Mechanical and in vitro degradation behavior of ultrafine calcium polyphosphate reinforced magnesium-alloy composites
Ailing Feng,Yong Han
DOI: https://doi.org/10.1016/j.matdes.2010.12.054
IF: 9.417
2011-01-01
Materials & Design
Abstract:Magnesium alloy (ZK60A) matrix composites reinforced with 2.5, 5, 7.5 and 10 wt.% calcium polyphosphate particles, which were sphere-like in shape with average size of about 750 nm, were fabricated by powder metallurgy. The microstructure, mechanical properties and degradation behavior in physiological saline of the composites were investigated. The obtained results show that ultrafine calcium polyphosphate particles uniformly distribute in the ZK60A matrices without voids for the composites containing 2.5 and 5 wt.% calcium polyphosphate. For the composites containing 7.5 and 10 wt.% calcium polyphosphate, however, calcium polyphosphate particles agglomerate in the ZK60A matrices, and some obvious voids appear. The ultimate tensile strengths, yield strengths and elastic moduli of the composites tend to increase when the calcium polyphosphate contents increase from 0 to 5 wt.%, however, appear to decrease with the further increase of calcium polyphosphate from 5 to 10 wt.%. The weight losses of the composites, pH values and Mg ion concentrations of the solutions immersing the composites gradually decrease with increase of calcium polyphosphate content, which indicates that the addition of more calcium polyphosphate into ZK60A alloy results in significant degradation slow-up of the composites. This can be attributed to the formation of dense corrosion product layers on the composites. The composites have good mechanical properties and controllable degradation rates and thereby have potential to be used as load-bearing bone implants. Keywords A. Magnesium-matrix composite E. Corrosion E. Mechanical 1 Introduction Traditional biomedical metal alloys such as Co–Cr–Mo, stainless steel, and titanium alloy have played an essential role in load-bearing implants for the repair or replacement of diseased or damaged bone [1,2] . However, the elastic modulus of these metal alloys is much higher than that of bone, leading to stress shielding and bone absorption [1] . Compared with the traditional metals alloys, a biodegradable material will not cause permanent physical irritation, avoiding the secondary surgery to remove implants [3] . In recent years, magnesium and its alloys have attracted great attention for orthopedic applications due to their biodegradable nature [4] . Moreover, the Young’s modulus of Mg and its alloys is about 45 GPa, much close to that of the human bone (10–15 GPa [5] ), which will minimize stress shielding effects [1,6] . Magnesium and its alloys also exhibit non-toxicity and good biocompatibility. For example, the presence of Mg enhances bone cell adhesion and has no inhibitory effect on cell growth [7] . Witte et al. indicated that high magnesium ion concentration even could lead to bone cell activation [8] . AZ91D alloy caused no significant harm to their neighboring tissues, could react in vivo with an appropriate inflammatory host response in a rabbit model and promoted both bone formation and resorption [9] . Li et al. reported that high activities of osteoblast and osteocytes were observed around the Mg–1Ca alloy pin for 1, 2 and 3 months [10] . However, the major drawbacks of magnesium and its alloys are their fast degradation rate in the physiological environment. The fast degradation of magnesium alloys not only results in losing their mechanical integrity before the injured tissues have sufficient time to heal [11] , but also leads to serious hydrogen evolution and alkalization of body fluid [12] . Up till now, three routines have been developed to solve the fast degradation rate of magnesium and its alloys. One is alloying magnesium with non-toxic elements such as Ca [10] , Zn and Zr [13] to form novel magnesium alloys. The second is surface modification of traditional magnesium alloys, such as coating Ca–P [14] , bone-like apatite [1] , brushite [15] , hydroxyapatite [6,16] layers on the alloys. An alternative routine is to form magnesium-matrix composite reinforced with bioactive ceramic. Recently, Witte et al. [17] reported a potential of AZ91D magnesium-matrix composites reinforced with hydroxyapatite (HA) particles for load-bearing applications. In this magnesium-matrix composites, however, the AZ91D matrix contains toxic element Al