Abstract:Polycrystalline material of a sulfate apatite with chemical composition Na6Ca4(SO4)6F2 or (Na2Ca4)Na4(SO4)6F2 has been synthesized by solid state reactions. Basic crystallographic data are as follows: hexagonal symmetry, a = 9.3976(1) Å, c = 6.8956(1) Å, V = 527.39(1) Å3, Z = 1, space group P63/m. For structural investigations the Rietveld method was employed. Thermal expansion has been studied between 25 and 600 °C. High temperature (HT) powder diffraction data as well as thermal analysis indicate that the apatite-type compound undergoes a reconstructive phase transition in the range between 610 and 630 °C. Single-crystals of the HT-polymorph were directly grown from the melt. Structural investigations based on single-crystal diffraction data of the quenched crystals performed at −100 °C showed orthorhombic symmetry (space group Pna21) with a = 12.7560(8) Å, b = 8.6930(4) Å, c = 9.8980(5) Å, V = 1097.57(10) Å3 and Z = 2. Unit cell parameters for a quenched polycrystalline sample of the HT-form obtained at ambient conditions from a LeBail-fit are as follows: a = 12.7875(1) Å, b = 8.7255(1) Å, c = 9.9261(1) Å, V = 1107.53(2) Å3. The lattice parameters of both modifications are related by the following approximate relationships: aHT ≈ 2cRT, bHT ≈ -(½aRT + bRT), cHT ≈ aRT. The HT-modification is isotypic with the corresponding potassium compound K6Ca4(SO4)6F2. The pronounced disorder of the sulphate group even at low temperatures has been studied by maximum entropy calculations. Despite the first-order character of the transformation clusters of sulfate groups surrounding the fluorine anions can be identified in both polymorphs. Each of the three next neighbor SO4-tetrahedra within a cluster is in turn surrounded by 8–9 M-cations (M: Na,Ca) defining cage-like units. However, in the apatite structure the corresponding three tricapped trigonal prisms are symmetry equivalent. Furthermore, the central fluorine atom of each cluster is coordinated by three next M-neighbors (FM3-triangles), whereas in the HT-polymorph a four-fold coordination is observed (FM4-tetrahedra).

Solid Solution Between Lead Fluorapatite and Lead Fluorvanadate Apatite: Mixing Behavior, Raman Feature and Thermal Expansivity

Solid solutions between lead fluorapatite and lead fluorvanadate apatite: compressibility determined by using a diamond-anvil cell coupled with synchrotron X-ray diffraction

Calcium-lead fluoro-vanadinite apatites. I. Disequilibrium structures

Synthesis of a new potassium-substituted lead fluorapatite and its structural characterization

Characterization, dissolution and solubility of lead fluorapatite at 25-45 °C

On the role of vanadium in the structure and properties of calcium-bismuth-sodium oxyapatite

Thermodynamic characterization of synthetic lead-arsenate apatites with different halogen substitutions

Structural Change in Lead Fluorapatite at High Pressure

Mobilities of Volatiles (H, F and C) in Apatite at High Temperatures

Phase Stability of Lead Phosphate Apatite Pb 10– x Cu x (PO 4 ) 6 O, Pb 10– x Cu x (PO 4 ) 6 (OH) 2 ( x = 0, 1), and Pb 8 Cu 2 (PO 4 ) 6

Expansivity and Compressibility of Strontium Fluorapatite and Barium Fluorapatite Determined by in Situ X-ray Diffraction at High-T/p Conditions: Significance of the M-site Cations

Synthetic Lead Bromapatite: X-ray Structure at Ambient Pressure and Compressibility Up to about 20 GPa

Wet Synthesis and Characterization of Lanthanum-Substituted Hydroxyapatite

Structural investigations, high temperature behavior and phase transition of Na6Ca4(SO4)6F2

Phase Stability of Lead Phosphate Apatite Pb$_{10-x}$Cu$_{x}$(PO$_{4}$)$_{6}$O, Pb$_{10-x}$Cu$_{x}$(PO$_{4}$)$_{6}$(OH)$_{2}$, and Pb$_{8}$Cu$_{2}$(PO$_{4}$)$_{6}$

The effect of triethanolamine on the formation of sol–gel derived fluoroapatite/hydroxyapatite solid solution

Synthesis and electrical properties of apatite-type La10Si6O27

Thermal Behavior of Pyromorphite (pb10(po4)6cl2): in Situ High Temperature Powder X-ray Diffraction Study

Characterization, Physicochemical Properties and Biocompatibility of La-incorporated Apatites

Structure and Thermal Expansion Behavior of Ca4La6-xNdx(SiO4)4(PO4)2O2 Apatite for Nuclear Waste Immobilization.

The Formation Mechanism of the Β-Tcp Phase in Synthetic Fluorohydroxyapatite with Different Fluorine Contents