Hydrogen Storage Properties of LaMg2Ni Prepared by Induction Melting

L. Z. Ouyang,L. Yao,H. W. Dong,L. Q. Li,M. Zhu

DOI: https://doi.org/10.1016/j.jallcom.2009.06.005

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:LaMg2Ni compound was prepared by induction melting, and its phase transformation during hydriding/dehydriding as well as hydrogen storage properties were investigated by X-ray diffraction (XRD) and pressure–composition isotherm (PCI) measurement. It was found that the reversible hydrogen storage capacity of LaMg2Ni alloy reaches 1.96wt.%. The enthalpy and entropy derived from the van’t Hoff equation for hydriding/dehydriding are −51kJ/mol H2, −105J/Kmol H2 and 79kJ/mol H2, 141J/Kmol H2, respectively. The kinetic curve for the hydriding at 561K was well fitted by the Avrami–Erofeev equation.