ChemInform Abstract: Stabilization of Cobalt Oxyhydrate Superconductor

Zhi Ren,Cao Wang,Xiang-fan Xu,Guang-han Cao,Zhu-an Xu,Yu-heng Zhang

DOI: https://doi.org/10.1002/chin.200830021

2008-01-01

ChemInform

Abstract:Stabilization of cobalt oxyhydrate superconductor was realized by post-treatment of the as-prepared superconductor in concentrated NaOH solution; this finding is expected to promote future experimental research on the intriguing material.

What problem does this paper attempt to address?

Stabilization of cobalt oxyhydrate superconductor.

Zhi Ren,Cao Wang,Xiang-fan Xu,Guang-han Cao,Zhu-an Xu,Yu-heng Zhang

DOI: https://doi.org/10.1039/b800378e

IF: 4.9

2008-01-01

Chemical Communications

Abstract:Stabilization of cobalt oxyhydrate superconductor was realized by post-treatment of the as-prepared superconductor in concentrated NaOH solution; this finding is expected to promote future experimental research on the intriguing material.
Synthesis of Cobalt Oxyhydrate Superconductor Through a Disproportionation Reaction Route.

Z Ren,YW Wang,S Liu,J Wang,Z Xu,GH Cao

DOI: https://doi.org/10.1021/cm048228z

IF: 10.508

2005-01-01

Chemistry of Materials

Abstract:A cobalt oxyhydrate superconductor with very low content of sodium and relatively high content of hydronium was synthesized through a disproportionation route in hydrochloric acid. The disproportionation react on was accompanied by ion exchange between Na+ and H3O+. By using the Na+ ion-selective electrode (ISE) method, energy-dispersive X-ray (EDX) spectroscopy, and thermogravimetric analysis, the composition of the superconductor was determined as Na-0.15(H3O)(0.2)CoO2 center dot wH(2)O. Magnetic susceptibility measurement indicated the bulk superconductivity below 4.1 K. The new synthetic method is expected to be employed in fabricating the superconducting cobalt oxyhydrate crystals.
SYNTHESIS AND CHRACTERIZATION OF COBALT OXYHYDRATE SUPERCONDUCTORS

GUANG-HAN CAO,ZHI REN,ZHU-AN XU

DOI: https://doi.org/10.3969/j.issn.1000-3258.2005.z1.001

2005-01-01

Abstract:Recent discovery of the first cobalt oxide superconductor has received much attention. Thenew superconductorshows extremechemical instability under ambient environment, therefore, the synthesis and characterization of the superconductor becomes an important issue. We present the characterizations as well as some typical synthetic method in this paper. A superconductor with very low content of sodium and very high content of hydronium through adisproportionation reaction route is reported.
Tuning Co Valence State in Cobalt Oxyhydrate Superconductor by Postreduction

Zhi Ren,Jian-Lin Luo,Zhu-An Xu,Guang-Han Cao

DOI: https://doi.org/10.1021/cm0702262

IF: 10.508

2007-01-01

Chemistry of Materials

Abstract:We report a successful tuning of Co valence state in cobalt oxyhydrate superconductor via a facile postreduction using NaOH as reducing agent. The change in Co valence was precisely determined by measuring the volume of the released oxygen. The possible hydronium incorporation was greatly suppressed in concentrated NaOH solution, making the absolute Co valence determinable. As a result, an updated superconducting phase diagram was obtained, which shows that the superconducting transition temperature increases monotonically with increasing Co valence in a narrow range from +3.58 to +3.65.
Chemical instability of the cobalt oxyhydrate superconductor under ambient conditions

M.L. Foo,R.E. Schaak,V.L. Miller,T. Klimczuk,N.S. Rogado,Y. Wang,G.C. Lau,C. Craley,H.W. Zandbergen,N.P. Ong,R.J. Cava

