Mechanical and in vitro degradation behavior of ultrafine calcium polyphosphate reinforced magnesium-alloy composites
Ailing Feng,Yong Han
DOI: https://doi.org/10.1016/j.matdes.2010.12.054
IF: 9.417
2011-01-01
Materials & Design
Abstract:Magnesium alloy (ZK60A) matrix composites reinforced with 2.5, 5, 7.5 and 10 wt.% calcium polyphosphate particles, which were sphere-like in shape with average size of about 750 nm, were fabricated by powder metallurgy. The microstructure, mechanical properties and degradation behavior in physiological saline of the composites were investigated. The obtained results show that ultrafine calcium polyphosphate particles uniformly distribute in the ZK60A matrices without voids for the composites containing 2.5 and 5 wt.% calcium polyphosphate. For the composites containing 7.5 and 10 wt.% calcium polyphosphate, however, calcium polyphosphate particles agglomerate in the ZK60A matrices, and some obvious voids appear. The ultimate tensile strengths, yield strengths and elastic moduli of the composites tend to increase when the calcium polyphosphate contents increase from 0 to 5 wt.%, however, appear to decrease with the further increase of calcium polyphosphate from 5 to 10 wt.%. The weight losses of the composites, pH values and Mg ion concentrations of the solutions immersing the composites gradually decrease with increase of calcium polyphosphate content, which indicates that the addition of more calcium polyphosphate into ZK60A alloy results in significant degradation slow-up of the composites. This can be attributed to the formation of dense corrosion product layers on the composites. The composites have good mechanical properties and controllable degradation rates and thereby have potential to be used as load-bearing bone implants. Keywords A. Magnesium-matrix composite E. Corrosion E. Mechanical 1 Introduction Traditional biomedical metal alloys such as Co–Cr–Mo, stainless steel, and titanium alloy have played an essential role in load-bearing implants for the repair or replacement of diseased or damaged bone [1,2] . However, the elastic modulus of these metal alloys is much higher than that of bone, leading to stress shielding and bone absorption [1] . Compared with the traditional metals alloys, a biodegradable material will not cause permanent physical irritation, avoiding the secondary surgery to remove implants [3] . In recent years, magnesium and its alloys have attracted great attention for orthopedic applications due to their biodegradable nature [4] . Moreover, the Young’s modulus of Mg and its alloys is about 45 GPa, much close to that of the human bone (10–15 GPa [5] ), which will minimize stress shielding effects [1,6] . Magnesium and its alloys also exhibit non-toxicity and good biocompatibility. For example, the presence of Mg enhances bone cell adhesion and has no inhibitory effect on cell growth [7] . Witte et al. indicated that high magnesium ion concentration even could lead to bone cell activation [8] . AZ91D alloy caused no significant harm to their neighboring tissues, could react in vivo with an appropriate inflammatory host response in a rabbit model and promoted both bone formation and resorption [9] . Li et al. reported that high activities of osteoblast and osteocytes were observed around the Mg–1Ca alloy pin for 1, 2 and 3 months [10] . However, the major drawbacks of magnesium and its alloys are their fast degradation rate in the physiological environment. The fast degradation of magnesium alloys not only results in losing their mechanical integrity before the injured tissues have sufficient time to heal [11] , but also leads to serious hydrogen evolution and alkalization of body fluid [12] . Up till now, three routines have been developed to solve the fast degradation rate of magnesium and its alloys. One is alloying magnesium with non-toxic elements such as Ca [10] , Zn and Zr [13] to form novel magnesium alloys. The second is surface modification of traditional magnesium alloys, such as coating Ca–P [14] , bone-like apatite [1] , brushite [15] , hydroxyapatite [6,16] layers on the alloys. An alternative routine is to form magnesium-matrix composite reinforced with bioactive ceramic. Recently, Witte et al. [17] reported a potential of AZ91D magnesium-matrix composites reinforced with hydroxyapatite (HA) particles for load-bearing applications. In this magnesium-matrix composites, however, the AZ91D matrix contains toxic element Al which appears to be the impairment of phosphorous metabolism and its resultant adverse effects [18] ; and also HA is a bioceramic with slow degradation rate, there being a risk that the HA particles remained from the completely degraded matrix could react with macrophages resulting in bone osteolysis [19] . To be suitable implant materials, Mg-alloys based composites should possess certain properties [3] : appropriate mechanical characteristics to offer adequate mechanical support to the injured tissue; a moderate degradation to effectively assist the healing process and to prevent from early destabilization; released ions during degradation need to be biocompatible. As known, ZK60A is a magnesium alloy containing non-toxic elements of Zn and Zr [20,21] . Calcium polyphosphate (CPP) is a polymeritic ceramic with good biocompatibility and osteoconductivity, exhibiting a stoichiometry of Ca(PO 3 ) 2 and a linear regular tetrahedral polymer structure based of PO 4 units [22–25] . It seems to promote rapid bone growth and can be tailored to degrade at a given rate in vivo to some degree through appropriate selection of the starting particle size [26] , and degradation products are Ca 2+ , HPO 4 2 - , PO 4 3 - [27,28] . This paper reports our effort to prepare novel magnesium-matrix composites, composed of ZK60A matrix reinforced with CPP particles, focusing on the microstructure, mechanical and degradation properties of the CPP p /ZK60A composites. 2 Experimental procedures The composites of ZK60A reinforced with four different percentage (2.5, 5, 7.5 and 10 wt.%) of CPP particles were synthesized by a powder metallurgy process as follows. The used ZK60A powder (WeiHao Corporation of China) were less than 50 μm in size, and had a composition of 5.21 wt.% Zn, 0.34 wt.% Zr and balanced Mg. Bulk CPP was prepared according to Ref. [29] , and then mounted in a high energy ball mill (pulverisette 4 Vario-Plantary Mill, Fritsch) to produce fine CPP powder under the condition of ball-to-powder weight ratio of 10 at 400 rpm for 16 h. Four kinds of mixed powders with CPP contents of 2.5, 5, 7.5 and 10 wt.% were obtained by addition of CPP into ZK60A and mixing them using a three-dimension blending machine in argon atmosphere at a rotation speed of 50 rpm for 8 h. The mixed ZK60A and CPP powders were then dried at 120 °C in a vacuum oven for 2 h. Each kind of the mixed powder was cold-pressed into cylindrical compact with diameter 40 mm at pressure of 400 MPa. The cylindrical compact was then hot-pressed at temperature of 380 °C and pressure of 150 MPa for 20 min, followed by hot extrusion at 380 °C to a rod of 10 mm in diameter. For comparison purpose, monolithic ZK60A rod was prepared using similar processing steps. The sizes of the fine CPP particles were measured with laser particle size analyzer (Mastersizer 2000, Malvern Instruments) and observed by transmission electron microscopy (TEM; JEM-2100F, JEOL). The samples cut from the composites rods were ground with SiC papers, polished with diamond paste, and then etched in an acetic picric solution for 10 s at room temperature. Their microstructures were conducted using scanning electron microscopy (SEM; JSM-7000F, JEOL) coupled with energy dispersive spectroscopy. X-ray diffraction (XRD) analysis was carried out using a RIGAKU D/MAX-2400 diffractometer with Cu K α ray ( λ = 1.5406 Å) at a scan step of 0.02°. The tensile tests of the composites were performed using an Instron 1195 universal testing machine. For tensile tests, specimens with 5 mm in diameter and 25 mm in gauge length were machined from the extruded rods with tensile axes parallel to the extrusion direction. In vitro degradation investigations were performed by immersing the composites samples in 50 ml physiological saline opened to air at 37 °C for 1 to 12 days, without refreshing the solutions during the experiments. The tested specimens were 9.5 mm in diameter and 3 mm in height. Once the tests were finished for each immersion time, the samples were extracted from the solutions, rinsed with distilled water, dried in hot air, and their surface morphologies were observed using SEM without removing corrosion product. The weight loss percentage of each composite sample subjected to physiological saline immersion was calculated from the expression ( M 0 − M 1 )/ M 0 , where ‘ M 0 ’ is the initial weight and ‘ M 1 ’ is the final weight which was obtained by weighting the sample after removing the corrosion product with chromic acid. The pH values, Mg and Ca concentrations of the samples-immersed solutions were measured with pH meter (PHSJ-4A, Leici) and inductively coupled plasma atomic emission spectrometry (ICP-AES; IRIS-Advantage, Thermo Fisher Scientific Incorporation), respectively. 