Thermal Weight Loss Performance of the SL Resin Used for Investment Casting

康小青,李涤尘,段玉岗,张莹莹

DOI: https://doi.org/10.14136/j.cnki.issn1673-2812.2013.01.016

2013-01-01

Abstract:The resin prototype made with stereolithography can been used as investment casting model.The gas release and expansion during resin model baking could crack the ceramic shell.Therefore,the weight loss process is a key issue to the formation of ceramic shell.The effects of the molecular structure,crosslinking density and monomer content on weight loss performance of cured resin were investigated in this paper.The results show that the UV-curable resin with weak bond exhibits low initial decomposition temperature,and gentle thermo-gravimetric curve slopes;The resin with rigid structure such as phenyl group exhibits high initial decomposition temperature;Both the function group number and the content of reactive monomer have important effect on thermal weight loss procedure,the weight loss of cured resin becomes difficult with increasing function group number,and vice versa.The initial weight loss temperature increases with the increase in reactive multi-function group monomer content.When the monomer content reaches a certain level however,the resin's weight loss becomes easier resulting from the decrease of the rigid groups ratio in the cured resin.The crosslink density also has an important effect on the initial decomposition temperature: the higher crosslink density,the higher initial decomposition temperature,and accordingly higher maximum thermal weight loss temperature.The baking experiment of the resin blade prototype verified that the ceramic blade shell without crack could be obtained using the resin prepared in the paper.