Abstract:Tm3+/Yb3+-codoped transparent oxyfluoride glass and glass ceramics were prepared by melt-quenching and subsequently heat-treatment to forming the fluoride nanocrystals embedded among the oxide glassy matrix.The advantages of these materials are that the rare earth ions are incorporated selectively in the fluoride crystal phase with lower phonon energy after heat-treatment and the material remains transparent due to much smaller size of precipitated crystals than the wavelength of visible light.Intense blue upconversion luminescence was observed under 980 nm laser excitation.X-ray diffraction(XRD)and fluorescence spectra investigation reveal that fluoride nanocrystals are distributed homogeneously among the glassy matrix for the sample doped with Tm3+/Yb3+.Tm3+ is one of the most studied rare-earth ions for blue laser operation based on upconversion.One approach to improving the luminescent efficiency of Tm3+ is to co-doped with other rare-earth ions.The choice of host materials is also an important issue when it deals with improving the efficiency of the emission process.With the increasing Yb3+ concentration,blue upconversion emissions show different variable tendency in glass and glass ceramics co-doped with Tm3+/Yb3+.In this paper,different upconversion energy transfer processes were explained and reverse energy transfer pathway from Tm3+(3H4)to Yb3+(2F5/2)was influenced by crystal lattice field in glass and glass ceramics.In glass,the competition of positive and reverse energy transfer between Tm3+ and Yb3+ ions causes maximal blue upconversion emission at optimal Yb3+ concentration.The blue upconversion emission,however,increases with the increasing Yb3+ ion in glass ceramics.

Optical properties of Tm3+-doped fluorozirconate glass

Optical transitions of Tm3+ ions in fluorozirconate glass

Optical Transitions and Up-Conversion Emission of Tm3+-singly Doped and Tm3+/Yb3+-codoped Oxyfluoride Glasses

The Upconversion Phenomenon in Tm3+-Doped Tellurite Glass

Spectral Properties of Tm 3+/yb3+ Co-doped Fluoride-Oxy Glass

Increased Radiative Lifetime of Tm3+:3F4→3H6 Transition in Oxyfluoride Tellurite Glasses

Mechanics of Upconversion Luminescence in Glass and Glass Ceramics Co-doped with Tm3+/Yb3+

Spectroscopic Properties Eu3+ Doped and Tm3+/Yb3+ Codoped Oxyfluoride Glass Ceramics Containing Ba2GdF7 Nanocrystals

Upconversion emissions in Yb<sup>3+</sup>–Tm<sup>3+</sup>-doped tellurite glasses excited at 976 nm

Multi-photon Absorption Upconversion Luminescence of a Tb^3+-doped Glass Excited by an Infrared Femtosecond Laser

Spectroscopic properties and energy transfer parameters of Yb 3 + /Tm 3 + co-doped fluorogermanate glasses

The Upconversion Luminescence Of Zblan : Tm3+,Yb3+ Glass Pumped By A Similar To 970nm Ld And Its Concentration Effect

Upconversion emissions in Yb 3+ –Tm 3+ -doped tellurite glasses excited at 976 nm

&Lt;title>upconversion Luminescence of ZBLAN:Tm <formula><sup><roman>3+</roman></sup></formula>,yb<formula><sup><roman>3+</roman></sup></formula>glass Pumped by a ~970-Nm LD and Its Concentration Effect</title>

Upconversion Properties of Er3+, Yb3+ and Tm3+ Codoped Fluorophosphate Glasses

Upconversion luminescence of ZBLAN:Tm3+,Yb3+ glass pumped by a approximately 970 nm LD and its concentration effect

Down-/Up-conversion luminescence behaviors and energy transfer analysis in Tm3+ and Tm3+/Yb3+ co-doped tellurite glasses

Upconversion emissions in Yb–Tm-doped tellurite glasses excited at 976 nm

Blue Upconversion Emission from Tm3+ Ion Doped into Glass Ceramics under Infrared Light (1.06 Mu M) Excitation

Investigation on Up-Conversion Luminescence of Tm3+ and Yb3+ Codoped Oxy-Fluorosilicate Glass Ceramics

Mid-infrared Luminescence Properties of Tm~(3+) and Ho~(3+) Co-doped Fluorogermanate Glasses