Abstract:Tm3+/Yb3+-codoped transparent oxyfluoride glass and glass ceramics were prepared by melt-quenching and subsequently heat-treatment to forming the fluoride nanocrystals embedded among the oxide glassy matrix.The advantages of these materials are that the rare earth ions are incorporated selectively in the fluoride crystal phase with lower phonon energy after heat-treatment and the material remains transparent due to much smaller size of precipitated crystals than the wavelength of visible light.Intense blue upconversion luminescence was observed under 980 nm laser excitation.X-ray diffraction(XRD)and fluorescence spectra investigation reveal that fluoride nanocrystals are distributed homogeneously among the glassy matrix for the sample doped with Tm3+/Yb3+.Tm3+ is one of the most studied rare-earth ions for blue laser operation based on upconversion.One approach to improving the luminescent efficiency of Tm3+ is to co-doped with other rare-earth ions.The choice of host materials is also an important issue when it deals with improving the efficiency of the emission process.With the increasing Yb3+ concentration,blue upconversion emissions show different variable tendency in glass and glass ceramics co-doped with Tm3+/Yb3+.In this paper,different upconversion energy transfer processes were explained and reverse energy transfer pathway from Tm3+(3H4)to Yb3+(2F5/2)was influenced by crystal lattice field in glass and glass ceramics.In glass,the competition of positive and reverse energy transfer between Tm3+ and Yb3+ ions causes maximal blue upconversion emission at optimal Yb3+ concentration.The blue upconversion emission,however,increases with the increasing Yb3+ ion in glass ceramics.

Blue Upconversion Luminescence in Tm3+/Yb3+-Codoped Lead Chloride Tellurite Glass

Host Dependent Frequency Upconversion of Yb3+/Tm3+-Codoped Oxyfluoride Tellurite Glasses

Upconversion Luminescence and Mechanisms of Tm3+/Yb3+-codoped Oxyhalide Tellurite Glasses

Upconversion Luminescence of Lead Halide-Modified Tm3+/Yb3+-codoped Tellurite Glasses

980 Nm Laser-Diode-excited Intense Blue Upconversion in Tm3+∕Yb3+-codoped Gallate–bismuth–lead Glasses

Upconversion emissions in Yb 3+ –Tm 3+ -doped tellurite glasses excited at 976 nm

Blue Upconversion Luminescence in Tm^(3+)/Yb^(3+) Co-Doped New Oxyfluoride Tellurite Glass

Upconversion Luminescence and Mechanisms in Yb3+-sensitized Tm3+-doped Oxyhalide Tellurite Glasses

Blue Upconversion Luminescence for Yb3+/Tm3+ Co-Doped Borosilicate Glasses

Blue Upconversion Emission In Yb3+ And Tm3+ Codoped Lead-Germanate-Tellurite Glasses

Upconversion emissions in Yb<sup>3+</sup>–Tm<sup>3+</sup>-doped tellurite glasses excited at 976 nm

Effects of chloride introduction on up-conversion luminescence in Tm3+ -doped tellurite glasses.

Blue Upconversion Emission in Yb <sup>3+</sup> and Tm <sup>3+</sup> Codoped Lead–Germanate–Tellurite Glasses

Intense Blue Up-Conversion Luminescence in Tm3+/Yb3+ Codoped Oxyfluoride Glass-Ceramics Containing Beta-Pbf2 Nanocrystals

Upconversion Luminescence of Tm3+/Yb3+-codoped Oxyhalide Tellurite Glasses

Upconversion emissions in Yb–Tm-doped tellurite glasses excited at 976 nm

Mechanisms and Concentrations Dependence of Up-Conversion Luminescence in Tm3+/Yb3+ Codoped Oxyfluoride Glass-Ceramics

Up-conversion Luminescence Properties of Yb3+/Tm3+ Co-doped Silicate Glasses

Upconversion Properties of Er3+, Yb3+ and Tm3+ Codoped Fluorophosphate Glasses

Optical Parameters and Upconversion Fluorescence in Tm3+/Yb3+ Codoped Tellurite Glass

Mechanics of Upconversion Luminescence in Glass and Glass Ceramics Co-doped with Tm3+/Yb3+