which appears to be the impairment of phosphorous metabolism and its resultant adverse effects [18] ; and also HA is a bioceramic with slow degradation rate, there being a risk that the HA particles remained from the completely degraded matrix could react with macrophages resulting in bone osteolysis [19] . To be suitable implant materials, Mg-alloys based composites should possess certain properties [3] : appropriate mechanical characteristics to offer adequate mechanical support to the injured tissue; a moderate degradation to effectively assist the healing process and to prevent from early destabilization; released ions during degradation need to be biocompatible. As known, ZK60A is a magnesium alloy containing non-toxic elements of Zn and Zr [20,21] . Calcium polyphosphate (CPP) is a polymeritic ceramic with good biocompatibility and osteoconductivity, exhibiting a stoichiometry of Ca(PO 3 ) 2 and a linear regular tetrahedral polymer structure based of PO 4 units [22–25] . It seems to promote rapid bone growth and can be tailored to degrade at a given rate in vivo to some degree through appropriate selection of the starting particle size [26] , and degradation products are Ca 2+ , HPO 4 2 - , PO 4 3 - [27,28] . This paper reports our effort to prepare novel magnesium-matrix composites, composed of ZK60A matrix reinforced with CPP particles, focusing on the microstructure, mechanical and degradation properties of the CPP p /ZK60A composites. 2 Experimental procedures The composites of ZK60A reinforced with four different percentage (2.5, 5, 7.5 and 10 wt.%) of CPP particles were synthesized by a powder metallurgy process as follows. The used ZK60A powder (WeiHao Corporation of China) were less than 50 μm in size, and had a composition of 5.21 wt.% Zn, 0.34 wt.% Zr and balanced Mg. Bulk CPP was prepared according to Ref. [29] , and then mounted in a high energy ball mill (pulverisette 4 Vario-Plantary Mill, Fritsch) to produce fine CPP powder under the condition of ball-to-powder weight ratio of 10 at 400 rpm for 16 h. Four kinds of mixed powders with CPP contents of 2.5, 5, 7.5 and 10 wt.% were obtained by addition of CPP into ZK60A and mixing them using a three-dimension blending machine in argon atmosphere at a rotation speed of 50 rpm for 8 h. The mixed ZK60A and CPP powders were then dried at 120 °C in a vacuum oven for 2 h. Each kind of the mixed powder was cold-pressed into cylindrical compact with diameter 40 mm at pressure of 400 MPa. The cylindrical compact was then hot-pressed at temperature of 380 °C and pressure of 150 MPa for 20 min, followed by hot extrusion at 380 °C to a rod of 10 mm in diameter. For comparison purpose, monolithic ZK60A rod was prepared using similar processing steps. The sizes of the fine CPP particles were measured with laser particle size analyzer (Mastersizer 2000, Malvern Instruments) and observed by transmission electron microscopy (TEM; JEM-2100F, JEOL). The samples cut from the composites rods were ground with SiC papers, polished with diamond paste, and then etched in an acetic picric solution for 10 s at room temperature. Their microstructures were conducted using scanning electron microscopy (SEM; JSM-7000F, JEOL) coupled with energy dispersive spectroscopy. X-ray diffraction (XRD) analysis was carried out using a RIGAKU D/MAX-2400 diffractometer with Cu K α ray ( λ = 1.5406 Å) at a scan step of 0.02°. The tensile tests of the composites were performed using an Instron 1195 universal testing machine. For tensile tests, specimens with 5 mm in diameter and 25 mm in gauge length were machined from the extruded rods with tensile axes parallel to the extrusion direction. In vitro degradation investigations were performed by immersing the composites samples in 50 ml physiological saline opened to air at 37 °C for 1 to 12 days, without refreshing the solutions during the experiments. The tested specimens were 9.5 mm in diameter and 3 mm in height. Once the tests were finished for each immersion time, the samples were extracted from the solutions, rinsed with distilled water, dried in hot air, and their surface morphologies were observed using SEM without removing corrosion product. The weight loss percentage of each composite sample subjected to physiological saline immersion was calculated from the expression ( M 0 − M 1 )/ M 0 , where ‘ M 0 ’ is the initial weight and ‘ M 1 ’ is the final weight which was obtained by weighting the sample after removing the corrosion product with chromic acid. The pH values, Mg and Ca concentrations of the samples-immersed solutions were measured with pH meter (PHSJ-4A, Leici) and inductively coupled plasma atomic emission spectrometry (ICP-AES; IRIS-Advantage, Thermo Fisher Scientific Incorporation), respectively. 