Abstract:High impact polystyrene (HIPS) composites containing both Decabromodiphenyl oxide (DBDPO)-antimony (Sb2O3) and Montmorillonite (MMT, pristine clay)- Hexadecyl trimethyl ammonium bromide (C16BrN) flame retarding system packages were prepared by One-Step Melt Blending in One-Pot. X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM), Underwriters Laboratory Vertical Burning Test (UL 94 V) and Cone Calorimeter Test have been performed to characterize the morphology and combustion properties of the fire retardant composites. Results show that HIPS-based nanocomposites with intercalation structure in the presence of DBDPO can be obtained, and much decreased heat release rate is achieved due to the good synergistic effect between MMT-C16BrN and DBDPO-antimony. This effect provides evidence for the reduction use of halogen-contained flame retardants in one composite system for the purpose of lowering the production cost and lessening unwanted environment effects and is very meaningful for the development of green ecological polymer-based fire retardant composites.

Studies on Fire Retarding Effect of Fire Retardant HIPS/Organo-MMT Nanocomposite--Synergistic Effect Between Conventional Additive and Organo-modified MMT