Microwave-Irradiated Preparation and Oil Fume-Adsorbing Properties of PMMABMA Resin

Ultrasound Assisted Continuous‐mixing for the Preparation of PP/SEBS/OMMT Ternary Nanocomposites

Surface Modification of Nanosized Alumina Hydrate

High Monomer Content Batch Microemulsion Polymerization of Butyl Acrylate and Acrylonitrile Initiated with Gamma Ray