Abstract:Aqueous polyurethane (PU) prepolymers were synthesized by emulsion polymerization in situ, with toluene diisocyanate (TD1-80), polyether binary alcohol (N210), dimethylol propionic acid (DMPA), hydroxyl ethyl methacrylate (HEMA), adipic dihydrazide (ADH) and diacetone acrylamide (DAAM) as the materials. Three kinds of aqueous polyurethane-acrylate (PUA) hybrid emulsions marked as PUA-1 (free cross-linking), PUA-2 (synthesized cross-linking) and PUA-3 (cross-linking at ambient temperature) were synthesized after the free radical polymerization by adding initiator, which were then used to prepare three kinds of varnishes. The effects of the dosages of DMPA, HEMA, ADH and DAAM on the properties of emulsions and films were finally investigated. It is found that, when the mass fraction of -COOH in DMPA and the mass fractions of HEMA, ADH and DAAM in PU are respectively 2.5%, 1.44%, 3.5% and 2.0%-3.0%, the emulsions and films are all of good properties. Moreover, the results obtained by particle size analyzer and TEM show that (1) the average particle sizes of PUA-1, PUA-2 and PUA-3 are respectively 40-50 nm, 90-100 nm and 30-40 nm; (2) PUA-1 particles are regular sphericities in shape, while PUA-2 particles are irregular sphericities with interpenetrating polymer network between the core and the shell; (3) as compared with PUA-1, PUA-2 is of larger particle size and wider particle size distribution; (4) PUA-3 is of very irregular particle shape, uniform particle size distribution and disorganized interpenetrating network between the shell and the core. Furthermore, in the three kinds of vanishes, the one prepared from PUA-3 is of the best water resistance, dry-heat resistance and stain resistance but is of the longest drying time for the film.

Adhesion Behaviors and Affecting Factors of Polymer Latexes

The Coating Properties of Waterborne UV-Curable Polyurethane Acrylate and Influencing Factors

Preparation and Characterization of a Self -Matting Coating Based on Waterborne Polyurethane-Polyacrylate Hybrid Dispersions

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Factors affecting performance of polyurethane-acrylate hybrid emulsion

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane‐acrylate composite

Influence of the Composition of Macromolecular Diols on the Rheology and Water Absorption of Polyurethane Acrylate Emulsions

Preparation, properties and application of waterborne hydroxyl-functional polyurethane/acrylic emulsions in two-component coatings

Preparation, Thermal Property and Morphology Analysis of Waterborne Polyurethane-Acrylate

Effect of Water Content on the Aggregation and Adhesion Properties of Waterborne Polyurethane

Synthesis and Adhesion Property of Waterborne Polyurethanes with Different Ionic Group Contents

Synthesis and Characterization of High Performance Water Borne Polyurethane Emulsion

Synthesis And Adhesion Properties Of Waterborne Polyurethane Dispersions With Long-Branched Aliphatic Chains

Study on Synthesis and Performance of Environmentally-friendly Waterborne Polyurethane Adhesive

Study on the Mechanical and Adhesive Properties of Waterborne Polyurethane with Multiple Modifications

Synthesis of Waterborne Polyurethane-acrylate Adhesive for Laminated Film

Study on influence factors of waterborne polyurethane (WPU) adhesives performanceⅡ—Effect of structure factors

Preparation and Properties of High Solid Content and Low Viscosity Waterborne Polyurethane—Acrylate Emulsion with a Reactive Emulsifier

Preparation and Characterization of Polyurethane-Acrylate Hybrid Emulsion

Studies on water resistance of the films from waterborne polyurethane hybrid emulsion