DOI: https://doi.org/10.1016/s0038-1098(03)00334-x

IF: 1.934

2003-06-01

Solid State Communications

Abstract:The layered sodium cobalt oxyhydrate superconductor Na0.3CoO2·1.4H2O is shown through X-ray diffraction and thermogravimetric studies to be one of the series of hydrated phases of Na0.3CoO2. Further, it is shown that the material is exceptionally sensitive to both temperature and humidity near ambient conditions, easily dehydrating to a non-superconducting lower hydrate. The observation of this stable lower hydrate with c=13.8Å implies that the superconductivity turns on in this system between CoO2 layer spacings of 6.9 and 9.9Å at nominally constant chemical doping.

physics, condensed matter
SUPERCONDUCTIVITY IN Na0.15(H3O)0.2CoO2·wH2O

ZHI REN,SONG LIU,GUANG-HAN CAO

DOI: https://doi.org/10.3969/j.issn.1000-3258.2005.z1.006

2005-01-01

Abstract:The newly discovered cobalt oxyhydrate superconductor bears similarity with the high temperature cuprate superconductor in view of their superconducting properties. In this paper, we report the superconducting properties of the cobalt oxyhydrate with relatively high hydronium content under magnetic fields. Finally, we discussed the possible 2D~3D crossover based on the obtained H-T phase diagram.
Hydrothermal Synthesis of Cobalt Sulfide Nanotubes: the Size Control and Its Application in Supercapacitors

Houzhao Wan,Xiao Ji,Jianjun Jiang,Jingwen Yu,Ling Miao,Li Zhang,Shaowei Bie,Haichao Chen,Yunjun Ruan

DOI: https://doi.org/10.1016/j.jpowsour.2013.06.027

IF: 9.2

2013-01-01

Journal of Power Sources

Abstract:Cobalt sulfide nanotubes are synthesized by hydrothermal method. The precursor is characterized by XRD, FTIR and SEM. We study the influence of temperature on the evolution of this special coarse shape nanostructure and analyze relationship between the sizes of cobalt sulfide nanotubes and the capacitive properties of active materials. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) are used to study the effects of microstructure and morphology of the samples on their capacitance and conductivity. The specific capacitance of cobalt sulfide nanotubes (obtained in 80 C) electrode exhibits a capacitance of 285 F g(-1) at the current density of 0.5 A g(-1) as well as rather good cycling stability. Moreover, during the cycling process, the coulombic efficiency remains 99%. The as-prepared cobalt sulfide nanotubes electrode exhibits excellent electrochemical performance as electrode materials for supercapacitors. (C) 2013 Elsevier B.V. All rights reserved.
Proton incorporations and superconductivity in a cobalt oxyhydrate

Guanghan Cao,Xiaoming Tang,Yi Xu,Ming Zhong,Xuezhi Chen,Chunmu Feng,Zhu'an Xu

DOI: https://doi.org/10.1016/j.ssc.2004.04.034

IF: 1.934

2004-07-01

Solid State Communications

Abstract:We report evidence of proton incorporations in a newly-discovered cobalt oxyhydrate superconductor. During the hydration process for Na0.32CoO2 by the direct reaction with liquid water, it was shown that substantial NaOH was gradually liberated, indicating that H+ is incorporated into the hydrated compound. Combined with the thermogravimetric analysis, the chemical composition of the typical sample is Na0.22H0.1CoO2·0.85H2O. It shows bulk superconductivity at 4.4 K.

physics, condensed matter
A novel route to phase formation of cobalt oxyhydrates using KMnO4 as an oxidizing agent

C.-J. Liu,C.-Y. Liao,L.-C. Huang,C.-H. Su,S. Neeleshwar,Y.-Y. Chen

DOI: https://doi.org/10.1016/j.physc.2004.09.005

2004-05-12

Abstract:We have first succeefully synthesized the sodium cobalt oxyhydrate superconductors using KMnO4 as a de-intercalating and oxidizing agent. It is a novel route to form the superconductive phase of NaxCoO2.yH2O without resorting to the commonly used Br2/CH3CN solution. The role of the KMnO4 is to de-intercalate the Na+ from the parent compound Na0.7CoO2 and oxidize the Co ion as a result. The higher molar ratio of KMnO4 relative to the sodium content tends to remove more Na+ from the parent compound and results in a slight expansion of the c-axis in the unit cell. The superconducting transition temperature is 4.6-3.8 K for samples treated by the aqueous KMnO4 solution with the molar ratio of KMnO4 relative to the sodium content in the range of 0.3 and 2.29.