3 Results and discussion 3.1 Microstructure characterization of the ball-milled CPP powder and composites In Fig. 1 shows the XRD profiles of the starting ceramic powder before and after high energy ball milling which is identified as the β-CPP particles. After high energy ball milling, it had been observed that the tendency of grain refinement or amorphous nature was obvious due to the broad diffraction bands. The typical SEM graph of the ball-milled CPP particles is presented in Fig. 2 , in which the upper inset shows their TEM image and the lower inset shows the curve of their size distribution. It indicates that the particles appear sphere or sphere-like, having the highest probability of size at 750 nm. In comparison with triangular or multiangular particles, the sphere or sphere-like particles may avoid stress concentration and subsequently the initiation and propagation of crack upon loading of particle-reinforced composite [30] . In Fig. 3 shows the microstructures of the CPP p /ZK60A composites with different CPP contents. It is indicated that the ultrafine CPP particles uniformly distribute in the ZK60A matrices without voids for the composites containing 2.5 and 5 wt.% CPP. For the composites containing 7.5 and 10 wt.% CPP, however, CPP particles agglomerate in the ZK60A matrices, and some obvious voids appear. Moreover, agglomeration of CPP particles in the composites is enhanced with addition of CPP from 7.5 to 10 wt.%. As an example, the inset in Fig. 3 b shows a morphology of particle/matrix interface and elements profiles around the interface in the composite containing 5 wt.% CPP, indicating that CPP particles can tightly bond to matrix. The elements profiles present that the magnesium content decreases gradually while the calcium, phosphorus and oxygen contents increase gradually from the matrix to the reinforcement, which reveals extremely limited mutual solubility between CPP and Mg matrix during processing. The reasonably uniform distribution of CPP particles for the 2.5% and 5% CPP composites can be attributed to suitable mixing parameters and the high extrusion ratio used in secondary processing [31] . However, a limited amount of clustering of reinforcement was unavoidable in high content of CPP, owing to the high surface energy associated with the ultrafine particles [30] . Fig. 4 presents the XRD results of the CPP p /ZK60A composites. In addition to the peaks attributed to Mg, there are distinguishable CPP peaks in the XRD patterns. It is shown that the CPP peaks are stronger in 10 wt.% CPP-containing composite than those in 5 wt.% CPP-containing composite. There is no obvious reaction product between CPP and Mg in XRD patterns. Based on the report that intermetallic phases could cause embrittlement and weaken the interfacial bonding of particle/matrix and in turn affect the mechanical properties of the composites [32] , it is expected that no existence of reactive product between CPP and Mg can improve the properties of CPP p /ZK60A composites. 3.2 Mechanical properties of the composites Fig. 5 exhibits the effect of CPP content on the mechanical properties of the CPP p /ZK60A composites. As shown in Fig. 5 , the ultimate tensile strengths (UTS), yield strengths (YS) and elastic moduli ( E ) of the composites tend to increase when the CPP contents increase from 0 to 5 wt.%, however, appear to decrease with the further increase of CPP from 5 to 10 wt.%. The maximum UTS and YS, obtained from the 5 wt.% CPP-containing composite, are about 337.4 MPa and 319.5 MPa, higher than those of ZK60A by 21.4% and 30.5%, respectively. The increase in strengths of the composites can be attributed to the combined effects of the following factors: (a) Orowan strengthening, e.g., owing to the presence of the dispersed small-size particles in the matrix, dislocation loops form as dislocation lines bow and bypass the particles; (b) good interfacial bonding between the ZK60A and the CPP particles (as shown in Fig. 3 b) gives rise to effective load transfer from matrix to CPP particles which have larger load-bearing capacity; (c) formation of internal thermal stress due to large difference in coefficient of thermal expansion between the matrix and CPP particles; (d) work hardening due to strain misfit between the reinforcing particles and matrix; (e) sphere-shaped reinforcements that have the effect of reducing interparticle spacing and the large surface area of submicron-size CPP particles that have the capability of generating more dislocations; Moreover, a large number of reinforcing CPP particles act as obstacles to the dislocation movement and end up with dislocation pile ups [30,33–35] . It may be noted that, based on the contributions by the above-mentioned strengthening mechanisms, the strengths of the composites should increase invariably with increasing weight fraction of CPP particles. However, the strengths of the composites tend to decrease when the CPP contents increase from 5 to 10 wt.%. This could be attributed to the presence of comparatively larger clusters of CPP particles and obvious voids. The agglomeration of CPP particles may lead to weak combination among CPP particles and grain boundary embrittlement thus reducing the strengths of the composites. At higher magnifications in Fig. 3 e and f, the particles in the composite with CPP contents of 5 wt.% were less than 5 μm, but most of the particle clusters in the composite with CPP contents of 10 wt.% were more than 5 μm. So it is also likely to reduce the contribution of Orowan strengthening in the composite with CPP contents of 10 wt.% once the clusters grow beyond a critical size of 5 μm [31] . So the maximum strengths were presented for the composites when a threshold amount of CPP particles were added in the matrix. In the present work, the maximum improvement of strength was obtained in the case of the CPP addition amount of 5 wt.%. It is known that the tensile strength of the cortical bone is 35–283 MPa [36] . The prepared CPP p /ZK60A composites have tensile yield strength of 240–300 MPa, which are higher than those of natural bone. On the other hand, increase in the elastic moduli of the composites containing 2.5 and 5 wt.% CPP can be attributed to the presence of: (a) the high modulus of reinforcement; (b) uniform distribution of reinforcement with good interfacial integrity which leads to a significant increase in internal stress between reinforcement and matrix resulting in the enhancement of elastic modulus; (c) the high loading transfer capacity of matrix–reinforcement interfaces [37,38] . Such defects as porosity may reduce the elastic modulus when the contents of CPP increase from 5% to 10% [38] . The elastic modulus (43–47 GPa) of the composites is close to that of human bone, suggesting that the CPP p /ZK60A composites are promising candidates for implants to reduce stress shielding and bone absorption. Fig. 6 shows SEM micrographs of the tensile fracture surfaces of ZK60A alloy and composites containing 5 and 10 wt.% CPP. Many ductile dimples can be observed on the fracture surfaces of all the samples. It is worth noticing that in addition to ductile dimples the 10 wt.% CPP-containing composite is coupled with interfacial detachment between CPP and matrix, leaving big pores on its fracture surface (as marked in Fig. 6 c). Such change in fracture morphologies of the samples can be explained as follows. Alloying with Zn may promote activation of non-basal slip system which is necessary to transform typical cleavage failure of magnesium to ductile fracture of ZK60A [39,40] . Under tensile load, fine microscopic voids including grain boundary ledges appear and propagate by the void-sheet mechanism following coalesce to ductile dimples on the fracture surface of ZK60A alloy [39] . It is reported that reinforced particles in Mg-alloy matrix composite could further activate non-basal slip system of Mg-alloy matrix [34,39] . Therefore, ductile dimples appear on the tensile fracture surfaces of the CPP p /ZK60A composites. When tensile load was applied to the composite, stress concentration may develop in regions such as the reinforcements and reinforcement/matrix interfaces. As the concentrated stress increases to a certain level, excessive dislocations might pile up at reinforcement/matrix interfaces leading to interfacial detachment between CPP and matrix, as suggested elsewhere [37,38,41] . 