Abstract:Multiferroic ceramics were prepared and characterized in (1-x)BiFeO3-x(0.5CaTiO(3)-0.5SmFeO(3)) system by a standard solid-state reaction process. The structure evolution was investigated by X-ray diffraction and Raman spectrum analyses. The refinement results confirmed the different phase assemblages with varying amounts of polar rhombohedral R3c and nonpolar orthorhombic Pbnm as a function of the substitution content. In the compositions range of 0.2x0.5, polar R3c and nonpolar Pbnm coexisted, which was referred to polar-to-nonpolar morphotropic phase boundary (MPB). According to the dielectric and DSC analysis results, the ceramics with x0.2 changed to diffused ferroelectric, and the ferroelectric properties were enhanced significantly. Two dielectric relaxations were detected in the temperature range of 200-300 K and 500-700 K, respectively. The high-temperature dielectric relaxation was attributed to the grain-boundary effects. While the low temperature dielectric relaxation obtained in the samples with x=0.3-0.5 was related to the charge transfer between Fe2+ and Fe3+. The magnetic hysteresis loops measured at different temperature indicated the enhanced magnetic properties in the present ceramics, which could be attributed to the suppressed cycloidal spin magnetic structure by Ti ions. In addition, the rare-earth Sm spin moments might also affect the magnetic properties at relatively lower temperature.

Structure and Multiferroic Properties of Bi<sub>0.9</sub>Y<sub>0.1</sub>FeO<sub>3</sub>-PbTiO<sub>3</sub> Ceramics

Ferroelectric and Magnetic Properties in (1-X)bifeo3-x(0.5catio(3)-0.5smfeo(3)) Ceramics

Structural Evolution in 0.67(sm Bi1−)FeO3-0.33BaTiO3 Solid Solution and Its Effect on Multiferroic Properties at Room Temperature

Multiferroic Properties of Single-Phase Bi0.85la0.15feo3 Lead-Free Ceramics

Multiferroic Orders in 0.5Bifeo3–0.5bi0·5k0·5tio3

Structure, ferroelectric and piezoelectric properties of multiferroic Bi 0.875Sm 0.125FeO 3 ceramics

Rietveld analysis and multiferroic properties of Fe doped Ba 0.95 Bi 0.05 TiO 3 ceramics

Effect of Yttrium Doping on the Structure, Dielectric Multiferroic and Magnetodielectric Properties of Bi5Ti3FeO15 Ceramics

Simultaneously Enhanced Ferroelectric and Magnetic Properties in 0.675bife1−x Cr X O3–0.325PbTiO3 (x = 0–0.05) Ceramics

Multiferroic properties of Bi1− xDyxFeO3 (x= 0–0.2) ceramics at various temperatures

Crystal Structure, Leakage Conduction Mechanism Evolution and Enhanced Multiferroic Properties in Y-doped BiFeO3 Ceramics

Effect of Chemical Modification on the Structure and Dielectric and Magnetic Properties of Multiferroic (1 – X )bifeo 3 - X DyFeO 3 Solid Solution

Synthesis, Structure and Dielectric Properties of (1−x)[0.9bifeo3–0.1dyfeo3]–xpbtio3 Pseudo-Binary Ceramics

Enhanced Ferroelectricity, Piezoelectricity and Ferromagnetism in (ba0.75ca0.25)tio3 Modified BiFeO3 Multiferroic Ceramics

Multiferroic Properties of (1−X)bifeo3-Xba(fe1/2nb1/2)o3 Ceramics

Microstructure, Dielectric and Ferroelectric Properties of Xbazr0.2ti0.8o3-(1 − X)bifeo3 Solid Solution Ceramics

Multiferroic Properties of Layer-Structured Bi5fe0.5co0.5ti3o15 Ceramics

Structure Transition and Enhanced Multiferroic Properties of Dy-doped BiFeO3

Multiferroic and Magnetoelectric Properties of Single-Phase Bi0.85la0.1ho0.05feo3 Ceramics

Structural, optical and multiferroic properties of (1−x)BiFeO3–(x)Pb(Fe2/3W1/3)O3 solid solution

Structure and Piezoelectric Properties of Bifeo3 and Bi0.92dy0.08feo3 Multiferroics at High Temperature