3 Results and discussion 3.1 Microstructure characterization of the ball-milled CPP powder and composites In Fig. 1 shows the XRD profiles of the starting ceramic powder before and after high energy ball milling which is identified as the β-CPP particles. After high energy ball milling, it had been observed that the tendency of grain refinement or amorphous nature was obvious due to the broad diffraction bands. The typical SEM graph of the ball-milled CPP particles is presented in Fig. 2 , in which the upper inset shows their TEM image and the lower inset shows the curve of their size distribution. It indicates that the particles appear sphere or sphere-like, having the highest probability of size at 750 nm. In comparison with triangular or multiangular particles, the sphere or sphere-like particles may avoid stress concentration and subsequently the initiation and propagation of crack upon loading of particle-reinforced composite [30] . In Fig. 3 shows the microstructures of the CPP p /ZK60A composites with different CPP contents. It is indicated that the ultrafine CPP particles uniformly distribute in the ZK60A matrices without voids for the composites containing 2.5 and 5 wt.% CPP. For the composites containing 7.5 and 10 wt.% CPP, however, CPP particles agglomerate in the ZK60A matrices, and some obvious voids appear. Moreover, agglomeration of CPP particles in the composites is enhanced with addition of CPP from 7.5 to 10 wt.%. As an example, the inset in Fig. 3 b shows a morphology of particle/matrix interface and elements profiles around the interface in the composite containing 5 wt.% CPP, indicating that CPP particles can tightly bond to matrix. The elements profiles present that the magnesium content decreases gradually while the calcium, phosphorus and oxygen contents increase gradually from the matrix to the reinforcement, which reveals extremely limited mutual solubility between CPP and Mg matrix during processing. The reasonably uniform distribution of CPP particles for the 2.5% and 5% CPP composites can be attributed to suitable mixing parameters and the high extrusion ratio used in secondary processing [31] . However, a limited amount of clustering of reinforcement was unavoidable in high content of CPP, owing to the high surface energy associated with the ultrafine particles [30] . Fig. 4 presents the XRD results of the CPP p /ZK60A composites. In addition to the peaks attributed to Mg, there are distinguishable CPP peaks in the XRD patterns. It is shown that the CPP peaks are stronger in 10 wt.% CPP-containing composite than those in 5 wt.% CPP-containing composite. There is no obvious reaction product between CPP and Mg in XRD patterns. Based on the report that intermetallic phases could cause embrittlement and weaken the interfacial bonding of particle/matrix and in turn affect the mechanical properties of the composites [32] , it is expected that no existence of reactive product between CPP and Mg can improve the properties of CPP p /ZK60A composites. 3.2 Mechanical properties of the composites Fig. 5 exhibits the effect of CPP content on the mechanical properties of the CPP p /ZK60A composites. As shown in Fig. 5 , the ultimate tensile strengths (UTS), yield strengths (YS) and elastic moduli ( E ) of the composites tend to increase when the CPP contents increase from 0 to 5 wt.%, however, appear to decrease with the further increase of CPP from 5 to 10 wt.%. The maximum UTS and YS, obtained from the 5 wt.% CPP-containing composite, are about 337.4 MPa and 319.5 MPa, higher than those of ZK60A by 21.4% and 30.5%, respectively. The increase in strengths of the composites can be attributed to the combined effects of the following factors: (a) Orowan strengthening, e.g., owing to the presence of the dispersed small-size particles in the matrix, dislocation loops form as dislocation lines bow and bypass the particles; (b) good interfacial bonding between the ZK60A and the CPP particles (as shown in Fig. 3 b) gives rise to effective load transfer from matrix to CPP particles which have larger load-bearing capacity; (c) formation of internal thermal stress due to large difference in