Abstract:Two chiral hydrogelators, L-18ValPyBr and D-18ValPyBr, composed of L- or D-valine, were synthesized. They self-assembled into thin membranes under high concentration and helical nanofibers under low concentration in pure water. Sol-gel transcription reactions were carried out under both acidic and basic conditions using the self-assemblies of these two gelators and the mixtures with CTAC as templates and TEOS as precursor. Under acidic conditions, minimum gel concentrations of L-18ValPyBr and D-18ValPyBr are very low. After sol-gel polymerization, a kind of cotton-like silica constructed by twisted mesoporous silica ribbons was obtained. These ribbons were 60 nm in width and 10 nm in thickness. Under basic conditions, both mesoporous twisted ribbons and nanotubes constructed by tightly coiled ribbons were obtained. Generally, left-handed helical structures were obtained by using L-18ValPyBr, while right-handed helical structures were obtained by using D-18ValPyBr. The morphologies were sensitive to the concentration of NH3. When the concentration of NH3 was 2.5 wt%, twisted ribbons were obtained. When the concentration of NH3 was higher than 5.0 wt%, nanotubes constructed by tightly coiled ribbons were obtained. Mesoporous silica structures in nano- and micro-size were prepared by using the mixtures of L-18ValPyBr and CTAC under both acidic and basic conditions. Under acidic conditions, helical mesoporous fibers were obtained, and their diameter was increased with increasing the ratio of CTAC to gelator. The nanofibers obtained under basic conditions were shorter than those obtained under acidic conditions. The mesoporous channels were parallel each other and running along the axis of nanofibers.

Nanofabrication of Helical Hybrid Silica Nanotubes Using Anionic Gelators

Preparation of Organic and Inorganic Hybrid Silica Nanotubes

The Formation of Helical Mesoporous Silica Nanotubes

Preparation of Helical Mesoporous Silica and Hybrid Silica Nanofibers Using Hydrogelator

Transfer helix and chirality to 1,4-phenylene silica nanostructures

Fabrication of Helical Mesoporous Silica Nanostructures Using Gelators and the Mixtures with CTAC

Control the Handedness of the Mesoporous Silica Nanoribbons and the Pore Channels Using Anionic Gelators

Preparation of Chiral 4,4′-Biphenylene-silica Nanoribbons

Preparation of Single-Handed Helical Carbon/Silica and Carbonaceous Nanotubes by Using 4,4 '-Biphenylene-bridged Polybissilsesquioxane

Single-Handed Helical Polybissilsesquioxane Nanotubes And Mesoporous Nanofibers Prepared By An External Templating Approach Using Low-Molecular-Weight Gelators

Hybrid Silica Nanotubes With Chiral Walls

Single-handed Helical Carbonaceous Nanotubes Prepared Using a Pair of Cationic Low Molecular Weight Gelators

Preparation of left-handed coiled silica nanotubes

Formation of silica nanotubes with spring-like pore channels in the walls

Handedness inversion in preparing chiral 4, 4(')-biphenylene-silica nanostructures.

Preparation of Chiral Mesoporous Silica Nanotubes and Nanoribbons Using a Dual-Templating Approach

Preparation of Helical Nanostructured Silica Using Gelator and Surfactant as Template

Control of Helical Silica Nanostructures Using A Chiral Surfactant

Tunable One-Dimensional Helical Nanostructures: from Supramolecular Self-Assemblies to Silica Nanomaterials

Preparation of Mesoporous Silica Nanoribbons and Nanoflakes with Short Pore Channels Using a Chiral Amphiphile.

Organization of Helical Mesoporous Silica Nanotubes