The Crystallization Kinetics Study of Finemet-Co Amorphous Alloys
WANG Ru-wu,LIU Jing,WANG Zhen,WANG Ke-lei,XU Yong-pan,GAN Zhang-hua,LU Zhi-hong,LI Yun-bao,WANG Deng-jing,YUAN Jie,WANG Yu-hua
2011-01-01
Journal of Functional Biomaterials
Abstract:Amorphous ribbons Fe73.5-xCoxSi13.5B9Cu1Nb3(x=10,30,50) were prepared by the standard single copper wheel melt spinning technique in the air atmosphere.The isothermal annealing was carried out at 550 and 600℃ for 1h in a vacuum furnace to induce the formation of nanocrystallite in amorphous ribbons.The X-ray diffraction(XRD) analyses showed that the average sizes D of α-Fe(Co,Si) grains for the samples annealed at 550℃ were 19.3,20.1,22.8 nm and those for the samples annealed at 600℃ were 24.8,25.2,26.5nm,respectively.The primary crystallization activation energies of amorphous ribbons were calculated using Kissinger,Ozawa and Augis-Bennett models based on differential thermal analysis data.The local Avrami exponenet n for primary crystallization was calculated using Johnson-Mehl-Avrami(JMA) equation.The significant variation of local Avrami exponent n with crystallized volume fraction α demonstrated that the primary crystallization kinetics of amorphous ribbons varied at different stages.In the initial stage(0α0.2),the crystallization mechanism was bulk crystallization with three dimensional nucleation and grain growth controlled by diffusion at decreasing nucleation rate.In the following stage(0.2α1.0),it was surface crystallization with one dimensional nucleation and grain growth at a near-zero nucleation rate.