Abstract:Two chiral hydrogelators, L-18ValPyBr and D-18ValPyBr, composed of L- or D-valine, were synthesized. They self-assembled into thin membranes under high concentration and helical nanofibers under low concentration in pure water. Sol-gel transcription reactions were carried out under both acidic and basic conditions using the self-assemblies of these two gelators and the mixtures with CTAC as templates and TEOS as precursor. Under acidic conditions, minimum gel concentrations of L-18ValPyBr and D-18ValPyBr are very low. After sol-gel polymerization, a kind of cotton-like silica constructed by twisted mesoporous silica ribbons was obtained. These ribbons were 60 nm in width and 10 nm in thickness. Under basic conditions, both mesoporous twisted ribbons and nanotubes constructed by tightly coiled ribbons were obtained. Generally, left-handed helical structures were obtained by using L-18ValPyBr, while right-handed helical structures were obtained by using D-18ValPyBr. The morphologies were sensitive to the concentration of NH3. When the concentration of NH3 was 2.5 wt%, twisted ribbons were obtained. When the concentration of NH3 was higher than 5.0 wt%, nanotubes constructed by tightly coiled ribbons were obtained. Mesoporous silica structures in nano- and micro-size were prepared by using the mixtures of L-18ValPyBr and CTAC under both acidic and basic conditions. Under acidic conditions, helical mesoporous fibers were obtained, and their diameter was increased with increasing the ratio of CTAC to gelator. The nanofibers obtained under basic conditions were shorter than those obtained under acidic conditions. The mesoporous channels were parallel each other and running along the axis of nanofibers.

Formation of silica nanotubes with spring-like pore channels in the walls

Formation of Hollow Mesoporous Silica Nanoworm with Two Holes at the Terminals.

The Formation of Helical Mesoporous Silica Nanotubes

Preparation of Mesoporous Silica Nanoflakes and Nanospheres with Perpendicular Pore Channels.

Preparation of Ethenylene-Silica Hollow Spheres with a Single-Layer of Mesopores Using a Chiral Amphiphile

Preparation of Mesoporous Silica Nanoribbons and Nanoflakes with Short Pore Channels Using a Chiral Amphiphile.

From Nanotubes to Nano-Cocoons with Coiled Pore Channels.

Organization of Helical Mesoporous Silica Nanotubes

Nanofabrication of Helical Hybrid Silica Nanotubes Using Anionic Gelators

Preparation of mesoporous silica hollow nanoworms

Preparation of Hierarchical Mesoporous Silica Nanoparticles Through a Single-Templating Approach

Preparation of Chiral Mesoporous Silica Nanotubes and Nanoribbons Using a Dual-Templating Approach

Preparation of Frustule-Like 1,2-Ethylene-silica Nanospheres Through A Chiral Amphiphile/Organic Solvent Dual-Templating Approach

Control of mesoporous silica nanostructures and pore-architectures using a thickener and a gelator.

Preparation of Silica Nanoflakes with Spherical Mesopores Using a Dual-Templating Approach

Fabrication of Helical Mesoporous Silica Nanostructures Using Gelators and the Mixtures with CTAC

A better understanding of the formation of silica nanococoons

Preparation of Helical Mesoporous Ethenylene-silica Nanofibers with Lamellar Mesopores on Their Surface

Hybrid Silica Nanotubes With Chiral Walls

Preparation of Organic and Inorganic Hybrid Silica Nanotubes

Synthesis and Characterization of Silica Nanotubes with Radially Oriented Mesopores