Abstract:As the dominated composition of Si3N4 ceramics,α-silicon nitride(α-Si3N4)can satisfy the strength and fracture toughness demand in the applications.However,α-Si3N4 is oxygen-sensitive at high tempera-tures,which limits its high-temperature performance.To improve the oxidation resistance of α-Si3N4 ce-ramics,it is necessary to shed light on the oxidation mechanism.Herein,the initial oxidation of α-Si3N4 was systematically studied at the atomic and molecular levels.The density functional theory(DFT)calcu-lation denotes that the(001)surface of α-Si3N4 has the best stability at both room temperature and high temperature.Besides,the oxidation process of the α-Si3N4(001)surface consists of O adsorption and N desorption,and the consequent formation of nitrogen-vacancy(VN)is the key step for further oxidation.Moreover,the molecular dynamics(MD)simulation indicates that the oxidation rate of α-Si3N4(100)surface is slower than that of α-Si3N4(001)surface due to the lower N concentration at the outermost layer.Therefore,the oxidation resistance of α-Si3N4 can be improved by regulating the(100)surface as the dominant exposure surface.In addition,reducing the concentration of N on the final exposed sur-face of α-Si3N4 by mean of constructing the homojunction of the Si-terminal(100)surface and other N-containing surfaces(such as(001)surface)should be also a feasible approach.

Surface oxidation to improve water-based gelcasting of silicon nitride

Water-Based Gelcasting of Surface-Coated Silicon Nitride Powder

Gas-discharging reactions and their effect on the microstructures of green bodies in gelcasting of non-oxide materials

New Design Concept for Stable Α-Silicon Nitride Based on the Initial Oxidation Evolution at the Atomic and Molecular Levels

Gas-discharging Reactions in Gelcasting of Si-containing Materials and Their Effect on Microstructure of Green Bodies

The contributing factor and elimination of macropores in Si3N4 green bodies formed by water-based gelcasting

The Gel-Casting Of Non-Oxide Ceramics

Preparation of High Concentrated Suspension and Gelcasting Process for Silicon Nitride Bonded Silicon Carbide Refractories

Surface Characterization of Silicon Nitride Powder and Electrokinetic Behavior of Its Aqueous Suspension

A facile strategy for fabricating self-sealing dense coating grown in-situ on porous silicon nitride ceramics

Study on Gelcasting of Silicon Nitride-Bonded Silicon Carbide Refractories

Enhancing oxidation resistance of silicon nitride using a Ca 2+ stabilizer

Effect of Pre-Oxidation of Si3N4 Powders on the Interaction Between Si3N4 Coating and Molten Si

Study on mechanism for eliminating the surface flaws of green body prepared by gelcasting via polymer

Combustion synthesis of Si2N2O powder for photovoltaic silicon casting application

Gelcasting of silicon carbide based on gelation of sodium alginate

Surface Characteristics and Aqueous Dispersibility of Commercial Silicon Nitride Powders: Effects of Acid Leaching, Surface Hydrolysis, and Thermal Oxidation

Oxidation Behavior of Dense SiC Coating in Water Vapor and Its Mixed Atmosphere with Air

Solidifying Concentrated Si<sub>3</sub>N<sub>4</sub> Suspensions for Gelcasting by Ultrasonic Effects

Gelcasting of Concentrated Aqueous Silicon Carbide Suspension

Surface Modification Of Nano-Sic Powders By Coating With Heterogeneous Nucleation Process