Abstract:CuO nanowires are known to have excellent electrochemical properties and can be produced by various methods. Among them a method which directly heat either the Si wafer with Cu layer or pure copper plate so called the thermal oxidation method has lately been drawing attention. However, during its production, interfacial delamination between the Cu layer and the wafer has always been an issue. In this study, the mechanism of interfacial delamination was experimentally elucidated by comparing a Si wafer with Cu layer deposited by electron beam evaporation with a pure copper plate. As a result, it was found that the deposited Cu layer decreased with increasing heating time of the Si wafer production. Moreover, the disappearance of the Cu layer and Cu2O layer on the Si wafer was found in the specimens with a heating time of 6 hours. It was suggested that this disappearance would form an opening between the CuO layer and the Si wafer leading to the delaminating of the interface between the oxide film and the wafer. The disappearance also suggested that the length and density of the CuO nanowires in the specimens with a heating time of 6 hours were minimized. As for the pure copper plate, the disappearance of the Cu layer and Cu2O layer was not seen regardless of the heating time, therefore there was no interfacial delamination and it was able to produce CuO nanowires at a high density.

Preparation of Large-Scale Cupric Oxide Nanowires by Thermal Evaporation Method

Large-scale Growth of Copper Oxide Nanowires on Various Copper Substrates

Cuprite Nanowires by Electrodeposition from Lyotropic Reverse Hexagonal Liquid Crystalline Phase

Growth of CuO Nanowires on Si Substrate by Thermal Oxidation Method and Its Interfacial Delamination Mechanism.

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

A Simple Wet Chemical Route for Large-Scale Synthesis of Cu(Oh)(2) Nanowires

Control of the Diameters of Cu2o Nanowires Fabricated by the Thermal Stress-Induced Method

Electrochemical Synthesis of Copper Nanowires

Thermal Oxidation Of Cu2s Nanowires: A Template Method For The Fabrication Of Mesoscopic Cuxo(X=1,2) Wires

Cu/SiO 2−x Nanowires with Compositional Modulation Structure Grown Via Thermal Evaporation

Characterization of zinc oxide crystal nanowires grown by thermal evaporation of ZnS powders

Thermal Evaporation Synthesis of Zinc Oxide Nanowires

In Situ Structure Evolution from Cu(OH)2 Nanobelts to Copper Nanowires

Preparation And Characterization Of Cuo Nanowire Arrays

Preparation and Characterization of CuO Nanorods by Thermal Decomposition of CuC2O4 Precursor

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Controllable Fabrication and Electrical Performance of Single Crystalline Cu2O Nanowires with High Aspect Ratios

P2&#x2013;26: Thermodynamic Mechanism Responsible for Growth of CuO Nanowires by Thermal Oxidation

Preparation of VO2 nanowires and their electric characterization

Oxide-assisted nucleation and growth of copper sulphide nanowire arrays