CO Oxidation over Highly Dispersive Supported Palladium Catalysts

WANG Zhao-wen,CHEN Ming-shu,WAN Hui-lin

2011-01-01

Abstract:In present studies,a series of oxide supported palladium catalysts were synthesized using various methods to achieve a better dispersion of the active component.CO oxidation was selected as a probe reaction to examine the catalytic performance.It was found that Pd/TiO2 catalyst prepared using palladium(II) acetate as a precursor exhibited high catalytic activity for CO oxidation at room temperature,which activity is much higher than those on Pd/SiO2 and Pd/Al2O3 catalysts.In-situ Fourier transform infrared spectroscopy(FT-IR) reveals that CO can react with surface lattice oxygen of TiO2 to form CO2 in the absence of gas O2 on the Pd/TiO2 catalyst.Comparative studies using BET,O2-chemisorption,in-situ FT-IR of CO adsorption and temperature programmed reduction(H2-TPR) techniques were carried out in order to elucidate the relationship between the structure and activity for CO oxidation at low temperature.Metallic Pd was found to be highly dispersed on TiO2 and Al2O3 support surfaces.A relatively high temperature reduction peak observed in H2-TPR suggests a strong interaction between Pd and the TiO2 support.The origins of the high activity for CO oxidation on Pd/TiO2 at near room temperature may come from the highly dispersive Pd and the strong interaction between Pd and support.