Abstract:Both the cubic single crystals and the spherical polycrystals of cuprous oxides (Cu2O) were prepared by the reduction of aqueous CuSO4, with hydrazine as a reductant in the presence of different organic molecule additives, such as hexadecyltrimethyl ammonium bromide (CTAB), glucose (C6H12O6), ethylene glycol (C2H6O2), and glycerol (C3H8O3), at room temperature. It was found that the organic additives added had an important influence on the formation mechanism of the Cu2O particles and could lead to different microstructures of the resultant Cu2O crystallites. The addition of CTAB to the reaction solution could induce the formation of cubic Cu2O single crystals, while glucose resulted in the formation of spherical polycrystals. All the samples were characterized by X-ray powder diffraction and transmission electron microscope (TEM). TEM observations indicated that the nanosized primary particles formed immediately after the reactants were mixed, followed by the competition between diffusion of the reactive constituents and aggregation of the nanosized primary particles. In the presence of CTAB, the diffusion of the reactants was a major factor contributing to the single crystal morphology of the Cu2O products, while the aggregation of the primary nano-particles into polycrystallites prevailed when glucose existed in the reaction system.

Preparation of Hollow Cuprous Oxide Nano-particles and Their Optical Properties

Preparation of Cuprous Oxide Particles of Different Crystallinity

Microstructure, Morphology and Sunlight Response of Cuprous Oxide Thin Films

Morphology Control Of Cuo Micro-Particles Using Zn2+ Ion And Ultrasonic Treatment

Size-controlled Preparation of Cu2O Octahedron Nanocrystals and Studies on Their Optical Absorption

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Preparation and optical properties of Cu2O hollow microsphere film and hollow nanosphere powder via a simple liquid reduction approach

Optical Properties of Cuprous Oxide Nanocrystals

Photocatalytic Degradation of Cuprous Oxide Nanostructures Under UV/Visible Irradiation

Synthesis of Highly Monodisperse Cu2O Nanocrystals and Their Applications as Hole-Transporting Layers in Solution-Processed Light-Emitting Diodes.

Preparation of CuO Nanoparticles by Microwave Irradiation

Growth and Morphological Evolution of Hexapod-Shaped Cuprous Oxide Microcrystals at Room Temperature

Formation of solid and hollow cuprous oxide nanocubes in water-in-oil microemulsions controlled by the yield of hydrated electrons.

Preparation of CdS Nanoparticles by Hydrothermal Method in Microemulsion

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

Preparation of Ultrafine Cu 2 O Powders with Different Morphologies from Cu(OH) 2 Gel

Spherical CuI Nanoparticles Prepared by Liquid Phase Method

Preparation of Large-Scale Cupric Oxide Nanowires by Thermal Evaporation Method

Preparation of Micron Size Cuprous Oxide Powder from Acidic CuCl2 Etchant Waste Solution

Synthesis and Photocatalytic Characterization of Porous Cuprous Oxide Octahedra

A novel wet-chemical method of preparing highly monodispersed Cu2O nanoparticles