3.3 In vitro degradation behavior of the composites In Fig. 7 a illustrates weight changes of the ZK60A alloy and CPP p /ZK60A composites after immersing in physiological saline for 1 to 12 days. Although the weight losses of each kind of composite samples tend to increase with immersion time, the weight losses of the composites samples gradually decrease with increase of CPP content at each immersion time. The pH values, Mg and Ca concentrations of the solutions immersing the composites samples are shown in Fig. 7 b–d. It is revealed that the pH values, Mg and Ca ion concentrations of the solutions immersing each kind of composite samples tend to increase as the immersion time is prolonged. However, the addition of more CPP into ZK60A alloy results in significant decrease in pH values and Mg ion concentrations of the solutions immersing the composite samples at each immersion time. The aforementioned results indicate that the degradation rates of the composites decrease gradually with the increase of CPP content. The pH value around implants is an important factor which can affect the cell differentiation, proliferation, and function [1] . It has been reported that a small piece (1 × 1 × 1 cm 3 ) of Mg coupon, which reacts with water to form Mg(OH) 2 and H 2 [42] , could give rise to an increase in pH value of 250 ml neutral Hank solution to 10 in 15 h [12] . The alkalization can unfavorably affect the pH dependent physiological reaction balances in the vicinity of the magnesium implant and may even lead to an alkaline poisoning effect [12] . High pH value not only cause serious hemolysis [43] , but also is not suitable for the cell differentiation, proliferation, and function [44] . In the present work, the addition of CPP into ZK60A alloy results in significant decrease in pH values of the solutions immersing the composites compared with ZK60A alloy at each immersion time. For example, after immersion for 12 day, the solution immersing 10 wt.% CPP-containing composite sample exhibits a pH value as low as 9.64. It is expected that the CPP p /ZK60A composites could present an improved biological response. After soaking in physiological saline for 12 days, in the case without removing any corrosive products, the ZK60A alloy and CPP p /ZK60A composites samples reveal XRD peaks of Mg and Mg(OH) 2 , as shown in Fig. 8 , indicating that the corrosive products of the samples in physiological saline are composed of Mg(OH) 2 . However, the morphologies of the corrosive layers on the samples are quite different, as shown in Fig. 9 . The Mg(OH) 2 layer on ZK60A alloy exhibits much rougher morphology than those on composites containing 5 and 10 wt.% CPP at low magnification, but also reveals a porous and plate-like crystalline morphology at high magnification (insert in Fig. 9 a). At high magnification, the layers on the composites become dense and the plate-like crystalline of Mg(OH) 2 become fine with the increase of CPP contents (inserts in Fig. 9 b and c). Fig. 9 d shows the cross-sectional morphology of the 10 wt.% CPP-containing composite after soaking in physiological saline for 12 days, also revealing a dense structure of the formed Mg(OH) 2 layer; furthermore, EDS spectrum detected on the cross-section of the layer indicates that there are a small amount of Ca to incorporate into the Mg(OH) 2 layer ( Fig. 9 e). Although the reason for change in the morphologies of the Mg(OH) 2 layers on the composites with addition of CPP is not clear at present, the formation of compact layers is thought to play a positive role in slow-up of degradation of composites. In fact, it is known that chloride ions in physiological saline preferentially combine with magnesium ions to transform Mg(OH) 2 into soluble MgCl 2 , causing breakdown of Mg(OH) 2 layer and pitting corrosion [45] . However, addition of small amount of Ca to AS41 (Mg–Al–Si) alloy could stabilize Mg(OH) 2 layer, which were attributed to incorporation of Ca 2+ in the layer, causing it to be more protective, as reported by Bakkar and Neubert [46] . Based on the previous work and Fig. 9 e, Ca 2+ generated by degradation of CPP in our composites may be adulterated into the Mg(OH) 2 layers, further enhancing their stability and thereby corrosion resistance of the composites. 4 Conclusions CPP particles reinforced ZK60A magnesium alloy matrix composites can be synthesized by powder metallurgy technique. The ultrafine CPP particles uniformly distribute in the ZK60A matrices without voids for the composites containing 2.5 and 5 wt.% CPP. For the composites containing 7.5 and 10 wt.% CPP, however, CPP particles agglomerate in the ZK60A matrices, and some obvious voids appear. The ultimate tensile strengths, yield strengths and elastic moduli of the composites tend to increase when the CPP contents increase from 0 to 5 wt.%, however, appear to decrease with the further increase of CPP from 5 to 10 wt.%. The results of the immersion test indicate that the corrosion rates decrease gradually with the increase of CPP contents. The addition of CPP into ZK60A alloy results in significant decrease in pH values of the solutions immersing the composites compared with ZK60A alloy, which may be caused by the acid degradation products of CPP and decreasing degradation rates of the composites. The corrosive products on the ZK60A alloy and composites immersed in physiological saline are composed of Mg(OH) 2 . The corrosive product layers on the composites are dense compared with the ZK60A alloy which is thought to play a positive role in slow-up of degradation of composites. The CPP p /ZK60A composites exhibit improved mechanical properties and corrosion resistance and thereby could be used as orthopedic implants for load-bearing applications. Acknowledgements We appreciate the National High Technology Research and Development Program of China (Grant number 2006AA03Z0447), and National Natural Science Foundation of China (Grant numbers 51071120, 50671078) for financially supporting this work. The authors also gratefully acknowledge Prof. Donglang Chai for his technical assistance. References [1] A. Pietak P. Mahoney G.J. Dias M.P. Staiger Bone-like matrix formation on magnesium and magnesium alloys J Mater Sci Mater Med 19 2008 407 415 [2] Y. Yun Z. Dong D. Yang M.J. Schulz V.N. Shanov S. Yarmolenko Biodegradable Mg corrosion and osteoblast cell culture studies Mater Sci Eng C 29 2009 1814 1821 [3] G. Song S. Song A possible biodegradable magnesium implant material Adv Eng Mater 9 2007 298 302 [4] C. Liu Y. Xin X. Tian J. Zhao P.K. Chu Corrosion resistance of titanium ion implanted AZ91 magnesium alloy J Vac Sci Technol A 25 2007 334 339 [5] F.E. Heakal A.M. Fekry M.Z. Fatayerji Electrochemical behavior of AZ91D magnesium alloy in phosphate medium: part II: induced passivation J Appl Electrochem 39 2009 1633 1642 [6] C. Wen S. Guan L. Peng C. Ren X. Wang Z. Hu Characterization and degradation behavior of AZ31 alloy surface modified by bone-like hydroxyapatite for implant applications Appl Surf Sci 255 2009 6433 6438 [7] M.P. Staiger A.M. Pietak J. Huadmai G. Dias Magnesium and its alloys as orthopedic biomaterials: a review Biomaterials 27 2006 1728 1734 [8] F. Witte V. Kaese H. Haferkamp E. Switzer A. Meyer-Lindenberg C.J. Wirth In vivo corrosion of four magnesium alloys and the associated bone response Biomaterials 26 2005 3557 3563 [9] F. Witte H. Ulrich C. Palm E. Willbold Biodegradable magnesium scaffolds: part II: peri-implant bone remodeling J Biomed Mater Res Part A 81A 2007 757 765 [10] Z. Li X. Gu S. Lou Y. Zheng The development of binary Mg–Ca alloys for use as biodegradable materials within bone Biomaterials 29 2008 1329 1344 [11] F. Witte J. Fischer J. Nellesen H.A. Crostack V. Kaese A. Pisch In vitro and in vivo corrosion measurements of magnesium alloys Biomaterials 27 2006 1013 1018 [12] G. Song Control of biodegradation of biocompatable magnesium alloys Corros Sci 49 2007 1696 1701 [13] X. Gu Y. Zheng Y. Cheng S. Zhong T. Xi In vitro corrosion and biocompatibility of binary magnesium alloys Biomaterials 30 2009 484 498 [14] L. Xu F. Pan G. Yu L. Yang E. Zhang K. Yang In vitro and in vivo evaluation of the surface bioactivity of a calcium phosphate coated magnesium alloy Biomaterials 30 2009 1512 1523 [15] L. Xu E. Zhang K. Yang Phosphating treatment and corrosion properties of Mg–Mn–Zn alloy for biomedical application J Mater Sci-Mater Med 20 2009 859 867 [16] Y.W. Song D.Y. Shan E.H. Han Electrodeposition of hydroxyapatite coating on AZ91D magnesium alloy for biomaterial application Mater Lett 62 2008 3276 