Abstract:Most of the existing studies on acid corrosion of concrete have focused on the mechanical behavior of concrete structures under monotonic load or without load. To investigate the mechanical properties of in-service concrete components under cyclic load in an acid corrosion environment, six groups of concrete prism specimens with different acid corrosion degrees (corrosion duration) were designed and prepared by the accelerated corrosion test method. The monotonic and cyclic axial compression load tests on these specimens were conducted to investigate the effects of corrosion degree on the mechanical properties of concrete specimens. The experimental results indicated that hydrochloric acid corrosion has obvious effects on the failure characteristics and mechanical properties of concrete. The surface of corroded concrete was easier to crack and spall under load, and the concrete spalling area enlarged as the acid corrosion duration increased. The compressive capacity of concrete specimens reduced rapidly with the increase in corrosion duration. The stress–strain envelope curves for concrete with different corrosion duration under cyclic load were essentially similar to that of concrete under monotonic load. The degradation rate of the descending section for the stress–strain curves of corroded concrete under cyclic load was much larger than that under the monotonic load due to the accumulation of internal damage in concrete. The peak strain and ultimate strain of corroded concrete increased significantly with the increase in corrosion duration and enhanced by 55.7% and 77.9%, respectively, compared with the uncorroded concrete, whereas the peak stress and elastic modulus rapidly decreased and reduced by 53.3% and 74.1%, respectively. Moreover, based on the strength degradation depth, the concept of effective bearing cross-sectional area ratio was proposed to characterize the corrosion degree of concrete, and the correction coefficient of descending section for the effective bearing cross-sectional area ratio was introduced to establish the constitutive model of corroded concrete under cyclic load, and the results calculated by this model matched well with the experimental values. The research in this paper can provide the experimental and theoretical basis for seismic life cycle and fatigue redesign of concrete structures in acid corrosion environments or coastal areas.

Laboratory Study on Urban Heat Island Effect on the Acid Corrosion of Concrete in Superficial Soil Layers

Study on the Behavior and Durability of Reinforced Concrete in Boric Acid Environment

Behavior of Reinforced Concrete Subjected to Boric Acid Corrosion of Nuclear Power Plant

Study on the Real-Time Dynamic Monitoring of Corrosion Rate of Reinforcement in Carbonation Environment

Analysis of Concrete Corrosion Resistant Performance Based on the Coupled Action of Acid Rain and Carbonization

Research on Mechanism of Concrete Corrosion Subjected to Underground Acid Liquid

Numerical simulation of electrochemical mechanism of steel rebar corrosion in concrete under natural climate with time-varying temperature and humidity

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Influence of Internal Temperature and Humidity in Concrete on the Corrosion Rate of Rebar

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen

Applicability Study on Accelerated Corrosion Methods of Steel Bars in Concrete Structure

Dynamic Electrochemical Model of Steel Corrosion in Concrete Microenvironment under Multifield Action of Heat-Moisture-Chlorine

Study on the Influences of Boric Acid on the Corrosion of Concrete

Effect of Environmental Temperature on Efficiency of Electrochemical Chloride Removal from Concrete

Optimal Design and Performance of Concrete with Function Component in Marine Environment

Experimental and Numerical Investigation of the Effect of the Urban Heat Island on Slope Stability

Experimental Research on Anti-Corrosion of Slag High Performance Concrete

Experimental Investigation on the Influence of Strength Grade on the Surface Fractal Dimension of Concrete under Sulfuric Acid Attack

Study on Corrosion Mechanism of Different Concentrations of Na2SO4 Solution on Early-Age Cast-In-Situ Concrete

Corrosion Mechanism Study of Concrete Structure Under the High-temperature High-humidity and Corrosiveness Surrounding

Study on Mechanical Properties and Constitutive Relationship of Concrete Corroded by Hydrochloric Acid under Cyclic Load