Upconversion Luminescence of Tm~(3+)/Yb~(3+) Codoped Oxyfluoride Glasses Ppumped at 970 nm
Duan Zhongchao,Zhang Junjie,He Dongbing,Dai Shixun,Hu Lili
DOI: https://doi.org/10.3321/j.issn:0253-2239.2005.12.015
2005-01-01
Acta Optica Sinica
Abstract:A new oxyfluoride glass system was developed with molar fractions of n(SiO_2)=0.30,n(PbF_2)=0.50,n=(Al_2O_3)=0.15,n(AlF_3)=(0.049-x),n(TmF_3)=y,n(YbF_3)=x(x=0,0.001,0.010,0.015,0.020,y=0,0.001) and its upconversion emission properties were investigated.Furthermore the upconversion mechanism was discussed.The experimental results showed that there was not upconversion emission for Tm~(3+) singly doped glasses under 970 nm excitation.While strong blue(452 nm,476 nm),red(647 nm) and near infrared(971 nm) emissions were found in Tm~(3+)/Yb~(3+) codoped glasses,which responded to the following radiative transition:()~1D_2→()~3F_4,()~1G_4→()~3H_6,()~1G_4→()~3F_4 and()~3H_4→()~3H_6.Moreover,the intensity of upconversion luminescence was strongly dependent on the concentration of Yb~(3+).It was indicated that under 970 nm excitation the upconversion luminescence intensity of Tm~(3+) increased with Yb~(3+) sensitizing.With Yb~(3+) concentration increasing,absorption of pump source and energy transfer between Tm~(3+) and Yb~(3+) were both enhanced,and as a result the upconversion luminescence intensity was increased.