3279 [17] F. Witte F. Feyerabend P. Maier J. Fischer M. Stormer C. Blawert Biodegradable magnesium-hydroxyapatite metal matrix composites Biomaterials 28 2007 2163 2174 [18] F. Witte H. Ulrich M. Rudert E. Willbold Biodegradable magnesium scaffolds: part I: appropriate inflammatory response J Biomed Mater Res Part A 81A 2007 748 756 [19] S. Landgraeber M. von Knoch F. Loer A. Wegner M. Tsokos B. Hussmann Extrinsic and intrinsic pathways of apoptosis in aseptic loosening after total hip replacement Biomaterials 29 2008 3444 3450 [20] W.A. House Trace element bioavailability as exemplified by iron and zinc Field Crop Res 60 1999 115 141 [21] L. Saldana A. Mendez-Vilas L. Jiang M. Multigner J.L. Gonzalez-Carrasco M.T. Perez-Prado In vitro biocompatibility of an ultrafine grained zirconium Biomaterials 28 2007 4343 4354 [22] K. Qiu C.X. Wan C.S. Zhao X. Chen C.W. Tang Y.W. Chen Fabrication and characterization of porous calcium polyphosphate scaffolds J Mater Sci 41 2006 2429 2434 [23] L.E. Jackson B.M. Kariuki M.E. Smith J.E. Barralet A.J. Wright Synthesis and structure of a calcium polyphosphate with a unique criss-cross arrangement of helical phosphate chains Chem Mater 17 2005 4642 4646 [24] Y.M. Lee Y.J. Seol Y.T. Lim S. Kim S.B. Han I.C. Rhyu Tissue-engineered growth of bone by marrow cell transplantation using porous calcium metaphosphate matrices J Biomed Mater Res 54 2001 216 2123 [25] S.D. Waldman M.D. Grynpas R.M. Pilliar R.A. Kandel Characterization of cartilaginous tissue formed on calcium polyphosphate substrates in vitro J Biomed Mater Res 62 2002 323 3230 [26] M.D. Grynpas R.M. Pilliar R.A. Kandel R. Renlund M. Filiaggi M. Dumitriu Porous calcium polyphosphate scaffolds for bone substitute applications in vivo studies Biomaterials 23 2002 2063 2070 [27] K. Wang F. Chen C. Liu C. Rüssel The effect of polymeric chain-like structure on the degradation and cellular biocompatibility of calcium polyphosphate Mater Sci Eng C 28 2008 1572 1578 [28] W. Song M. Tian F. Chen Y. Tian C. Wan X. Yu The study on the degradation and mineralization mechanism of ion-doped calcium polyphosphate in vitro J Biomed Mater Res Part B 89B 2009 430 438 [29] R.M. Pilliar M.J. Filiaggi J.D. Wells M.D. Grynpas R.A. Kandel Porous calcium polyphosphate scaffolds for bone substitute applications – in vitro characterization Biomaterials 22 2001 963 972 [30] X.L. Zhong W.L.E. Wong M. Gupta Enhancing strength and ductility of magnesium by integrating it with aluminum nanoparticles Acta Mater 55 2007 6338 6344 [31] W.L.E. Wong M. Gupta Development of Mg/Cu nanocomposites using microwave assisted rapid sintering Compos Sci Technol 67 2007 1541 1552 [32] B.W. Chua L. Lu M.O. Lai Influence of SiC particles on mechanical properties of Mg based composite Compos Struct 47 1999 595 601 [33] M. Habibnejad-Korayem R. Mahmudi W.J. Poole Enhanced properties of Mg-based nano-composites reinforced with Al 2 O 3 nano-particles Mater Sci Eng A 519 2009 198 203 [34] C.S. Goh J. Wei L.C. Lee M. Gupta Development of novel carbon nanotube reinforced magnesium nanocomposites using the powder metallurgy technique Nanotechnology 17 2006 7 12 [35] S.F. Hassan M. Gupta Development of ductile magnesium composite materials using titanium as reinforcement J Alloys Compd 345 2002 246 251 [36] F. Witte N. Hort C. Vogt S. Cohen K.U. Kainer R. Willumeit Degradable biomaterials based on magnesium corrosion Curr Opin Solid State Mater Sci 12 2008 63 72 [37] S.F. Hassan M. Gupta Development of high performance magnesium nano-composites using nano-Al 2 O 3 as reinforcement Mater Sci Eng A 392 2005 163 168 [38] Y.L. Xi D.L. Chai W.X. Zhang J.E. Zhou Titanium alloy reinforced magnesium matrix composite with improved mechanical properties Scr Mater 54 2006 19 23 [39] S.F. Hassan M. Gupta Development of nano-Y 2 O 3 containing magnesium nanocomposites using solidification processing J Alloys Compd 429 2007 176 183 [40] S.R. Agnew O. Duygulu Plastic anisotropy and the role of non-basal slip in magnesium alloy AZ31B Int J Plast 21 2005 1161 1193 [41] N. Afrin D.L. Chen X. Cao M. Jahazi Microstructure and tensile properties of friction stir welded AZ31B magnesium alloy Mater Sci Eng A 472 2008 179 186 [42] S. Zhang X. Zhang C. Zhao J. Li Y. Song C. Xie Research on an Mg–Zn alloy as a degradable biomaterial Acta Biomater 6 2010 626 640 [43] E. Zhang D. Yin L. Xu L. Yang K. Yang Microstructure, mechanical and corrosion properties and biocompatibility of Mg–Zn–Mn alloys for biomedical application Mater Sci Eng C 29 2009 987 993 [44] E. Zhang L. Yang J. Xu H. Chen Microstructure, mechanical properties and bio-corrosion properties of Mg–Si(–Ca, Zn) alloy for biomedical application Acta Biomater 6 2010 1756 1762 [45] S. Tiwari R. Balasubramaniam M. Gupta Corrosion behavior of SiC reinforced magnesium composites Corros Sci 49 2007 711 725 [46] A. Bakkar V. Neubert Corrosion behaviour of carbon fibres/magnesium metal matrix composite and electrochemical response of its constituents Electrochim Acta 54 2009 1597 1606
What problem does this paper attempt to address?
-
Corrosion Behavior and Biological Properties of ZK60/HA Composites Prepared by Laser Powder Bed Fusion
Cijun Shuai,Cheng Chen,Zhenyu Zhao,Youwen Yang
DOI: https://doi.org/10.3390/mi15091156
IF: 3.4
2024-09-16
Micromachines
Abstract:Magnesium alloy ZK60 shows great promise as a medical metal material, but its corrosion resistance in the body is inadequate. Hydroxyapatite (HA), the primary inorganic component of human and animal bones, can form chemical bonds with body tissues at the interface, promoting the deposition of phosphorus products and creating a dense calcium and phosphorus layer. To enhance the properties of ZK60, HA was added to create HA/ZK60 composite materials. These composites, fabricated using the advanced technique of LPBF, demonstrated superior corrosion resistance and enhanced bone inductive capabilities compared to pristine ZK60. Notably, the incorporation of 3 wt% led to a significant reduction in bulk porosity, achieving a value of 0.8%. The Ecorr value increased from −1.38 V to −1.32 V, while the minimum Icorr value recorded at 33.9 μA·cm−2. Nano-HA achieved the lowest volumetric porosity and optimal corrosion resistance. Additionally, these composites significantly promoted osteogenic differentiation in bone marrow stromal cells (BMSCs), as evidenced by increased alkaline phosphatase (ALP) activity and robust calcium nodule formation, highlighting their excellent biocompatibility and osteo-inductive potential. However, when increasing the HA content to 6 wt%, the bulk porosity rose significantly to 3.3%. The Ecorr value was −1.3 V, with the Icorr value being approximately 50 μA·cm−2. This increase in porosity and weaker interfacial bonding, ultimately accelerated electrochemical corrosion. Therefore, a carefully balanced amount of HA significantly enhances the performance of the ZK60 magnesium alloy, while excessive amounts can be detrimental.
chemistry, analytical,nanoscience & nanotechnology,instruments & instrumentation,physics, applied
-
In Vitro Degradation Performance and Biological Response of a Mg–Zn–Zr Alloy
X. N. Gu,N. Li,Y. F. Zheng,Liquan Ruan
DOI: https://doi.org/10.1016/j.mseb.2011.05.032
2011-01-01
Abstract:The feasibility of a Mg-Zn-Zr alloy for biomedical applications was studied through microstructure characterization, corrosion tests in different biological media, and cell proliferation, differentiation and adhesion tests. Corrosion tests showed that the ZK60 alloy in the as-extruded state with finer grain sizes exhibited slower corrosion rates than the same alloy in the as-cast state. The tests in different biological fluids showed that the corrosion rates of the as-cast and as-extruded ZK60 alloy in DMEM + FBS were the highest, while those in Hank's solution were the lowest. The corrosion rate of the as-extruded ZK60 alloy was similar to the corrosion rates of other commercial magnesium alloys, namely the die-cast AZ910, die-cast AM50, extruded AZ31 and extruded WE43 alloys. The results obtained from the indirect cytotoxicity evaluation showed that the 100% concentrated cast and extruded ZK60 alloy extracts resulted in significantly reduced cell numbers and total protein amounts, as compared to the negative control. The cell number and total protein amount increased with the gradual dilution of the extracts, but the protein normalized ALP activity showed an opposite trend. For the direct assay, L-929 and MG63 cells exhibited good adhesion with spread pseudopod on the surface of extruded ZK60 alloy samples after 24 h culture. In short, the as-extruded ZK60 alloy could be a good candidate material for biodegradable implants. (C) 2011 Elsevier B.V. All rights reserved.
