Preparation and photo-catalytic properties of nanostructured TiO2 thin films coated on different ceramics

Xuechang Ren,Zaifeng Shi,Lingren Kong,Zhongbo Wei

DOI: https://doi.org/10.3969/j.issn.1673-9108.2006.02.004

2006-01-01

Abstract:In the research,titanium dioxide films were coated on two kinds of ceramics by using sol-gel method.XRD,XPS and SEM were used to investigate their photo-catalytic property.The results indicated that the average grainsize of TiO_2 was about 15 nm,the TiO_2 thin film coated on the vitreous enamel was uniform and continuous,which thickness was about 300 nm,and the films coated on the stoneware were nonuniform;some(ions) from the two substrates were observed to permeated to the films by XPS.Photocatatytic degradation experiment showed that phenol can be degraded by the TiO_2 thin films coated on the two kinds of ceramics,its kinetics was the first order,the photocatalytic activity followed the decreasing order: TiO_2/vitreous enamel>TiO_2/stoneware;it was considered that Ca~(2+) permeated from substrates could reduce the photocatalytic activity,and the TiO_2 thin films could degrade Badistan wastewater.When the degradation experiments were repeated 20 times for the same film,the removal ration of TiO_2/vitreous enamel and TiO_2/stoneware were decreased 9% and 6% respectively.