A Hierarchical Zeolite Microsphere Prepared by an Eco-Friendly and Practical Route for Efficient Reaction of Bulky Molecules
Sufang Hu,Hanqiong Jia,Jinghong Ma,Wenming Hao,Ruifeng Li
DOI: https://doi.org/10.1016/j.micromeso.2019.109931
IF: 5.876
2019-01-01
Microporous and Mesoporous Materials
Abstract:The hierarchical zeolite ZSM-5 was synthesized in a CH3CH2OH-H2O hydrothermal system by using hexadecyltrimethyl ammonium bromide (CTAB) as sole template at a low crystallization temperature (130 degrees C). The effects of ethanol and CTAB on crystallization process and morphologies of ZSM-5 products were investigated. Ethanol molecules in synthesis system were beneficial to speed up crystallization, though crystal growth in NaOH-CTAB-H2O system was more difficult. The existence of CTAB resulted in highly crystalline and pure phase hierarchical ZSM-5 microspheres assembled by nanocrystals. The traces of crystallization evolution by XRD, FT-IR, N-2 adsorption/desorption, SEM/TEM, Si-29 MAS NMR, Al-27 MAS NMR spectra and TGA revealed that the hierarchical ZSM-5 microspheres were formed through the transformation of mesostructured amorphous aluminosilicates, in which the initial surfactant micelles were gradually excluded and thus acted as a molecule structure-directing agent to direct the crystallization of MFI nanozeolite. At the same time, the CTAB may disrupt nanocrystals further growth and aggregate them into hierarchical microsphere through CTA(+). Pyridine (Py) and pivalonitrile (Pn) adsorbed FT-IR spectra showed that the hierarchical ZSM-5 microspheres possessed large number of accessible acid sites due to the introduction of mesopores into zeolite. Therefore, it displayed much higher catalytic activities for both large molecules 1,3,5-trimethylbenzene (TMB) transformation and 1,3,5-triisopropylbenzene (TIPB) cracking reactions than conventional MFI zeolite, and the high selectivity to isomerization products (1,2,3- and 1,2,4-TMB) and benzene product from over-cracking.