-
Corrosion-wear behavior of a biocompatible magnesium matrix composite in simulated body fluid
Jinlong Su,Jie Teng,Zili Xu,Yuan Li
DOI: https://doi.org/10.1007/s40544-020-0361-8
IF: 4.924
2020-07-15
Friction
Abstract:Abstract Magnesium matrix composites are a new generation of biocompatible implant materials, but they will inevitably undergo simultaneous wear and corrosion in the human body. In this study, hydroxyapatite (Ca 10 (PO 4 ) 6 (OH) 2 , HA) is used in a magnesium matrix composite to study its effects on the corrosion–wear behavior. Two samples (a magnesium alloy composed of Mg, Zn, and Zr (ZK60) alloy and ZK60/10HA composite) were fabricated using the powder metallurgy (PM) process. Their corrosion–wear behavior was investigated using the sliding wear test in a simulated body fluid (SBF). At all the sliding velocities tested, the corrosion-wear resistance of ZK60/10HA was superior to ZK60. At a sliding velocity of 942.5 mm/min, ZK60/10HA demonstrated a 42% improvement in corrosion–wear resistance compared to ZK60. For ZK60, the main wear mechanism under dry conditions was abrasion, while the wear mechanisms in the SBF were abrasion and corrosion. For ZK60/10HA, the wear mechanisms under dry conditions were abrasion and delamination, while in SBF they were mainly abrasion and corrosion, accompanied by slight delamination. The results indicated that HA particles can be used as an effective corrosion–wear inhibitor in biocompatible magnesium matrix composites.
engineering, mechanical
-
Ceramic coating on Mg alloy for enhanced degradation resistance as implant material
Saifullah Mahmud,Mostafizur Rahman,Hazera Khatun,Osman Ali,Ramjan Ali,Mosiur Rahaman,Sadia Islam,Yusuf Ali,Md Mostafizur Rahman,Md. Osman Ali,Md. Ramjan Ali
DOI: https://doi.org/10.1016/j.surfcoat.2024.130544
IF: 4.865
2024-02-21
Surface and Coatings Technology
Abstract:Magnesium (Mg) alloys display very appealing characteristics, including biocompatibility, bioactivity, biodegradability, lightweightness, and a similar density to cortical bone tissue, but they have some constraints, such as inappropriate corrosion and degradation resistance, which lead to failing early mechanical strength. Therefore, calcium phosphate (CaP)-based ceramic coating like hydroxyapatite (HA) coating is fabricated on the anodization-induced surfaces of pure Mg and ZK41 Mg alloy specimens to overcome those constraints in medical applications. In mechanical integrity like microhardness, adhesion strength tests demonstrated that HA coated ZK41 and Mg specimens significantly increased Vickers' hardness number (about 2 times) compared to unmodified substrates and had greater adhesion strength in comparison with the anodization-induced layer, respectively. In the in vitro immersion test, the HA-coated samples showed plate-like and needle-like crystal formations. This provided more surface area, which improved the corrosion and degradation resistance characteristics. As a consequence, the least amount of weight loss has occurred. Additionally, the anodized (AN) Mg, HA coated Mg, untreated ZK41, and anodized ZK41 samples all have higher corrosion rates than the HA coated ZK41 (0.018 mm/year). Cell viability of HA coated Mg and its alloy ZK41 was comparatively high, which ensures biocompatibility as an implant material. Therefore, HA coatings for Mg and ZK41 alloys for clinical applications could be more promising. In this study, ZK41 Mg alloy has been used as an inventive substrate for HA coating in place of the prior Mg alloys, with the intention of addressing the earlier drawbacks.
physics, applied,materials science, coatings & films
-
A Study on the Structure and Biomedical Application Characteristics of Phosphate Coatings on ZKX500 Magnesium Alloys
Ying-Ting Huang,Wen-Yu Wu,Fei-Yi Hung,Fa-Chuan Kuan,Kai-Lan Hsu,Wei-Ren Su,Chen-Wei Yen
DOI: https://doi.org/10.3390/bioengineering9100542
2022-10-11
Abstract:Magnesium-matrix implants can be detected by X-ray, making post-operative monitoring easier. Since the density and mechanical properties of Mg alloys are similar to those of human bones, the stress-shielding effect can be avoided, accelerating the recovery and regeneration of bone tissues. Additionally, Mg biodegradability shields patients from the infection risk and medical financial burden of needing another surgery. However, the major challenge for magnesium-matrix implants is the rapid degradation rate, which necessitates surface treatment. In this study, the ZKX500 Mg alloy was used, and a non-toxic and eco-friendly anodic oxidation method was adopted to improve corrosion resistance. The results indicate that the anodic coating mainly consisted of magnesium phosphate. After anodic oxidation, the specimen surface developed a coating and an ion-exchanged layer that could slow down the degradation and help maintain the mechanical properties. The results of the tensile and impact tests reveal that after being immersed in SBF for 28 days, the anodic oxidation-treated specimens maintained good strength, ductility, and toughness. Anodic coating provides an excellent surface for cell attachment and growth. In the animal experiment, the anodic oxidation-treated magnesium bone screw used had no adverse effect and could support the injured part for at least 3 months.
-
The combined effect of zinc and calcium on the biodegradation of ultrahigh-purity magnesium implants
Begüm Okutan,Uwe Y Schwarze,Leopold Berger,Diana C Martinez,Valentin Herber,Omer Suljevic,Tomasz Plocinski,Wojciech Swieszkowski,Susana G Santos,Rainer Schindl,Jörg F Löffler,Annelie M Weinberg,Nicole G Sommer
DOI: https://doi.org/10.1016/j.bioadv.2023.213287
Abstract:Magnesium (Mg)-based implants are promising candidates for orthopedic interventions, because of their biocompatibility, good mechanical features, and ability to degrade completely in the body, eliminating the need for an additional removal surgery. In the present study, we synthesized and investigated two Mg-based materials, ultrahigh-purity ZX00 (Mg-Zn-Ca; <0.5 wt% Zn and <0.5 wt% Ca, in wt%; Fe-content <1 ppm) and ultrahigh-purity Mg (XHP-Mg, >99.999 wt% Mg; Fe-content <1 ppm), in vitro and in vivo in juvenile healthy rats to clarify the effect of the alloying elements Zn and Ca on mechanical properties, microstructure, cytocompatibility and degradation rate. Potential differences in bone formation and bone in-growth were also assessed and compared with state-of-the-art non-degradable titanium (Ti)-implanted, sham-operated, and control (non-intervention) groups, using micro-computed tomography, histology and scanning electron microscopy. At 6 and 24 weeks after implantation, serum alkaline phosphatase (ALP), calcium (Ca), and Mg level were measured and bone marrow stromal cells (BMSCs) were isolated for real-time PCR analysis. Results show that ZX00 implants have smaller grain size and superior mechanical properties than XHP-Mg, and that both reveal good biocompatibility in cytocompatibilty tests. ZX00 homogenously degraded with an increased gas accumulation 12 and 24 weeks after implantation, whereas XHP-Mg exhibited higher gas accumulation already at 2 weeks. Serum ALP, Ca, and Mg levels were comparable among all groups and both Mg-based implants led to similar relative expression levels of Alp, Runx2, and Bmp-2 genes at weeks 6 and 24. Histologically, Mg-based implants are superior for new bone tissue formation and bone in-growth compared to Ti implants. Furthermore, by tracking the sequence of multicolor fluorochrome labels, we observed higher mineral apposition rate at week 2 in both Mg-based implants compared to the control groups. Our findings suggest that (i) ZX00 and XHP-Mg support bone formation and remodeling, (ii) both Mg-based implants are superior to Ti implants in terms of new bone tissue formation and osseointegration, and (iii) ZX00 is more favorable due to its lower degradation rate and moderate gas accumulation.
