Abstract:CuO nanowires are known to have excellent electrochemical properties and can be produced by various methods. Among them a method which directly heat either the Si wafer with Cu layer or pure copper plate so called the thermal oxidation method has lately been drawing attention. However, during its production, interfacial delamination between the Cu layer and the wafer has always been an issue. In this study, the mechanism of interfacial delamination was experimentally elucidated by comparing a Si wafer with Cu layer deposited by electron beam evaporation with a pure copper plate. As a result, it was found that the deposited Cu layer decreased with increasing heating time of the Si wafer production. Moreover, the disappearance of the Cu layer and Cu2O layer on the Si wafer was found in the specimens with a heating time of 6 hours. It was suggested that this disappearance would form an opening between the CuO layer and the Si wafer leading to the delaminating of the interface between the oxide film and the wafer. The disappearance also suggested that the length and density of the CuO nanowires in the specimens with a heating time of 6 hours were minimized. As for the pure copper plate, the disappearance of the Cu layer and Cu2O layer was not seen regardless of the heating time, therefore there was no interfacial delamination and it was able to produce CuO nanowires at a high density.

Preparation and Characterization of CuO Nanorods by Thermal Decomposition of CuC2O4 Precursor

Preparation and characterization of NiO nanorods by thermal decomposition of NiC2O4 precursor

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Preparation and Characterization of SnO2 Nanorods by Thermal Decomposition of SnC2O4 Precursor

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

A simple and novel route for the preparation of ZnO nanorods

Fabrication Of Coo Nanorods Via Thermal Decomposition Of Coc2o4 Precursor

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

Synthesis of NiO nanorods by a novel simple precursor thermal decomposition approach

Growth of CuO Nanowires on Si Substrate by Thermal Oxidation Method and Its Interfacial Delamination Mechanism.

Preparation, characterization and catalytic property of CuO nano/microspheres via thermal decomposition of cathode-plasma generating Cu2(OH)3NO3 nano/microspheres.

Preparation and characterization of ZnO nanorods

Preparation And Characterization Of Cuo Nanowire Arrays

Cuo Nanodendrites Synthesized by A Novel Hydrothermal Route

Preparation and Characterization of Copper Oxide Nanoparticles Through Solid State Thermal Decomposition of an Aqua Nitrato Copper(II) Complex with a Tridentate Schiff-base Ligand as a New Precursor

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Preparation and characterization of hierarchical nanostructures composed by CuO nanowires within directional microporous Cu

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Preparation of Large-Scale Cupric Oxide Nanowires by Thermal Evaporation Method

In-situ Preparation of 1D CuO Nanostructures Using Cu2(OH)2CO3 Nanoribbons As Precursor for Sacrifice-Template Via Heat-Treatment

Growth of Novel Nanostructured Copper Oxide (cuo) Films on Copper Foil