Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Study on the foam releasion corrosion inhibitor for natural gas gathering and transferring metal pipe

Study on corrosion inhibitor technology in gas pipeline

Corrosion Inhibition Properties of Corrosion Inhibitors to under-Deposit Corrosion of X65 Steel in CO2 Corrosion Conditions

Experimental Evaluation of Anticorrosion of a Standard 20# Gathering Pipeline by Injecting Oxygen-Reduced Air into Simulated In-Service Wells

Preparation of a Corrosion Inhibitor Preventing H2S Corrosion and Coupon Test

Epitope spreading in systemic lupus erythematosus: identification of triggering peptide sequences.

PREPARATION OF A CORROSION INHIBITOR PREVENTING H_2S CORROSION AND COUPON TEST

Research on Oil and Gas Field CO_2 Corrosion Protection Technology

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

CO_2 Corrosion and Protection Technology in Oil and Gas Field

Corrosion Status of Oil Well Pipe and Anti-corrosion Technology Development

Study on Corrosion Mechanism of N80 Steel Pipe Columns and Threads by CO2-Cl− in Shale Gas

Unveiling the inhibition of high-pressure CO2 flow accelerated corrosion at gradual contraction and gradual expansion tubings

Research on Evaluation of Corrosion Inhibitors for Oxygen Reducing Air Drive Gas Wells

Effect of CO2 Partial Pressure on the Corrosion Inhibition of N80 Carbon Steel by Gum Arabic in a CO2-Water Saline Environment for Shale Oil and Gas Industry

Study on the inhibition mechanism of corrosion under inert deposit-covered X65 steel by three corrosion inhibitors

Study on an all-in-one foaming agent with corrosion inhibition for air foam flooding

Study of the Corrosion and Protection Technology of Oil and Gas Pipeline

Molecular Dynamics Simulation of Methane Hydrate Formation on Pipeline Surface in the Presence of Corrosion Inhibitors

Study on Corrosion in CO2 Chemical Absorption Process Using Amine Solution

Revealing the Deterioration Effect of Scale Inhibitor on the Performance of Corrosion Inhibitor under Dynamic Conditions