Abstract:This study deals with the effect of conventional sintering and microwave sintering on the densification kinetics of Titanium Carbide (TiC) in the presence of Ni (1, 1.5, 2 wt%). TiC compacts were obtained after uniaxial pressing of powders synthesised by ball milling of Titanium and Carbon and sintering was done in the presence of Nickel. The samples prepared were subjected to conventional as well as microwave sintering. The XRD and SEM analysis were used for a study of the reaction of Ti and C powders upon addition of Ni, which reduced the sintering temperature to 1200 °C. The densification of TiC powders was due to the Ti-Ni eutectic system, the liquid phase formed at this temperature assisting the sintering process. The SEM images revealed the flake like structure of TiC in which the carbon diffused into Ti upon the addition of Ni, thereby supporting enhanced mass transfer. The XRD pattern showed the presence of Titanium Oxide (TiO2) along with TiC which resulted in non-uniform distribution of hardness. Maximum hardness was achieved in the conventional sintered compacts which gradually increased with increase in Ni addition. The presence of the oxide phase and the formation of micro cracks resulted in non-uniform hardness for microwave sintered compacts. The maximum hardness of conventional sintered compact (375 HLD) was nearly 1.5 times more than the maximum hardness of the microwave sintered compact (250 HLD). The density of the microwave sintered compact was found to be higher by 8% than with the conventionally sintered compact.

Preparation of titanium carbide powders by sol–gel and microwave carbothermal reduction methods at low temperature

Preparation of Titanium Carbide by Carburisation of Titanium Dioxide

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Preparation of Nano-TiC Powders by In-situ Carbothermal Method in Vacuum

Preparation of Titanium Carbonitride Powder by Carbothermal Reduction Method

Synthesis and Characterization of TiC Nanopowders Via Sol-Gel and Subsequent Carbothermal Reduction Process

Carbothermal Preparation of Ultra-Fine TiB2 Powders Using Solution-Derived Precursors Via Sol-Gel Method

Synthesis of Ti(C,N) ultrafine powders by carbothermal reduction of TiO2 derived from sol–gel process

Exploring the impact of pH and temperature on TiC nanopowders syntesized via sol-gel and subsequent crystallization by carbothermal reduction method

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

Studies on the carbothermal preparation of titanium carbonitride powders in the open system

Synthesis of Stoichiometric Titanium Carbide by a Combination of Carbothermal Reduction and Molten Salt Method and Its Characterization

Microwave Synthesis of Nano-Titanium Carbide

Synthesis of Superfine Tib2 Powders by Low-Temperature Carbothermal Reduction

Progress in Preparation and Application of Ultrafine TiC Powder

Synthesis of TiC Powder by Carbothermal Reduction and Phase Evolution

Formation of Ultrafine Titanium Carbide Powder by Combustion Synthesis

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Low Temperature Synthesis of Nano Ti(C, N) by Novel Mechanical and Thermal Activation Method

Low Temperature and Pressureless Synthesis of High-Purity Ti3SiC2 MAX Phase from TiC Via Κ-Al2o3 Addition Through Reactive Melt Infiltration

Influence of Several Carbon Source on Ti(C,N)powders Prepared by Carbothermal Reduction and Nitridation Method