Abstract:Two chiral hydrogelators, L-18ValPyBr and D-18ValPyBr, composed of L- or D-valine, were synthesized. They self-assembled into thin membranes under high concentration and helical nanofibers under low concentration in pure water. Sol-gel transcription reactions were carried out under both acidic and basic conditions using the self-assemblies of these two gelators and the mixtures with CTAC as templates and TEOS as precursor. Under acidic conditions, minimum gel concentrations of L-18ValPyBr and D-18ValPyBr are very low. After sol-gel polymerization, a kind of cotton-like silica constructed by twisted mesoporous silica ribbons was obtained. These ribbons were 60 nm in width and 10 nm in thickness. Under basic conditions, both mesoporous twisted ribbons and nanotubes constructed by tightly coiled ribbons were obtained. Generally, left-handed helical structures were obtained by using L-18ValPyBr, while right-handed helical structures were obtained by using D-18ValPyBr. The morphologies were sensitive to the concentration of NH3. When the concentration of NH3 was 2.5 wt%, twisted ribbons were obtained. When the concentration of NH3 was higher than 5.0 wt%, nanotubes constructed by tightly coiled ribbons were obtained. Mesoporous silica structures in nano- and micro-size were prepared by using the mixtures of L-18ValPyBr and CTAC under both acidic and basic conditions. Under acidic conditions, helical mesoporous fibers were obtained, and their diameter was increased with increasing the ratio of CTAC to gelator. The nanofibers obtained under basic conditions were shorter than those obtained under acidic conditions. The mesoporous channels were parallel each other and running along the axis of nanofibers.

Preparation of Helical Mesoporous Silica and Hybrid Silica Nanofibers Using Hydrogelator

Nanofabrication of Helical Hybrid Silica Nanotubes Using Anionic Gelators

Fabrication of Helical Mesoporous Silica Nanostructures Using Gelators and the Mixtures with CTAC

The Formation of Helical Mesoporous Silica Nanotubes

Preparation of Helical Nanostructured Silica Using Gelator and Surfactant as Template

Nanofiberization of Inner Helical Mesoporous Silica Using Chiral Gelator As Template under a Shear Flow

Control of Helical Silica Nanostructures Using A Chiral Surfactant

Control of mesoporous silica nanostructures and pore-architectures using a thickener and a gelator.

Control the Handedness of the Mesoporous Silica Nanoribbons and the Pore Channels Using Anionic Gelators

Single-Handed Helical Polybissilsesquioxane Nanotubes And Mesoporous Nanofibers Prepared By An External Templating Approach Using Low-Molecular-Weight Gelators

Preparation of Chiral 1,4-Phenylene-silicas Via Chiral Low-Molecular-Weight Amphiphiles

Fabrication of Helical Hybrid Silica Bundles

Preparation of Mesoporous Silica Nanoribbons and Nanoflakes with Short Pore Channels Using a Chiral Amphiphile.

Preparation of Silica Nanosprings Using Cationic Gelators As Template

Preparation of Helical Mesoporous Ethenylene-silica Nanofibers with Lamellar Mesopores on Their Surface

Transfer helix and chirality to 1,4-phenylene silica nanostructures

Preparation of Organic and Inorganic Hybrid Silica Nanotubes

Preparation of Ethenylene-Silica Hollow Spheres with a Single-Layer of Mesopores Using a Chiral Amphiphile

Preparation of Helical Mesoporous Ethenylene-Silica Nanofibers Using L-2-methyl-1-butanol As Co-Structure-directing Agent

Preparation of Helical Mesoporous Ethylene–silica Nanofibers Using CTAB and (S)-2-methyl-1-butanol

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes