The Corrosion Behavior of Melt-Spun CrNi20P Alloys in Concentrated Hydrochloric and Hydrofluoric Acids

BP ZHANG,H HABAZAKI,A KAWASHIMA,K ASAMI,K HASHIMOTO
DOI: https://doi.org/10.1016/0010-938x(93)90002-x
IF: 7.72
1993-01-01
Corrosion Science
Abstract:Amorphous alloys containing up to 60 at% Cr were prepared by a rotating wheel method. When the chromium content was increased to 70 at% (Cr10Ni20P alloy), a small number of nanocrystallites assigned to Cr3P and bcc Cr phases by XRD and TEM appeared in the amorphous matrix. The amorphous alloys exhibit undetectable corrosion rate in both 6 and 12 M HCl at 30°C, while the corrosion rate abruptly increased in 12 M HCl when the crystalline phases exist. The Cr10Ni20P alloy was spontaneously passive in 6 M HCl but depassivated in 12 M HCl. All the melt-spun CrNi20P alloys show an almost constant low corrosion rate of about 3 × 10−3 mm y−1 in 47% HF at 30°C, regardless of the structure. The insensibility of the corrosion behavior in HF solution to the structure is attributed to spontaneous passivation due to the high activity of the phosphorus containing phase for the oxygen reduction.
What problem does this paper attempt to address?