-
Optimization of the in Vitro Biodegradability, Cytocompatibility, and Wear Resistance of the AZ31B Alloy by Micro-Arc Oxidation Coatings Doped with Zinc Phosphate
Chao Yang,Suihan Cui,Ricky K. Y. Fu,Liyuan Sheng,Min Wen,Daokui Xu,Ying Zhao,Yufeng Zheng,Paul K. Chu,Zhongzhen Wu
DOI: https://doi.org/10.1016/j.jmst.2023.09.019
2024-01-01
Abstract:As implanted bone fixation materials, magnesium (Mg) alloys have significant advantages because the density and elastic modulus are closest to those of the human bone and they can bio-degrade in the physiological environment. However, Mg alloys degrade too rapidly and uncontrollably thus hampering clinical adoption. In this study, a highly corrosion-resistant zinc-phosphate-doped micro-arc oxidation (MAO) coating is prepared on the AZ31B alloy, and the degradation process is assessed in vitro. With increasing zinc phosphate concentrations, both the corrosion potentials and charge transfer resistance of the AZ31B alloy coated with MAO coatings increase gradually, while the corrosion current densities di-minish gradually. Immersion tests in the simulated body fluid (SBF) reveal that the increased zinc phos-phate concentration in MAO coating decreases the degradation rate, consequently reducing the release rates of Mg2+ and OH - in the physiological micro-environment, which obtains the lowest weight loss of only 5.22% after immersion for 56 days. Effective regulation of degradation provides a weak alkaline environment that is suitable for long-term cell growth and subsequent promotion of bone proliferation, differentiation, mineralization, and cytocompatibility. In addition, the zinc-phosphate-doped MAO coat-ings show an improved wear resistance as manifested by a wear rate of only 3.81 x 10 -5 mm3 N -1 m -1 . The results reveal a suitable strategy to improve the properties of biodegradable Mg alloys to balance tissue healing with mechanical degradation.(c) 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
-
Characterization and Degradation Study of Calcium Phosphate Coating on Magnesium Alloy Bone Implant in Vitro
J. X. Yang,F. Z. Cui,Q. S. Yin,Y. Zhang,T. Zhang,X. M. Wang
DOI: https://doi.org/10.1109/tps.2009.2016664
IF: 1.368
2009-01-01
IEEE Transactions on Plasma Science
Abstract:Magnesium alloys have similar mechanical properties with natural bone, and they degrade within a certain time span. Therefore, magnesium alloys are suitable to be made as bone screws or plates. However, high susceptibility to corrosion has limited their applications in the orthopedic field. They would possess great medical functions if the degradation rates of magnesium alloys could be reduced. This paper describes approaches to form calcium phosphate coating on magnesium alloy (AZ31) to control the degradation rate. Samples of AZ31 were placed in the supersaturated calcification solution prepared with Ca(NO3)(2), NaH2PO4, and NaHCO3, and then, the calcium phosphate coating was formed. The composition, phase structure, and morphology of the coatings were investigated. The degradation behaviors of the naked and coated magnesium (Mg) alloys were studied in simulated body fluid. The results of this paper have shown that the coatings significantly decrease the degradation rate of the original Mg alloy, indicating that the Mg alloy with calcium phosphate coating is a promising degradable bone material.
-
In vitro degradation and biocompatibility of WE43, ZK60, and AZ91 biodegradable magnesium alloys
C. L. Liu,Jiang Jiang,Mei Wang,Yueji Wang,Paul Chu,Weijiu Huang
DOI: https://doi.org/10.4028/www.scientific.net/AMR.287-290.2008
2011-01-01
Abstract:Successful application of magnesium alloys as degradable load-bearing implants is determined by their biological performance especially degradation and corrosion behavior in the human body. Three magnesium alloys, namely WE43, ZK60, and AZ91 are investigated in this work. The in vitro degradation behavior, cytotoxicity, and genotoxicity are evaluated by corrosion tests, 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay, and micronuclei tests, respectively. Immersion tests indicate that the ZK60 alloy has the best corrosion resistance and lowest corrosion rate in flank's solution, followed by AZ91 alloy and WE43 alloy in that order. The MTT results obtained from the three magnesium alloys after 7 days of immersion indicate good cellular viability. However, excessively high aluminum and magnesium concentrations have a negative influence on the genetic stability.
-
In Vitro Biodegradation and Mechanical Properties of Mg-Zn Alloy and Mg-Zn-Hydroxyapatite Composite Produced by Mechanical Alloying for Potential Application in Bone Repair
Emee Marina Salleh,Hussain Zuhailawati,Siti Noor Fazliah Mohd Noor,Norinsan Kamil Othman
DOI: https://doi.org/10.1007/s11661-018-4873-z
2018-08-30
Metallurgical and Materials Transactions A
Abstract:A biodegradable Mg-6.5 wt pct Zn (Mg-Zn) alloy and Mg-6.5 wt pct Zn reinforced with 10 wt pct hydroxyapatite (HA) composite were prepared by mechanical milling. In vitro biodegradation activity as a function of immersion time was performed in Hank’s balanced salt solution (HBSS). The dissolution of Mg ions (Mg2+) decreased from 75.74 µg/ml of pure Mg to 59.24 µg/ml and 46.88 µg/ml corresponding to the Mg-Zn alloy and Mg-Zn/HA composite, respectively. This finding indicates the progressive effect of HA followed by the Zn addition in decelerating the degradation rate of Mg. More positive corrosion potential of Mg-6.5 wt pct Zn alloy (− 1.5015 V) and Mg-Zn/10 wt pct HA composite (− 1.4647 V) than that of pure Mg (− 1.6972 V) suggested that the Mg-Zn/10 wt pct HA composite exhibited the highest corrosion resistance in the bioenvironment. The compressive strength values after 7 days of immersion in HBSS of the Mg-Zn alloy and Mg-Zn/HA composite are 230.64 and 278.46 MPa, respectively, and these are considerably higher compared to the compressive strength of the cortical bone (100 to 230 MPa).
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
In Vitro Degradation and In Vivo Biocompatibility of Strontium-Doped Magnesium Phosphate-Reinforced Magnesium Composites
Sourav Dutta,Rabiul Khan,N Surya Prakash,Sanjay Gupta,Debaki Ghosh,Samit K Nandi,Mangal Roy
DOI: https://doi.org/10.1021/acsbiomaterials.2c00142
2022-10-10
Abstract:Magnesium is projected for use as a degradable orthopedic biomaterial. However, its fast degradation in physiological media is considered as a significant challenge for its successful clinical applications. Bioactive reinforcements containing Mg-based composites constitute one of the promising approaches for developing degradable metallic implants because of their adjustable mechanical behaviors, corrosion resistance, and biological response. Strontium is a trace element known for its role in enhancing osteoblast activity. In this study, bioactive SrO-doped magnesium phosphate (MgP)-reinforced Mg composites containing 1, 3, and 5 wt % MgP were developed through the casting route. The influence of the SrO-doped MgP reinforcement on degradation behaviors of the composites along with its cell-material interactions and in vivo biocompatibility was investigated. The wt % and distribution of MgP particles significantly improved the mechanical properties of the composite. HBSS immersion study indicated the least corrosion rate (0.56 ± 0.038 mmpy) for the Mg-3MgP composite. The higher corrosion resistance of Mg-3MgP leads to a controlled release of Sr-containing bioactive reinforcement, which eventually enhanced the cytotoxicity as measured using MG-63 cell-material interactions. The in vivo biocompatibility of the composite was evaluated using the rabbit femur defect model. Micro-computed tomography (μ-CT) and histological analysis supported the fact that Mg-3MgP maintained its structural integrity and enhanced osteogenesis (50.36 ± 2.03%) after 2 months of implantation. The results indicated that the Mg-MgP composite could be used as a degradable internal fracture fixation device material.
