Abstract:The processing conditions were varied during the production of polycarbonate-based composites with the multiwalled carbon nanotubes (MWCNTs) Baytubes® C150 P (Bayer MaterialScience AG, Leverkusen, Germany), by melt mixing with an extruder on a laboratory scale. These included the screw design, rotation speed, throughput, feeding position and MWCNT content. Particular attention was paid to the shortening of the MWCNT length as a function of the conditions mentioned. It was found that there is a correlation between the applied specific mechanical energy (SME) during the melt mixing process and MWCNT dispersion, which was quantified by the agglomerate area ratio of the non-dispersed nanotubes based on optical microscopic analysis. The higher the SME value, the lower this ratio, which indicates better dispersion. Above an SME value of about 0.4 kWh/kg, no further improvement in dispersion was achieved. The MWCNT length, as measured by the quantitative analysis of TEM images of the MWCNTs dissolved from the composites, decreased with the SME value down to values of 44% of the original MWCNT length. At a constant loading of 3 wt.%, the tensile strength and tensile modulus were almost independent of the SME, while the elongation at break and notched impact strength showed an increasing trend. The variation in the feeding position showed that feeding the MWCNTs into a side feeder led to slightly better electrical and mechanical properties for both types of MWCNTs studied (Baytubes® C150 P and NanocylTM NC7000 (Nanocyl S.A., Sambreville, Belgium)). However, feeding into the hopper led to better CNT dispersion with Baytubes® C150 P, while this was the case with NanocylTM NC7000 when feeding into the side feeder. The screw profile had an influence on the dispersion, the MWCNT length and the electrical resistance, but only to a small extent. Distributive screws led to a greater shortening of the MWCNT length than dispersive screws. By varying the MWCNT content, it was shown that a greater MWCNT shortening occurred at higher loadings. Two-stage masterbatch dilution leads to stronger shortening than composite production with direct MWCNT incorporation.

Melt Mixing of Polycarbonate with Multi‐Walled Carbon Nanotubes in Miniature Mixers

Nanocomposites of Poly(vinylidene Fluoride) with Multiwalled Carbon Nanotubes

Electrical, Morphological and Rheological Study of Melt-Mixed Polystyrene/Copper Nanowire Nanocomposites

Visualization of Poly(ether Imide) and Polycarbonate Blending in an Internal Mixer

A Facile Route to Prepare High−performance Dielectric Nanocomposites of Poly(methyl Methacrylate)/poly(vinylidene Fluoride)/carbon Nanotubes

Simultaneous Ultrasonication‐assisted Internal Mixing to Prepare MWCNTs‐filled Epoxy Composites with Increased Strength and Thermal Conductivity

Electrical and rheological percolation of PMMA/MWCNT nanocomposites as a function of CNT geometry and functionality

Migration of MWCNTs during melt preparation of ABS/PC/MWCNT conductive composites via PC/MWCNT masterbatch approach

Preparation Of Conductive Polyphenylene Sulfide/Polyamide 6/Multiwalled Carbon Nanotube Composites Using The Slow Migration Rate Of Multiwalled Carbon Nanotubes From Polyphenylene Sulfide To Polyamide 6

Influence of Twin Screw Extrusion Conditions on MWCNT Length and Dispersion and Resulting Electrical and Mechanical Properties of Polycarbonate Composites

Selective Location and Conductive Network Formation of Multiwalled Carbon Nanotubes in Polycarbonate/poly(vinylidene Fluoride) Blends

Efficient Dispersion of Multi‐walled Carbon Nanotubes by in Situ Polymerization

Toughness Enhancement of Poly(methyl methacrylate) (PMMA)/Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) Nanocomposites by Multiwall Carbon Nanotubes (MWNT)

Multi-walled Carbon Nanotubes/silicone Rubber Nanocomposites Prepared by High Shear Mechanical Mixing

The Study on the Microstructures and High Performances of Melt Blending Polyurethane/Multiwalled Carbon Nanotubes Composites

Effect of Preparation Method of Multi-Walled Carbon Nanotube/poly(methyl Methacrylate) Nanocomposite on Its Characteristics.

Interfacial Distribution of PMMA-grafted MWCNTs in Immiscible Blends for Improved Electrical Conductivity

Investigation on the Multiwalled Carbon Nanotubes Reinforced Polyamide 6/polypropylene Composites

Preparation and Rheological Characterization of Poly(methyl Methacrylate)/functionalized Multi-Walled Carbon Nanotubes Composites

Nano-CaCO 3 /polypropylene composites made with ultra-high-speed mixer

Preparation of MWCNTs/CF/PEEK Multi-Scale Composites with Good Mechanical and Electrical Conductivity by a Two-Step Process of AFP and Out-of-autoclave Tempering