Superconductivity,Materials Science
Superconductor made by electrolyzed and oxidized water

Chia-Jyi Liu,Tsung-Hsien Wu,Lin-Li Hsu,Jung-Sheng Wang,Shu-Yo Chen,Wei Jen Chang,Jiunn-Yuan Lin

DOI: https://doi.org/10.48550/arXiv.cond-mat/0604264

2006-04-11

Superconductivity

Abstract:By deintercalation of Na+ followed by inserting bilayers of water molecules into the host lattice, the layered cobalt oxide of gamma-Na0.7CoO2 undergoes a topotactic transformation to a layered cobalt oxyhydrate of Na0.35(H2O)1.3CoO2-delta with the c-axis expanded from c = 10.9 anstrom to c = 19.6 anstrom. In this paper, we demonstrate that the superconducting phase of c = 19.6 anstrom can be directly obtained by simply immersing gamma-Na0.7CoO2 powders in electrolyzed/oxidized (EO) water, which is readily available from a commercial electrolyzed water generator. We found that high oxidation-reduction potential of EO water drives the oxidation of the cobalt ions accompanying by the formation of the superconductive c = 19.6 anstrom phase. Our results demonstrate how EO water can be used to oxidize the cobalt ions and hence form superconducting cobalt oxyhydrates in a clean and simple way and may provide an economic and environment-friendly route to oxidize the transition metal of complex metal oxides
Superconductivity and Cobalt Oxidation State in Metastable Na(x)CoO(2-delta)*yH2O (x ~ 1/3; y ~ 4x)

P. W. Barnes,M. Avdeev,J. D. Jorgensen,D. G. Hinks,H. Claus,S. Short

DOI: https://doi.org/10.1103/PhysRevB.72.134515

2005-06-22

Abstract:We report the synthesis and superconducting properties of a metastable form of the known superconductor NaxCoO2*yH2O (x ~ 1/3, y ~ 4x). Instead of using the conventional bromine-acetonitrile mixture for sodium deintercalation, we use an aqueous bromine solution. Using this method, we oxidize the sample to a point that the sodium cobaltate becomes unstable, leading to formation of other products if not controlled. This compound has the same structure as the reported superconductor, yet it exhibits a systematic variation of the superconducting transition temperature (Tc) as a function of time. Immediately after synthesis, this compound is not a superconductor, even though it contains appropriate amounts of sodium and water. The samples become superconducting with low Tc values after ~ 90 h. Tc continually increases until it reaches a maximum value (4.5 K) after about 260 h. Then Tc drops drastically, becoming non-superconducting approximately 100 h later. Corresponding time-dependent neutron powder diffraction data shows that the changes in superconductivity exhibited by the metastable cobaltate correspond to slow formation of oxygen vacancies in the CoO2 layers. In effect, the formation of these defects continually reduces the cobalt oxidation state causing the sample to evolve through its superconducting life cycle. Thus, the dome-shaped superconducting phase diagram is mapped as a function of cobalt oxidation state using a single sample. The width of this dome based on the formal oxidation state of cobalt is very narrow - approximately 0.1 valence units wide. Interestingly, the maximum Tc in NaxCoO2*yH2O occurs when the cobalt oxidation state is near 3.5. Thus, we speculate that the maximum Tc occurs near the charge ordered insulating state that correlates with the average cobalt oxidation state of 3.5.

