Abstract:In this study, the physicochemical properties and biocompatibilities of La-containing apatites were intensively investigated together with their characterizations in terms of composition, structure, valent state and morphology using X-ray diffraction, Fourier-transform infrared spectra, X-ray photoelectron spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy, respectively. The results indicate that the La3+ ion can be incorporated into the crystal lattice of hydroxyapatite resulting in the production of La-incorporated apatites (LaxCa10−x(PO4)6(OH)2+x−2yOy□y−x (x⩽0.5, y<1+x/2) or LaxCa10−x(PO4)6Oy□y−x (0.5<x<2, y=1+x/2)) by high-temperature solid phase synthesis. For La content <20%, the product is composed of the major phase, Lax-OAP, as well as a small amount of tricalcium phosphate, but for a La content of 20%, the product is pure La-incorporated oxyapatite with the formula La2Ca8(PO4)6O2 (La2-OAP, x=2, y=2). It is also found that the La content plays important roles in both the physicochemical properties and biocompatibilities of the La-incorporated apatites. In contrast to La-free apatite, La-incorporated apatites possess a series of attractive properties, including higher thermal stability, higher flexural strength, lower dissolution rate, larger alkaline phosphatase activity, preferable osteoblast morphology and comparable cytotoxicity. In particular, the sintered La-incorporated apatite block achieves a maximal flexure strength of 66.69±0.98MPa at 5% La content (confidence coefficient 0.95), increased 320% in comparison with the La-free apatite. The present study suggests that the La-incorporated apatite possesses application potential in developing a new type of bioactive coating material for metal implants and also as a promising La carrier for further exploring the beneficial functions of La in the human body.

Characterization, Physicochemical Properties and Biocompatibility of La-incorporated Apatites

Wet Synthesis and Characterization of Lanthanum-Substituted Hydroxyapatite

Lanthanum-silicon-substituted hydroxyapatite: Mechanochemical synthesis and prospects for medical applications

Lanthanum Contained Hydroxyapatite Coatings Prepared by Micro-Arc Oxidation

Characterization, mechanical properties, corrosion behaviour and bone-like apatite formation ability of fluorine substituted hydroxyapatite coating

Preparation and Biocompatibility of Nanoscaled La/Ag/HAP Powder

Synthesis and characterization of Al3+ and M (M = W6+, In3+, Nb5+, Mg2+) co-doped lanthanum silicate oxy-apatite electrolytes

Thermal Behavior, Sintering and Mechanical Characterization of Multiple Ion-Substituted Hydroxyapatite Bioceramics

Synthesis and Characterization of Tb-incorporated Apatite Nano-scale Powders

Fluoridation of Synthetic Apatite: Effect on the Formation of Calcium-Deficient Hydroxyapatite and the Properties of Porous Scaffold

Influences of Sr dose on the crystal structure parameters and Sr distributions of Sr-incorporated hydroxyapatite

Studies on morpho-structure and ionic conductivity of apatite-type lanthanum silicate doped with transitional metal cations

[Studies on the application of apatite to dental materials. (I) --Apatite ceramics-- (author's transl)]

Effects of La on Microstructures and Biocompatibility of Pure Ti Micro-Arc Oxidation Coatings

Synthesis and electrical properties of apatite-type La10Si6O27

Mechanism of Mn incorporation into hydroxyapatite: Insights from SR-XRD, Raman, XAS, and DFT calculation

Design of the electronic structure and properties of calcium apatites via isomorphic modification of the cation sublattice, and prospects of their application

The influence of Sr doses on the in vitro biocompatibility and in vivo degradability of single-phase Sr-incorporated HAP cement.

PREPARATION AND PROPERTIES OF LANTHANUM-DOPED HYDROXYAPATITE COATING ON COMMERCIALLY PURE TITANIUM

Structure and Thermal Expansion Behavior of Ca4La6-xNdx(SiO4)4(PO4)2O2 Apatite for Nuclear Waste Immobilization.

Effect of hydroxyapatite coating crystallinity on dissolution and osseointegration in vivo.