-
Corrosion Activity of Ultrafine-Grained Pure Magnesium and ZK60 Magnesium Alloy in Phosphate Buffered Saline Solution
Stella Diederichs,Dayan Nugmanov,Yulia Ivanisenko,Eberhard Kerscher
DOI: https://doi.org/10.3390/ma17112726
IF: 3.4
2024-06-05
Materials
Abstract:The magnesium alloy ZK60 is a promising candidate as a material for biodegradable implants. One of the most important factors for biodegradable implants is the modification of their corrosion behavior to match the requirements for the healing bone or tissue. The corrosion behavior can be influenced by different factors, among them the grain size, which can be changed by severe plastic deformation processes such as High Pressure Torsion Extrusion (HPTE). This study focuses on the corrosion behavior of samples of pure magnesium and ZK60 before and after HPTE, and the influence of the microstructure on the corrosion activity. The samples are subjected to immersion tests in phosphate buffered saline solution (PBS). The corrosion activity is defined by the emerging hydrogen volume from the corrosion process which is collected and by subsequently observing the resulting sample surfaces. The findings of this study suggest that pure magnesium shows lower corrosion activities than ZK60 and that HPTE processing leads to higher corrosion activities in PBS.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
-
Biodegradation ZK50 magnesium alloy compression screws: Mechanical properties, biodegradable characteristics and implant test
Yen-Ting Chen,Fei-Yi Hung,Yen-Ling Lin,Chia-Yen Lin
DOI: https://doi.org/10.1016/j.jos.2020.01.018
Abstract:Background: Magnesium alloy implants have lower stress load and can be absorbed gradually, but their degradation rates are too fast generally. A magnesium alloy contained 5% Zn and 0.5% Zr (ZK50) which have lower degradation rate are designed to be applied to cannulated bone screw. Methods: An oxidation heat treatment of 380 °C for 2 h proceeds to modify the ZK50 Mg alloy (ZK50-H). The microstructure observation, degradation tests and Biocompatibility analysis are proceeded between ZK50 and ZK50-H. Finally, a mini-pig implantation test is proceeded to provide a reference of implant application for future pre-clinical evaluation. Results: The heat treatment can improve the mechanical properties. A passive ceramic layer formed after simulated body fluid (SBF) solution immersion can restrict the degradation effectively. The cytotoxicity test shows the initial biosafety of ZK50 Mg alloy. A mini-pig implantation test of bone screw has proceeded to confirm the advanced biocompatibility. The ZK50-H screws can maintain enough support at least 8 weeks which the fracture of bone can get curing. The excellent osteoinduction of ZK50-H has a positive effect to growth of new bones and help the mini-pig regain heal faster in 12 weeks. Conclusion: This study shows ZK50-H Mg alloy screw is a feasible degradation implant and can be carried out the next-step clinical experiments.
-
Mechanical properties, corrosion behavior, and cytotoxicity of biodegradable Zn/Mg multilayered composites prepared by accumulative roll bonding process
Quanxiang Sun,Dechuang Zhang,Xian Tong,Jianguo Lin,Yuncang Li,Cuie Wen
DOI: https://doi.org/10.1016/j.actbio.2023.11.025
2024-01-01
Abstract:Zinc (Zn), magnesium (Mg), and their respective alloys have attracted great attention as biodegradable bone-implant materials due to their excellent biocompatibility and biodegradability. However, the poor mechanical strength of Zn alloys and the rapid degradation rate of Mg alloys limit their clinical application. The manufacture of Zn and Mg bimetals may be a promising way to improve their mechanical and degradation properties. Here we report on Zn/Mg multilayered composites prepared via an accumulative roll bonding (ARB) process. With an increase in the number of ARB cycles, the thicknesses of the Zn layer and the Mg layer were reduced, while a large number of heterogeneous interfaces were introduced into the Zn/Mg multilayered composites. The composite samples after 14 ARB cycles showed the highest yield strength of 411±3 MPa and highest ultimate tensile strength of 501±3 MPa among all the ARB processed samples, significantly higher than those of the Zn/Zn and Mg/Mg multilayered samples. The Zn and Mg layers remained continuous in the Zn/Mg composite samples after annealing at 150 °C for 10 min, resulting in a decrease in yield strength from 411±3 MPa to 349±3 MPa but an increase in elongation from 8±1% to 28±1%. The degradation rate of the Zn/Mg multilayered composite samples in Hanks' solution was ranged from 127±18 µm/y to 6±1 µm/y. The Zn/Mg multilayered composites showed over 100% cell viability with their 25% and 12.5% extracts in relation to MG-63 cells after culturing for 3 d, indicating excellent cytocompatibility. STATEMENT OF SIGNIFICANCE: This work reports a biodegradable Zn/Mg multilayered composite prepared by accumulative roll bonding (ARB) process. The yield and ultimate tensile strength of the Zn/Mg multilayered composites were improved due to grain refinement and the introduction of a large number of heterogeneous interfaces. The composite samples after 14 ARB cycles showed the highest yield strength of 411±3 MPa and highest ultimate tensile strength of 501±3 MPa among all the ARB processed samples. The degradation rate of the Zn/Mg multilayered composite meets the required degradation rate for biodegradable bone-implant materials. The results demonstrated that it is a very promising approach to improve the strength and biocompatibility of biodegradable Zn-based alloys.
-
Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials
Guangxin Shen,Shaoyuan Lyu,Qianqian Yu,Xuewei Wang,Minfang Chen
DOI: https://doi.org/10.1016/j.jallcom.2024.177174
IF: 6.2
2024-10-31
Journal of Alloys and Compounds
Abstract:The effect of nano-CaO content on the microstructure, mechanical properties, and in vitro degradation performance of extruded Mg-1Zn alloys was investigated to enhance the strength and corrosion resistance of biodegradable materials for medical implants. The results showed that the addition of CaO nanoparticles effectively refined the size of dynamic recrystallization grains in the extruded composites. During the extrusion process, Ca 2 Mg 6 Zn 3 and Mg 2 Ca phases precipitated in the Mg-1Zn-0.5CaO and Mg-1Zn-1CaO composites, respectively. As the CaO content increased, the basal texture strength was elevated from 3.97 for the Mg-1Zn alloy to 12.05 for the Mg-1Zn-1CaO composite. Benefiting from the combined mechanisms of grain refinement, dislocation strengthening, and precipitation strengthening, the yield strength of the materials was fortified with an increase in CaO content. During the short immersion time, the matrix of the extruded Mg-1Zn-0.5CaO composite was preferentially corroded, resulting in the formation of a dense corrosion product layer that impeded the transport of ions in the electrolyte solution, thereby exhibiting the lowest annual corrosion rate. With an increase in the immersion time, galvanic corrosion destroyed the protective film, leading to a slightly higher corrosion rate in the extruded Mg-1Zn-0.5CaO composite compared to the Mg-1Zn alloy. The substantial nano-Mg 2 Ca phase particles were preferentially degraded, causing severe pitting corrosion in the extruded Mg-1Zn-1CaO composite, which exhibited the highest degradation rate. The extruded Mg-1Zn-0.5CaO composite exhibited superior overall properties; its yield strength, elongation, and annual corrosion rate after immersion (21 d) were 334.9 MPa, 8.9 %, and 1.06 mm/y, respectively.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Degradation Behavior of Medical MgZZC-1 in Various Simulated Body Fluids
Jie Pan,Jinling Zhang,Yelei Li,Fanxi Yang,Yanchong Yu,Shebin Wang
DOI: https://doi.org/10.1021/acs.langmuir.4c01715
IF: 3.9
2024-07-16
Langmuir
Abstract:Magnesium-based biodegradable metal bone implants exhibit superior mechanical properties compared to biodegradable polymers for orthopedic and cardiovascular stents. In this study, MgZZC-x (x = 1, 1.2) alloys were screened by in vitro biocompatibility tests in three simulated body fluids under nontoxic conditions. The MgZZC-1 alloys with better biocompatibility were selected to predict the days required for complete degradation. The evolution of degradation products was analyzed, and the mechanism of formation of the product film was inferred. A degradation kinetic model was established to investigate the effect of MEM components on the degradation of the alloys. The results demonstrate that the proteins in MEM can greatly retard the degradation progress by attaching to the surface of MgZZC-1 alloys, which are predicted to degrade completely within 341 days. The carbonate and phosphate buffers were adjusted to pH in MEM solution, delaying the degradation of magnesium alloys. This process in MEM more accurately reflects the actual degradation in the body and is superior to that in Hanks and SBF solutions. This study will promote the application of biodegradable materials in clinical medicine.
