Abstract:The preparation and characteristics of silicon nanoarrays is now an attractive areas of research. At present,most research focused on the optical and electrical properties and applications,and less field emission characteristics,as a mature technology of silicon planar support, silicon field emission cathode materials are easily compatible with the microelectronic integrated circuits, and so they have a broad application prospects.We present the fabrication of large-scale two dimensional periodic silicon nanoarrays using nanosphere lithography,and the field emission characteristics have been studied. The fabrication process includes following steps: first the crystalline silicon substrate was coated with a monolayer of self polystyrene (PS) spheres of 220 nm in diameter, then the sample was etched by reactive ion etching to produce silicon nanoarrays. AFM images of the nanoarrays show that the tips stand 60～70 nm high and the area density can achieve 6×109/cm2. All field emission measurements were performed at a vacuum of 1.0×10-4 Pa or better. Expected to improve the field emission characteristics, about 60 nm thickness of a amorphous carbon film was deposited on top of the silicon nanoarrays by plasma-enhanced chemical vapour deposition. Field emission results show that compared to silicon nanoarrays, silicon nanoarrays coated with a thin a-C film effectively lower the threshold fields, approximately 8.1 V/μm, while field enhancement factor increased. When the electric field intensity reached 20 V/μm, the current density can reach about 1.4 mA/cm2. The improvement of field emission originates from the anisotropic structure of the films,when conductive sp2 clusters embedded in an insulating sp3 matrix,the electric field has been enhanced.

Synthesis and Field Emission Characteristics of Carbon Nanosheets

Synthesis and Characterization of Carbon Nanotube Grown on Flexible and Conducting Carbon Fiber Sheet for Field Emitter

Field Emission from Dense, Sparse, and Patterned Arrays of Carbon Nanofibers

Field Emission from Few-Layer Graphene Nanosheets Produced by Liquid Phase Exfoliation of Graphite.

Nanosized graphene sheets enhanced electron field emission behavior in pure carbon film

Field emission from Nanocomposite Carbon

Field Emission Properties of Nanocomposite Carbon Nitride Films

Field emission from a new form of thin film amorphous carbon having nanoparticle inclusions and carbon nanotubes

Carbon Nanotubes As Field Emission Sources

Field Emission From Short And Stubby Vertically Aligned Carbon Nanotubes

Field Emission of Graphene and Carbon Nanotubes

Flame-synthesis of Carbon Nanotubes on Silicon Substrates and Their Field Emission Properties

Experimental Studies on Field Emission Characteristic of Graphite

Microwave sintering and field emission property of CNTs/diamond composite

Electron Field Emission Characteristics from Single-crystal Silicon Nanoarrays Fabricated by Direct Lithography with Nanosphere Mask

Uniform carbon nanoflake films and their field emissions

The synthesis of vertically oriented carbon nanosheet-carbon nanotube hybrid films and their excellent field emission properties

Synthesis of CNTs Film and Influence of Treatment of CNTs Film on Field Emission Properties

Field emission of graphite nanosheets/diamond and carbon nanotubes/diamond composites sintered

Field emission behavior of aligned carbon nanofiber arrays

Preparation and characterization of graphene nanosheets from graphite flakes through assisted intercalation-expansion using a microwave oven