coefficient of thermal expansion between the matrix and CPP particles; (d) work hardening due to strain misfit between the reinforcing particles and matrix; (e) sphere-shaped reinforcements that have the effect of reducing interparticle spacing and the large surface area of submicron-size CPP particles that have the capability of generating more dislocations; Moreover, a large number of reinforcing CPP particles act as obstacles to the dislocation movement and end up with dislocation pile ups [30,33–35] . It may be noted that, based on the contributions by the above-mentioned strengthening mechanisms, the strengths of the composites should increase invariably with increasing weight fraction of CPP particles. However, the strengths of the composites tend to decrease when the CPP contents increase from 5 to 10 wt.%. This could be attributed to the presence of comparatively larger clusters of CPP particles and obvious voids. The agglomeration of CPP particles may lead to weak combination among CPP particles and grain boundary embrittlement thus reducing the strengths of the composites. At higher magnifications in Fig. 3 e and f, the particles in the composite with CPP contents of 5 wt.% were less than 5 μm, but most of the particle clusters in the composite with CPP contents of 10 wt.% were more than 5 μm. So it is also likely to reduce the contribution of Orowan strengthening in the composite with CPP contents of 10 wt.% once the clusters grow beyond a critical size of 5 μm [31] . So the maximum strengths were presented for the composites when a threshold amount of CPP particles were added in the matrix. In the present work, the maximum improvement of strength was obtained in the case of the CPP addition amount of 5 wt.%. It is known that the tensile strength of the cortical bone is 35–283 MPa [36] . The prepared CPP p /ZK60A composites have tensile yield strength of 240–300 MPa, which are higher than those of natural bone. On the other hand, increase in the elastic moduli of the composites containing 2.5 and 5 wt.% CPP can be attributed to the presence of: (a) the high modulus of reinforcement; (b) uniform distribution of reinforcement with good interfacial integrity which leads to a significant increase in internal stress between reinforcement and matrix resulting in the enhancement of elastic modulus; (c) the high loading transfer capacity of matrix–reinforcement interfaces [37,38] . Such defects as porosity may reduce the elastic modulus when the contents of CPP increase from 5% to 10% [38] . The elastic modulus (43–47 GPa) of the composites is close to that of human bone, suggesting that the CPP p /ZK60A composites are promising candidates for implants to reduce stress shielding and bone absorption. Fig. 6 shows SEM micrographs of the tensile fracture surfaces of ZK60A alloy and composites containing 5 and 10 wt.% CPP. Many ductile dimples can be observed on the fracture surfaces of all the samples. It is worth noticing that in addition to ductile dimples the 10 wt.% CPP-containing composite is coupled with interfacial detachment between CPP and matrix, leaving big pores on its fracture surface (as marked in Fig. 6 c). Such change in fracture morphologies of the samples can be explained as follows. Alloying with Zn may promote activation of non-basal slip system which is necessary to transform typical cleavage failure of magnesium to ductile fracture of ZK60A [39,40] . Under tensile load, fine microscopic voids including grain boundary ledges appear and propagate by the void-sheet mechanism following coalesce to ductile dimples on the fracture surface of ZK60A alloy [39] . It is reported that reinforced particles in Mg-alloy matrix composite could further activate non-basal slip system of Mg-alloy matrix [34,39] . Therefore, ductile dimples appear on the tensile fracture surfaces of the CPP p /ZK60A composites. When tensile load was applied to the composite, stress concentration may develop in regions such as the reinforcements and reinforcement/matrix interfaces. As the concentrated stress increases to a certain level, excessive dislocations might pile up at reinforcement/matrix interfaces leading to interfacial detachment between CPP and matrix, as suggested elsewhere [37,38,41] . 