-
Additive manufacturing of ZK60 magnesium alloy by selective laser melting: Parameter optimization, microstructure and biodegradability
C.L. Wu,Wei Zai,H.C. Man
DOI: https://doi.org/10.1016/j.mtcomm.2020.101922
IF: 3.8
2021-03-01
Materials Today Communications
Abstract:<p>Mg-Zn-Zr (ZK60) magnesium alloy samples were prepared by selective laser melting (SLM). The processability of ZK60 prepared by SLM was thoroughly investigated via varying the laser processing parameters. Experimental results show that laser power and scan velocity played an important role in determining the quality of SLM ZK60. SLM ZK60 with minimal defects and high dimensional accuracy could be obtained at a laser power of 50 W and scanning velocity of 500–800 mm/s. The formation mechanisms of pores were also identified and illustrated thoroughly in size and shape in the transition regimes. Significantly refined grains were observed in SLM ZK60, with an average grain size (<em>G</em><sub>a</sub>) of 7.3 μm for SLM ZK60 versus 56.4 μm for cast ZK60. Besides the α-Mg phase, the Mg<sub>7</sub>Zn<sub>3</sub> eutectic phase was precipitated in the α-Mg matrix in SLM ZK60, and the MgZn phase in cast ZK60. The hardness of cast ZK60 and SLM ZK60 was 0.55 and 0.78 GPa, respectively, with similar elastic modulus. SLM ZK60 exhibited a higher corrosion resistance in Hanks' solution compared with cast ZK60 as indicated by a decrease of about 30 % in hydrogen evolution rate and of about 50 % in the corrosion current density. The SLM ZK60 fabricated in the present study exhibits a great potential for biomedical applications due to desirable mechanical properties and a reasonably low degradable rate.</p>
materials science, multidisciplinary
-
Biopolymer-coated magnesium-alloy-based multi-functional bio-nanocomposite scaffolds
Adithya Garimella,Darshan Rathi,Rajesh Jangid,Deepak Khare,Ashutosh Kumar Dubey,Subrata Bandhu Ghosh,Sanchita Bandyopadhyay-Ghosh
DOI: https://doi.org/10.1080/10667857.2024.2390291
2024-08-19
Materials Technology
Abstract:PM-technique produced magnesium-alloy bio-nanocomposite porous scaffolds with carbamide as porogen. Mg samples were alloyed with Ca, Zn, and Sr for enhanced mechanical performance and deterioration resistance. Nano-fluorcanasite, a bioactive-chain-silicate glass-ceramic reinforcement, was added to the magnesium-metal-matrix to induce new bone cell growth. Dip-coating was used to coat bare magnesium samples with PCL. FE-SEM-EDS findings showed gradient-porosity and coating thickness of 70–90 μm. After 28-days of immersion, C-S1 and C-S2 had compressive and residual-compressive strengths 10% to 15% higher than C-S0. As Ca, Zn, and Sr hydroxyapatites formed, C-S1 and C-S2 degradation reduced with immersion time. Biodegradation matches immersion liquid pH, hydrogen gas evolution, and cytocompatibility. As porosity increased from 50% to 60%, scaffold compressive strength and modulus decreased but remained in line with that of a human cancellous bone. PCL-coated customized nanocomposite magnesium alloy-based biomaterials may be promising biodegradable bone tissue repair implant materials with configurable mechanical and degradable attributes.
materials science, multidisciplinary
-
Biodegradable WE43 Mg alloy/hydroxyapatite interpenetrating phase composites with reduced hydrogen evolution
Lenka Drotárová,Karel Slámečka,Tomáš Balint,Michaela Remešová,Radovan Hudák,Jozef Živčák,Marek Schnitzer,Ladislav Čelko,Edgar B. Montufar
DOI: https://doi.org/10.1016/j.bioactmat.2024.08.048
IF: 18.9
2024-09-13
Bioactive Materials
Abstract:Highlights • High porosity (75 %) WE43 Mg alloy scaffolds were infiltrated with alpha tricalcium phosphate. • Hydrothermal treatments produced Mg/hydroxyapatite composites at low temperature. • Composites showed much higher compressive strength and corrosion resistance than scaffolds. • Composites demonstrated high damage tolerance due to stress transfer and delocalization of strain. • Hydrothermal treatment improved the degradation resistance of the Mg alloy trough passivation. Biodegradable magnesium implants offer a solution for bone repair without the need for implant removal. However, concerns persist regarding peri-implant gas accumulation, which has limited their widespread clinical acceptance. Consequently, there is a need to minimise the mass of magnesium to reduce the total volume of gas generated around the implants. Incorporating porosity is a direct approach to reducing the mass of the implants, but it also decreases the strength and degradation resistance. This study demonstrates that the infiltration of a calcium phosphate cement into an additively manufactured WE43 Mg alloy scaffold with 75 % porosity, followed by hydrothermal treatment, yields biodegradable magnesium/hydroxyapatite interpenetrating phase composites that generate an order of magnitude less hydrogen gas during degradation than WE43 scaffolds. The enhanced degradation resistance results from magnesium passivation, allowing osteoblast proliferation in indirect contact with composites. Additionally, the composites exhibit a compressive strength 1.8 times greater than that of the scaffolds, falling within the upper range of the compressive strength of cancellous bone. These results emphasise the potential of the new biodegradable interpenetrating phase composites for the fabrication of temporary osteosynthesis devices. Optimizing cement hardening and magnesium passivation during hydrothermal processing is crucial for achieving both high compressive strength and low degradation rate. Graphical abstract Download: Download high-res image (451KB) Download: Download full-size image
engineering, biomedical,materials science, biomaterials
-
Preparation of medical Mg–Zn alloys and the effect of different zinc contents on the alloy
Yunpeng Hu,Xuan Guo,Yang Qiao,Xiangyu Wang,Qichao Lin
DOI: https://doi.org/10.1007/s10856-021-06637-0
2022-01-01
Abstract:Abstract In recent years, along with the development and application of magnesium alloys, magnesium alloys have been widely used in automotive, aerospace, medicine, sports, and other fields. In the field of medical materials, magnesium not only has the advantage of light weight, high strength, and a density similar to that of human bone, but also has good biocompatibility and promotes the growth of human bone. However, the mechanical properties and corrosion resistance of magnesium alloys need to be further improved to meet the requirements for human biodegradable implants. In this study, three alloys (mass fractions: Mg–10Zn, Mg–20Zn, and Mg–30Zn (wt.%)) were prepared using powder metallurgy by homogeneously mixing powders of the above materials in a certain amount with magnesium as the substrate through the addition of zinc elements, which also have good biocompatibility. The effect of zinc on the microstructure, mechanical properties, wear performance, and corrosion resistance of magnesium–zinc alloys was studied when the zinc content was different. The results show that compared with the traditional magnesium alloy using powder metallurgy, prepared magnesium alloy has good resistance to compression and bending, its maximum compressive stress can reach up to 318.96 MPa, the maximum bending strength reached 189.41 MPa, and can meet the mechanical properties of the alloy as a human bone-plate requirements. On the polarization curve, the maximum positive shift of corrosion potential of the specimens was 73 mv and the maximum decrease of corrosion-current density was 53.2%. From the comparison of the above properties, it was concluded that the three prepared alloys of which Mg–20% Zn had the best overall performance. Its maximum compressive stress, maximum bending strength, and corrosion-current density reached 318.96 MPa, 189.41 MPa and 2.08 × 10 −5 A·cm −2 respectively, which are more suitable for use as human implant bone splints in human-body fluid environment.