Numerical Simulation Study of Laser-arc Hybrid Welding of 6063/5083 Aluminum Alloy
Xiaowen Chen,Song Tang,Wanlin Xie,Defen Zhang
DOI: https://doi.org/10.1007/s11665-024-09842-4
IF: 2.3
2024-07-23
Journal of Materials Engineering and Performance
Abstract:This study numerically simulates the laser-arc hybrid welding of 6-mm-thick 6063/5083 dissimilar aluminum alloy plates using Simufact welding simulation software. The changes in workpiece stress and deformation are calculated from the fixture clamping state, pre-welding heating, and post-welding heat treatment. The results indicate that unloading the fixture at an appropriate time is beneficial for reducing residual stress in the workpiece, especially on the 5083 aluminum alloy side, where it can decrease by up to 43 MPa. However, unloading the fixture can increase the amount of workpiece deformation and cause significant angular deformation. Increasing the preheating temperature has a positive effect on reducing residual stress on both sides of the base material. When the preheating temperature is between 70 and 170 °C, the high residual stress area on the 5083 aluminum alloy side decreases most significantly, ultimately reaching 128 MPa. Meanwhile, within this preheating temperature range, the total deformation of the workpiece is relatively small, and its effect on the weld position is not significant. Excessively high preheating temperatures can increase the lateral shrinkage of the workpiece. The annealing temperature after welding mainly affects the rate of workpiece heating. After annealing treatment, the stress at the weld position decreases significantly, and its lateral shrinkage improves, which is beneficial for improving dimensional accuracy.
materials science, multidisciplinary