Abstract:The effect of cooling on the brittleness of glasses in general, and bulk metallic glasses (BMGs) in particular, is usually studied with continuously varying cooling rates; slower cooling rates lead to stiffer, harder, and more brittle glasses than higher cooling rates. These protocols obscure any potential discontinuity that a glass might experience depending on whether its microstructure resembles that of a fragile or a strong glass-forming liquid. Here, we use large-scale molecular dynamics to simulate the nanoindentation behavior of model BMGs (Zr$_{0.6}$Cu$_{0.3}$Al$_{0.1}$) obtained by rapidly quenching equilibrium melts from temperatures above and below the fragile-to-strong transition temperature $T_\textrm{fst}$, leading to fragile and strong glasses, respectively. While the contact modulus deduced from the indentation simulation evolves smoothly with the temperature $T_\text{q}$ from which the melt is quenched, the plastic response changes quasi-discontinuously as $T_\text{q}$ passes through $T_\textrm{fst}$. In particular, strong glasses develop highly asymmetric flow profiles with mature shear bands, in contrast to fragile glasses. Quantitative differences reveal themselves not only through a formal von Mises localization parameter analysis but also through image analysis of flow patterns using pre-trained artificial intelligence models. Moreover, seemingly erratic flow profiles for our indentation geometry produced surprisingly reproducible and, thus, deterministic features. It remains to be determined to what extent other classes of glass formers follow our observation that the degree of brittleness is significantly influenced by whether the melt is fragile or strong when it falls out of equilibrium at the glass transition temperature.

Embrittlement of A Bulk Metallic Glass Due to Low-Temperature Annealing

Isothermal annealing induced embrittlement of Zr41.25Ti13.75Ni10Cu12.5Be22.5 bulk metallic glass

Tension and stress relaxation behavior of a La-based bulk metallic glass

Ambient Temperature Embrittlement of a Zr-based Bulk Metallic Glass

Mechanical Property Degradation of a CuZr-based Bulk Metallic Glass Composite Induced by Sub-Tg Annealing

The Effects of Annealing on the Microstructure and the Dynamic Mechanical Strength of a ZrCuNiAl Bulk Metallic Glass

Annealing Effect on Beta-Relaxation in a La-based Bulk Metallic Glass

Investigation of Deformation Behavior of Zr-Ti-Ni-Cu-Be Bulk Metallic Glass Containing Nanocrystals

Atomic Origin of Annealing Embrittlement in Metallic Glasses

Microstructure and Mechanical Properties of A Partially Crystallized La-Based Bulk Metallic Glass

Structural transformation and rheological processes in bulk metallic glass Zr41Ti14Cu12.5Ni10Be22.5

Brittleness of metallic glasses dictated by their state at the fragile-to-strong transition temperature

Sub-T-g Annealing Effect on the Kinetics of Glass Transition and Crystallization for a Ti-Zr-Be-Fe Bulk Metallic Glass

Temperature-Induced Ductile-To-Brittle Transition of Bulk Metallic Glasses

Intermediate Temperature Brittleness in Metallic Glasses

Suppression of Annealing-Induced Embrittlement in Bulk Metallic Glass by Surface Crystalline Coating

The Effects of Thin Coatings on the Mechanical Properties and Resistance to Annealing-Induced Embrittlement of Bulk Metallic Glass

Temperature Effect on Fracture of a Zr-Based Bulk Metallic Glass

Formation of CuZr-based Bulk Metallic Glass Composites Containing Nanometer-Scale B2-CuZr Phase Through Sub-Tg Annealing

On low-temperature strength and tensile ductility of bulk metallic glass composites containing stable or shape memory β-Ti crystals

Structural Evolution in Bulk Metallic Glass under High-Temperature Tension