3.3 In vitro degradation behavior of the composites In Fig. 7 a illustrates weight changes of the ZK60A alloy and CPP p /ZK60A composites after immersing in physiological saline for 1 to 12 days. Although the weight losses of each kind of composite samples tend to increase with immersion time, the weight losses of the composites samples gradually decrease with increase of CPP content at each immersion time. The pH values, Mg and Ca concentrations of the solutions immersing the composites samples are shown in Fig. 7 b–d. It is revealed that the pH values, Mg and Ca ion concentrations of the solutions immersing each kind of composite samples tend to increase as the immersion time is prolonged. However, the addition of more CPP into ZK60A alloy results in significant decrease in pH values and Mg ion concentrations of the solutions immersing the composite samples at each immersion time. The aforementioned results indicate that the degradation rates of the composites decrease gradually with the increase of CPP content. The pH value around implants is an important factor which can affect the cell differentiation, proliferation, and function [1] . It has been reported that a small piece (1 × 1 × 1 cm 3 ) of Mg coupon, which reacts with water to form Mg(OH) 2 and H 2 [42] , could give rise to an increase in pH value of 250 ml neutral Hank solution to 10 in 15 h [12] . The alkalization can unfavorably affect the pH dependent physiological reaction balances in the vicinity of the magnesium implant and may even lead to an alkaline poisoning effect [12] . High pH value not only cause serious hemolysis [43] , but also is not suitable for the cell differentiation, proliferation, and function [44] . In the present work, the addition of CPP into ZK60A alloy results in significant decrease in pH values of the solutions immersing the composites compared with ZK60A alloy at each immersion time. For example, after immersion for 12 day, the solution immersing 10 wt.% CPP-containing composite sample exhibits a pH value as low as 9.64. It is expected that the CPP p /ZK60A composites could present an improved biological response. After soaking in physiological saline for 12 days, in the case without removing any corrosive products, the ZK60A alloy and CPP p /ZK60A composites samples reveal XRD peaks of Mg and Mg(OH) 2 , as shown in Fig. 8 , indicating that the corrosive products of the samples in physiological saline are composed of Mg(OH) 2 . However, the morphologies of the corrosive layers on the samples are quite different, as shown in Fig. 9 . The Mg(OH) 2 layer on ZK60A alloy exhibits much rougher morphology than those on composites containing 5 and 10 wt.% CPP at low magnification, but also reveals a porous and plate-like crystalline morphology at high magnification (insert in Fig. 9 a). At high magnification, the layers on the composites become dense and the plate-like crystalline of Mg(OH) 2 become fine with the increase of CPP contents (inserts in Fig. 9 b and c). Fig. 9 d shows the cross-sectional morphology of the 10 wt.% CPP-containing composite after soaking in physiological saline for 12 days, also revealing a dense structure of the formed Mg(OH) 2 layer; furthermore, EDS spectrum detected on the cross-section of the layer indicates that there are a small amount of Ca to incorporate into the Mg(OH) 2 layer ( Fig. 9 e). Although the reason for change in the morphologies of the Mg(OH) 2 layers on the composites with addition of CPP is not clear at present, the formation of compact layers is thought to play a positive role in slow-up of degradation of composites. In fact, it is known that chloride ions in physiological saline preferentially combine with magnesium ions to transform Mg(OH) 2 into soluble MgCl 2 , causing breakdown of Mg(OH) 2 layer and pitting corrosion [45] . However, addition of small amount of Ca to AS41 (Mg–Al–Si) alloy could stabilize Mg(OH) 2 layer, which were attributed to incorporation of Ca 2+ in the layer, causing it to be more protective, as reported by Bakkar and Neubert [46] . Based on the previous work and Fig. 9 e, Ca 2+ generated by degradation of CPP in our composites may be adulterated into the Mg(OH) 2 layers, further enhancing their stability and thereby corrosion resistance of the composites. 4 Conclusions CPP particles reinforced ZK60A magnesium alloy matrix composites can be synthesized by powder metallurgy technique. The ultrafine CPP particles uniformly distribute in the ZK60A matrices without voids for the composites containing 2.5 and 5 wt.% CPP. For the composites containing 7.5 and 10 wt.