STUDY ON THE FLAME RETARDING SYNERGISM OF ORGANICALLY MODIFIED MONTMORILLONITE WITH DBDPE/Sb_2O_3 IN HDPE

Luo Caigui,Tong Zhangfa,Yin Zuodong,Lu Zengmeng,Qin Shanli,Cui Xuemin

DOI: https://doi.org/10.3969/j.issn.1003-9384.2013.01.013

2013-01-01

Abstract:Seeing that the high density polyethylene(HDPE) is inflammable,flame retardant composites of high density polyethylene and organically modified montmorillonite(OMMT) were prepared by means of direct melt-blending technique for HDPE,OMMT and halogen-antimony flame retardant(HAFR)-DBDPE/Sb2O3.The flame-retardant synergism of OMMT with HAFR in HDPE/OMMT composites was studied by means of limiting oxygen index(LOI),vertical burning grade(UL-94),the mechanical property and the thermal stability tests.The results showed that the synergistic flame retardant effect of OMMT and HAFR was satisfactory.The LOI of flame-retardant HDPE/OMM1 composite material increased from 19.6% of pure HDPE to 27.8%,the vertical flammability level gradually raised from "complete combustion" to level V-0,and combustion droplet was not produced with a good char formation effect.Tensile strength increased from 13.24 MPa to 24.53 MPa,which testified that the material had good mechanical properties.Weight loss rate decreased from 96.17% of pure HDPE to 90.37%,which indicated that the thermal stability was improved compared with pure HDPE.Flame-retardant HDPE/OMM4 composite materials also have a similar situation,and its performances are better.