Directional Growth Charater of the Ni-11.5wt%Si Eutectic Alloy

Cui Chunjuan,Zhang Jun,Wu Kun,Zou Dening,Ma Youping,Liu Lin,Fu Hengzhi

2012-01-01

Rare Metal Materials and Engineering

Abstract:As a high-strength and corrosion-resistance new metal matrix composite, Ni-Ni3Si has the potential for application prospect in the field of high temperature structure material field, such as aerospace. This article studied the directional growth character of the Ni-Ni3Si eutectic composite which was prepared by Bridgman directional solidification techniques. Microstructure of the unsolidified sample is dendritic crystal, bulky Ni3Si phase behaving as the primary phase grows earlier than the eutectic structure in the transition region, and microstructure of Ni-Ni3Si eutectic in the stable growth zone is the regular lamellar eutectic structure. The Ni-Ni3Si eutectic solute distribution was studied by the XRD and EDS technology, and it is shown that the directionally solidified Ni-Ni3Si composite materials is composed of Ni, Ni3Si and Ni31Si12 phase. Ni31Si12 is the metastable phase which is formed due to the eutectoid decomposition. of the beta(2)-Ni3Si phase. Moreover, lamellar spacing adjustment also occurs during solidification processing.