% CPP, however, CPP particles agglomerate in the ZK60A matrices, and some obvious voids appear. The ultimate tensile strengths, yield strengths and elastic moduli of the composites tend to increase when the CPP contents increase from 0 to 5 wt.%, however, appear to decrease with the further increase of CPP from 5 to 10 wt.%. The results of the immersion test indicate that the corrosion rates decrease gradually with the increase of CPP contents. The addition of CPP into ZK60A alloy results in significant decrease in pH values of the solutions immersing the composites compared with ZK60A alloy, which may be caused by the acid degradation products of CPP and decreasing degradation rates of the composites. The corrosive products on the ZK60A alloy and composites immersed in physiological saline are composed of Mg(OH) 2 . The corrosive product layers on the composites are dense compared with the ZK60A alloy which is thought to play a positive role in slow-up of degradation of composites. The CPP p /ZK60A composites exhibit improved mechanical properties and corrosion resistance and thereby could be used as orthopedic implants for load-bearing applications. Acknowledgements We appreciate the National High Technology Research and Development Program of China (Grant number 2006AA03Z0447), and National Natural Science Foundation of China (Grant numbers 51071120, 50671078) for financially supporting this work. The authors also gratefully acknowledge Prof. Donglang Chai for his technical assistance. References [1] A. Pietak P. Mahoney G.J. Dias M.P. Staiger Bone-like matrix formation on magnesium and magnesium alloys J Mater Sci Mater Med 19 2008 407 415 [2] Y. Yun Z. Dong D. Yang M.J. Schulz V.N. Shanov S. Yarmolenko Biodegradable Mg corrosion and osteoblast cell culture studies Mater Sci Eng C 29 2009 1814 1821 [3] G. Song S. Song A possible biodegradable magnesium implant material Adv Eng Mater 9 2007 298 302 [4] C. Liu Y. Xin X. Tian J. Zhao P.K. Chu Corrosion resistance of titanium ion implanted AZ91 magnesium alloy J Vac Sci Technol A 25 2007 334 339 [5] F.E. Heakal A.M. Fekry M.Z. Fatayerji Electrochemical behavior of AZ91D magnesium alloy in phosphate medium: part II: induced passivation J Appl Electrochem 39 2009 1633 1642 [6] C. Wen S. Guan L. Peng C. Ren X. Wang Z. Hu Characterization and degradation behavior of AZ31 alloy surface modified by bone-like hydroxyapatite for implant applications Appl Surf Sci 255 2009 6433 6438 [7] M.P. Staiger A.M. Pietak J. Huadmai G. Dias Magnesium and its alloys as orthopedic biomaterials: a review Biomaterials 27 2006 1728 1734 [8] F. Witte V. Kaese H. Haferkamp E. Switzer A. Meyer-Lindenberg C.J. Wirth In vivo corrosion of four magnesium alloys and the associated bone response Biomaterials 26 2005 3557 3563 [9] F. Witte H. Ulrich C. Palm E. Willbold Biodegradable magnesium scaffolds: part II: peri-implant bone remodeling J Biomed Mater Res Part A 81A 2007 757 765 [10] Z. Li X. Gu S. Lou Y. Zheng The development of binary Mg–Ca alloys for use as biodegradable materials within bone Biomaterials 29 2008 1329 1344 [11] F. Witte J. Fischer J. Nellesen H.A. Crostack V. Kaese A. Pisch In vitro and in vivo corrosion measurements of magnesium alloys Biomaterials 27 2006 1013 1018 [12] G. Song Control of biodegradation of biocompatable magnesium alloys Corros Sci 49 2007 1696 1701 [13] X. Gu Y. Zheng Y. Cheng S. Zhong T. Xi In vitro corrosion and biocompatibility of binary magnesium alloys Biomaterials 30 2009 484 498 [14] L. Xu F. Pan G. Yu L. Yang E. Zhang K. Yang In vitro and in vivo evaluation of the surface bioactivity of a calcium phosphate coated magnesium alloy Biomaterials 30 2009 1512 1523 [15] L. Xu E. Zhang K. Yang Phosphating treatment and corrosion properties of Mg–Mn–Zn alloy for biomedical application J Mater Sci-Mater Med 20 2009 859 867 [16] Y.W. Song D.Y. Shan E.H. Han Electrodeposition of hydroxyapatite coating on AZ91D magnesium alloy for biomaterial application Mater Lett 62 2008 3276 3279 [17] F. Witte F. Feyerabend P. Maier J. Fischer M. Stormer C. Blawert Biodegradable magnesium-hydroxyapatite metal matrix composites Biomaterials 28 2007 2163 2174 [18] F. Witte H. Ulrich M. Rudert E. Willbold Biodegradable magnesium scaffolds: part I: appropriate inflammatory response J Biomed Mater Res Part A 81A 2007 748 756 [19] S. Landgraeber M. von Knoch F. Loer A. Wegner M. Tsokos B. Hussmann Extrinsic and intrinsic pathways of apoptosis in aseptic loosening after total hip replacement Biomaterials 29 2008 3444 3450 [20] W.A. House Trace