Materials Science,Superconductivity
ChemInform Abstract: Enhanced Oxide Ion Conductivity in Stabilized Cubic BaInO2.5 by Mn5+ Doping.

yuzeng sun,chengxu yang,ting shu,guobao li,fuhui liao,jianhua lin

DOI: https://doi.org/10.1002/chin.201332008

2013-01-01

ChemInform

Abstract:Mn‐doped, room temperature stabilized cubic BaInO 2.5 is prepared by solid state reaction of BaCO 3 , In 2 O 3 , and MnCO 3 with molar ratios of Ba:In:Mn = 1:(1‐x):x (0.13 ≤ x ≤ 0.33) in Al 2 O 3 crucibles at 1200 °C for 12 h and at 1350 °C for 24 h.
Solid-state Synthesis of Cobalt Ferrite Fitted with Γ-Fe2o3-containing Nanocage for Peroxymonosulfate Activation and Cobalt Leaching Control

Xiaojie Qiu,Dahu Ding,Shengjiong Yang,Gen Wang,Rongzhi Chen,Mawuli Dzakpasu,Pengkang Jin,Xiaochang C. Wang

DOI: https://doi.org/10.1016/j.cej.2020.126994

IF: 15.1

2020-01-01

Chemical Engineering Journal

Abstract:We report a solid-state synthesis procedure for the facile fabrication of N-doped cobalt ferrite (N-CoFeO). A surface ferric coagulation-thermal treatment process was then developed to minimize cobalt leaching by creating a gamma-Fe2O3-containing nanocage on the surface of the N-CoFeO. A remarkable decrease in the concentration of leached Co from 182.2 mu g L-1 to 2.7 mu g L-1 evidenced the promising potential of the cobalt leaching inhibition method. Further study confirmed that the minimization of cobalt leaching was achieved via cation vacancies in the gamma-Fe2O3-containing nanocage. This cation vacancies could bind metal ions and facilitate the generation of surface hydroxyl groups, rendering negligible Co leaching during reaction process. Furthermore, the nanocage covered N-CoFeO (N-CoFeO@Fex) exhibited superior performance for bisphenol A degradation within a wide pH range. Higher dosages of both the catalyst and peroxymonosulfate jointly intensified the degradation performance. Both radical and non-radical pathways were involved in the degradation process. It also should be noted that HO center dot exhibited negligible contributions to BPA degradation during the catalytic process. Furthermore, BPA degradation pathway was proposed by chromatography-mass analysis assisted with density functional theory (DFT) calculation, and the mechanism were proposed comprehensively.
Suppressing-accelerating effect of Nitrotetrazolium Blue chloride in boosting superconformal cobalt filling

Yaqiang Li,Xiaochuan Ma,Ruopeng Li,Jinqiu Zhang,Peixia Yang,Anmin Liu,Bo Wang,Peter Broekmann,Maozhong An

DOI: https://doi.org/10.1016/j.jelechem.2023.117671

IF: 4.598

2023-07-01

Journal of Electroanalytical Chemistry

Abstract:Achieving cobalt superconformal (bottom-up) growth is significantly important. Electrochemical methods, including cyclic voltammetry, electrochemical impedance spectra and EQCM-derived Coulomb-voltage curves, were used to confirm the suppressing influence of new suppressor Nitrotetrazolium Blue chloride (NBT). In situ Raman spectroscopy was used confirm that NBT can effectively adsorb on cobalt surface. Besides, EQCM-derived Coulomb-voltage illustrates that it is more beneficial for cobalt electrodeposition at high pH. The NBT effect on hydrogen evolution reaction (HER) was studied by LSV and chronoamperometry. Finite element simulation is used to investigate the accelerating effect of NBT on HER and convection. Suppressing-accelerating effect is proposed to illustrate effect of NBT. NBT can not only suppress the cobalt deposition but also can accelerate local convection by intensifying HER, which can in turn strengthen NBT adsorption. SEM analysis demonstrates that convection and NBT can refine grain. High-quality cobalt is achieved with low SDT values ranging from 24 μm to 45 μm and high FP values (75.4 % for 150 μm, 88.9 % for 100 μm and 87.2 % for 50 μm).

chemistry, analytical,electrochemistry
Solvothermal Preparation of Microspherical Shaped Cobalt–manganese Oxide As Electrode Materials for Supercapacitors

Wen Lei,Ping He,Yuhao Wang,Xingquan Zhang,An Xia,Faqin Dong

DOI: https://doi.org/10.1016/j.compscitech.2014.07.019

IF: 9.1

2014-01-01

Composites Science and Technology

Abstract:Microspherical shaped cobalt–manganese oxide (CMO) as electrode materials for supercapacitor is synthesized by solvothermal method. The microstructure and surface morphology of CMO are characterized by X-ray diffraction and scanning electron microscopy, respectively. Cyclic voltammetry and chronopotentiometry are employed for the characteristics of electrode process and the calculation of specific capacitance in KOH solution. It is shown that as prepared CMO with cobalt/manganese mole ratio of 1:2 has excellent specific capacitance of 348.0Fg−1 at current density of 0.5Ag−1. In addition, long-term stability of the composites electrode is measured at current density of 1.0Ag−1, and 58.6% of initial capacitance is retained after 500 cycles.
Enhanced Oxide Ion Conductivity in Stabilized Cubic BaInO2.5 by Mn5+ Doping

Yuzeng Sun,Chengxu Yang,Ting Shu,Guobao Li,Fuhui Liao,Jianhua Lin

DOI: https://doi.org/10.1016/j.inoche.2013.04.035

IF: 3.428

2013-01-01

Inorganic Chemistry Communications

Abstract:The preparation of room-temperature stabilized cubic BaInO2.5 was successfully achieved by adjusting Mn5+ doping (0.13≤x≤0.33) using high-temperature solid state reactions. XPS and magnetic investigations revealed that the valence state of Mn ions in stabilized cubic BaInO2.5 was +5. The stabilized cubic BaInO2.5 showed enhanced oxide ion conductivity, and the best low-temperature conductivity at 400°C was 3.0×10−3Scm−1, which was larger than previously reported highest conductivity for stabilized cubic BaInO2.5.
Structural Changes of YBa2Cu3O7-δSuperconductor with Co Substitution

X. S. Wu,S. S. Jiang,W. M. Chen,J. Lin,F. M. Pan,X. Jin,C. Gou,D. F. Chen,K. Sun

DOI: https://doi.org/10.1007/bf02767689

1997-01-01

Journal of Superconductivity

Abstract:YBa2(Cu1-yCoy)3O7-δ superconductors with y = 0.00 ∼0.06 are synthesized. The content of oxygen increases with increase in cobalt content, while the oxidation of copper is almost independent of cobalt concentration. The orthorhombic-to-tetragonal transition occurs in the range of 0.028< y< 0.038 according to neutron powder diffraction studies on samples with y = 0.03. Structural refinements for X-ray and neutron diffraction data show that there is an orthorhombic phase with y≤0.02 and a tetragonal phase with y>0.04. There is an orthorhombic and a tetragonal phase coexisting in a sample withY = 0.03. The content of cobalt in the tetragonal phase (0.038) is larger than that in the orthorhombic one (0.028). It seems that the structure of YBa2Cu|1-y CoyO x is unstable near the point of phase transition.
Hydrothermal Synthesis, Characterization, and Electrochemical Behaviour of Cobalt Oxide (Co3O4) Nanoparticles for Stable Electrode with Enhanced Supercapacitance

C. T. Anuradha,P. Raji

DOI: https://doi.org/10.1007/s13538-022-01214-4

2022-10-26

Brazilian Journal of Physics

Abstract:The electrochemical performance of highly crystalline cobalt oxide (Co 3 O 4 ) nanoparticles is described in this work using an oxalate-assisted hydrothermal synthesis in the presence of a natural surfactant. The Co 3 O 4 nanoparticle has a cubic spinel crystal structure with a crystallite size of 39 nm as determined XRD analysis. FTIR and UV–vis spectrum methods are used to evaluate the optical and functional properties of the synthesized Co 3 O 4 nanoparticles. Due to the quantum confinement effect, the UV–vis spectrum of Co 3 O 4 nanoparticles shows a wide energy band gap of 4.78 eV, which confirms the semiconducting nature of Co 3 O 4 nanoparticles. The excellent performance is attributable to the simple accessibility of the electrolyte as well as the porous poly-pyramidal shape, which enables Co 3 O 4 nanoparticles' volume expansion. In light of their charging and discharging behaviour, electrochemical examination of green chemical oxalate aided Co 3 O 4 nanoparticles reveals remarkable super capacitance behaviour with rapid dissemination of electrolyte ions on the electrode. These findings discover that the hydrothermally synthesized Co 3 O 4 nanoparticles are novel materials for making high-potential super capacitors.