element bioavailability as exemplified by iron and zinc Field Crop Res 60 1999 115 141 [21] L. Saldana A. Mendez-Vilas L. Jiang M. Multigner J.L. Gonzalez-Carrasco M.T. Perez-Prado In vitro biocompatibility of an ultrafine grained zirconium Biomaterials 28 2007 4343 4354 [22] K. Qiu C.X. Wan C.S. Zhao X. Chen C.W. Tang Y.W. Chen Fabrication and characterization of porous calcium polyphosphate scaffolds J Mater Sci 41 2006 2429 2434 [23] L.E. Jackson B.M. Kariuki M.E. Smith J.E. Barralet A.J. Wright Synthesis and structure of a calcium polyphosphate with a unique criss-cross arrangement of helical phosphate chains Chem Mater 17 2005 4642 4646 [24] Y.M. Lee Y.J. Seol Y.T. Lim S. Kim S.B. Han I.C. Rhyu Tissue-engineered growth of bone by marrow cell transplantation using porous calcium metaphosphate matrices J Biomed Mater Res 54 2001 216 2123 [25] S.D. Waldman M.D. Grynpas R.M. Pilliar R.A. Kandel Characterization of cartilaginous tissue formed on calcium polyphosphate substrates in vitro J Biomed Mater Res 62 2002 323 3230 [26] M.D. Grynpas R.M. Pilliar R.A. Kandel R. Renlund M. Filiaggi M. Dumitriu Porous calcium polyphosphate scaffolds for bone substitute applications in vivo studies Biomaterials 23 2002 2063 2070 [27] K. Wang F. Chen C. Liu C. Rüssel The effect of polymeric chain-like structure on the degradation and cellular biocompatibility of calcium polyphosphate Mater Sci Eng C 28 2008 1572 1578 [28] W. Song M. Tian F. Chen Y. Tian C. Wan X. Yu The study on the degradation and mineralization mechanism of ion-doped calcium polyphosphate in vitro J Biomed Mater Res Part B 89B 2009 430 438 [29] R.M. Pilliar M.J. Filiaggi J.D. Wells M.D. Grynpas R.A. Kandel Porous calcium polyphosphate scaffolds for bone substitute applications – in vitro characterization Biomaterials 22 2001 963 972 [30] X.L. Zhong W.L.E. Wong M. Gupta Enhancing strength and ductility of magnesium by integrating it with aluminum nanoparticles Acta Mater 55 2007 6338 6344 [31] W.L.E. Wong M. Gupta Development of Mg/Cu nanocomposites using microwave assisted rapid sintering Compos Sci Technol 67 2007 1541 1552 [32] B.W. Chua L. Lu M.O. Lai Influence of SiC particles on mechanical properties of Mg based composite Compos Struct 47 1999 595 601 [33] M. Habibnejad-Korayem R. Mahmudi W.J. Poole Enhanced properties of Mg-based nano-composites reinforced with Al 2 O 3 nano-particles Mater Sci Eng A 519 2009 198 203 [34] C.S. Goh J. Wei L.C. Lee M. Gupta Development of novel carbon nanotube reinforced magnesium nanocomposites using the powder metallurgy technique Nanotechnology 17 2006 7 12 [35] S.F. Hassan M. Gupta Development of ductile magnesium composite materials using titanium as reinforcement J Alloys Compd 345 2002 246 251 [36] F. Witte N. Hort C. Vogt S. Cohen K.U. Kainer R. Willumeit Degradable biomaterials based on magnesium corrosion Curr Opin Solid State Mater Sci 12 2008 63 72 [37] S.F. Hassan M. Gupta Development of high performance magnesium nano-composites using nano-Al 2 O 3 as reinforcement Mater Sci Eng A 392 2005 163 168 [38] Y.L. Xi D.L. Chai W.X. Zhang J.E. Zhou Titanium alloy reinforced magnesium matrix composite with improved mechanical properties Scr Mater 54 2006 19 23 [39] S.F. Hassan M. Gupta Development of nano-Y 2 O 3 containing magnesium nanocomposites using solidification processing J Alloys Compd 429 2007 176 183 [40] S.R. Agnew O. Duygulu Plastic anisotropy and the role of non-basal slip in magnesium alloy AZ31B Int J Plast 21 2005 1161 1193 [41] N. Afrin D.L. Chen X. Cao M. Jahazi Microstructure and tensile properties of friction stir welded AZ31B magnesium alloy Mater Sci Eng A 472 2008 179 186 [42] S. Zhang X. Zhang C. Zhao J. Li Y. Song C. Xie Research on an Mg–Zn alloy as a degradable biomaterial Acta Biomater 6 2010 626 640 [43] E. Zhang D. Yin L. Xu L. Yang K. Yang Microstructure, mechanical and corrosion properties and biocompatibility of Mg–Zn–Mn alloys for biomedical application Mater Sci Eng C 29 2009 987 993 [44] E. Zhang L. Yang J. Xu H. Chen Microstructure, mechanical properties and bio-corrosion properties of Mg–Si(–Ca, Zn) alloy for biomedical application Acta Biomater 6 2010 1756 1762 [45] S. Tiwari R. Balasubramaniam M. Gupta Corrosion behavior of SiC reinforced magnesium composites Corros Sci 49 2007 711 725 [46] A. Bakkar V. Neubert Corrosion behaviour of carbon fibres/magnesium metal matrix composite and electrochemical response of its constituents Electrochim Acta 54 2009 1597 1606