physics, multidisciplinary
Superconductivity at 31 K in Alkaline Metal-Doped Cobalt Oxides

HH Wen,HP Yang,XF Lu,J Yan

DOI: https://doi.org/10.1088/0256-307x/20/5/338

2003-01-01

Abstract:By using a simple solid reaction method, we have fabricated alkaline metal doped cobalt oxides An(x)CoO(2+delta) (An = Na, K). The magnetic measurement shows a superconducting-like diamagnetic signal at 31 K based on a strong superparamagnetic signal. Below 31 K, the magnetization hysteresis loops contain a strong rough linear superparamagnetic background and a superconducting hysteresis. The typical magnetization hysteresis loops for a type-II superconductor are found. Preliminary resistive data also show a fast dropping of resistance below T-c. These give indication of superconductivity below 31 K in An(x) CoO2+delta (An = Na, K).
Scalable complete conversion of MgCo2O4 by mechanochemistry for high-performance supercapacitors

Zhiyuan Liu,Qixuan Xiang,Hao Zhang,Xianglong Zhang,Huijun Tang,Yaping Zhao

DOI: https://doi.org/10.1039/d4qi02020k

IF: 7.779

2024-01-01

Inorganic Chemistry Frontiers

Abstract:MgCo2O4, a cobalt-based binary oxide, has garnered increasing attention as a promising active material for supercapacitor electrodes due to its enhanced conductivity and high theoretical capacitance. In this study, a...

chemistry, inorganic & nuclear

ChemInform Abstract: Stabilization of Cobalt Oxyhydrate Superconductor

Stabilization of cobalt oxyhydrate superconductor.

Synthesis of Cobalt Oxyhydrate Superconductor Through a Disproportionation Reaction Route.

SYNTHESIS AND CHRACTERIZATION OF COBALT OXYHYDRATE SUPERCONDUCTORS

Tuning Co Valence State in Cobalt Oxyhydrate Superconductor by Postreduction

Chemical instability of the cobalt oxyhydrate superconductor under ambient conditions

SUPERCONDUCTIVITY IN Na0.15(H3O)0.2CoO2·wH2O

Hydrothermal Synthesis of Cobalt Sulfide Nanotubes: the Size Control and Its Application in Supercapacitors

Proton incorporations and superconductivity in a cobalt oxyhydrate

A novel route to phase formation of cobalt oxyhydrates using KMnO4 as an oxidizing agent

Superconductor made by electrolyzed and oxidized water

Superconductivity and Cobalt Oxidation State in Metastable Na(x)CoO(2-delta)*yH2O (x ~ 1/3; y ~ 4x)

ChemInform Abstract: Enhanced Oxide Ion Conductivity in Stabilized Cubic BaInO2.5 by Mn5+ Doping.

Solid-state Synthesis of Cobalt Ferrite Fitted with Γ-Fe2o3-containing Nanocage for Peroxymonosulfate Activation and Cobalt Leaching Control

Suppressing-accelerating effect of Nitrotetrazolium Blue chloride in boosting superconformal cobalt filling

Solvothermal Preparation of Microspherical Shaped Cobalt–manganese Oxide As Electrode Materials for Supercapacitors

Enhanced Oxide Ion Conductivity in Stabilized Cubic BaInO2.5 by Mn5+ Doping

Structural Changes of YBa2Cu3O7-δSuperconductor with Co Substitution

Hydrothermal Synthesis, Characterization, and Electrochemical Behaviour of Cobalt Oxide (Co3O4) Nanoparticles for Stable Electrode with Enhanced Supercapacitance

Superconductivity at 31 K in Alkaline Metal-Doped Cobalt Oxides

Scalable complete conversion of MgCo2O4 by mechanochemistry for high-performance supercapacitors